Yaobian Jianzhan Firing Technology

A kind of craft and green body technology, applied in the field of Yaobian Jianzhan firing technology, can solve the problems of difficult experiment success, few reference materials, complex itself, etc., achieve high artistic value and appreciation value, easy to control, and clear process flow Effect

Active Publication Date: 2022-06-17
陆金喜
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The firing of Yaobian Jianzhan has always been the tireless pursuit of Jianzhan craftsmen, but because there are very few reference materials of its predecessors and the itself is very complicated, it is difficult to succeed in the experiment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Yaobian Jianzhan Firing Technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Yaobian Jianzhan firing process includes the following steps:

[0044] (1) Preparation of green body raw materials and glaze;

[0045] The green body raw material is prepared by the following method: mixing, pulverizing, and elutriating 60 parts by weight of white mud, 20 parts by weight of red mud and 15 parts by weight of field mud; , to obtain the green body raw material;

[0046] Described glaze slurry is prepared by the following method: the glaze stone of 70 weight parts, the potassium feldspar of 8 weight parts and the lychee wood ash of 12 weight parts and the limestone of 12 weight parts are mixed, add the water of 3 times by weight and put into ball mill and grind, Then pass through a 90-mesh sieve to obtain glaze slurry;

[0047] Described lychee wood ash is prepared by the following method: burning dry lychee wood to obtain ashes, and the ashes pass through a 90-mesh sieve to obtain lychee wood ash.

[0048] (2) drawing, trimming, bisque-firing and coolin...

Embodiment 2

[0062] Yaobian Jianzhan firing process includes the following steps:

[0063] (1) Preparation of green body raw materials and glaze;

[0064] The green body raw material is prepared by the following method: mixing, pulverizing, and elutriating 55 parts by weight of white mud, 10 parts by weight of red mud and 25 parts by weight of field mud; , to obtain the green body raw material;

[0065] Described glaze slurry is prepared by the following method: the glaze stone of 75 weight parts, the potassium feldspar of 9 weight parts and the lychee wood ash of 10 weight parts and the limestone of 10 weight parts are mixed, add the water of 3 times by weight and put into ball mill and grind, Then pass through an 80-mesh sieve to obtain a glaze slurry;

[0066] Described lychee wood ash is prepared by the following method: burning dry lychee wood to obtain ashes, and the ashes pass through an 80-mesh sieve to obtain lychee wood ash.

[0067] (2) drawing, trimming, bisque-firing and co...

Embodiment 3

[0080] Yaobian Jianzhan firing process includes the following steps:

[0081] (1) Preparation of green body raw materials and glaze;

[0082] The green body raw material is prepared by the following method: mixing, pulverizing, and elutriating 65 parts by weight of white mud, 30 parts by weight of red mud and 20 parts by weight of field mud, passing through an 80-mesh sieve, filter-pressing, refining mud, stale , to obtain the green body raw material;

[0083] Described glaze slurry is prepared by the following method: the glaze stone of 65 weight parts, the potassium feldspar of 5 weight parts and the lychee wood ash of 15 weight parts and the limestone of 15 weight parts are mixed, add the water of 2.5 weight times and put into ball mill and grind, Then pass through a 100-mesh sieve to obtain glaze slurry;

[0084] The lychee wood ash is prepared by the following method: burning dry lychee wood to obtain ashes, and passing the ashes through a 100-mesh sieve to obtain lyche...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a firing process for Yaobian Jianzhan, which comprises the following steps: preparing body raw materials and glaze materials, drawing the body raw materials into shape, trimming, biscuit firing, and cooling to obtain the body, glazing, and drying the glaze The final green body is put into the kiln for roasting, cooled naturally, and then out of the kiln. The formula, firing atmosphere, temperature curve and other technical processes of the invention are clear, easy to control, good in stability and high in yield. There are oil droplets of different sizes floating on the surface of the fired Yaobian Jianzhan, and there are red, green, sky blue and other colored halos around the outer edges of these oil droplets. , Just like the stars in the sky gathered in groups, the universe is changing, vast and profound, with extremely high artistic value and appreciation value.

Description

technical field [0001] The invention relates to the technical field of porcelain, in particular to a firing process of Yaobian Jianguan. Background technique [0002] Jianzhan, because its origin is Jian'an County, Jianzhou Prefecture, is called Jianzhan. It prospered in the late Northern Song Dynasty and the early and middle stages of the Southern Song Dynasty. It was the royal tea set in the Song Dynasty. [0003] The observable change is that oil droplets of different sizes appear on the glaze surface of the Jianzhan with a thick black glaze, and the oil droplets are surrounded by a halo-like brilliance, which is colorful and splendid, and seems to have a dazzling halo. Changeable, as magnificent as a rainbow. Yaobian Jianzhan is the top grade of Jianzhan. [0004] Yaobian Jianzhan should have the following characteristics: [0005] 1. The green body contains iron, the glaze layer is thick, and it is fired at high temperature; [0006] 2. One-time glazing and one-time...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/24C03C8/00C04B41/86C04B33/34
CPCC04B33/13C04B33/24C03C8/00C04B41/86C04B41/5022C04B33/34C04B2235/661
Inventor 陆金喜
Owner 陆金喜
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com