Preparation method of high-strength PP material containing coffee grounds

A coffee grounds, high-strength technology, applied in the textile field, can solve the problem of high cost, and achieve the effect of eliminating sink marks, delaying the burning speed, and accelerating the crystallization speed.

Inactive Publication Date: 2020-04-14
咖法科技(上海)有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, such treatment requires additional preparatio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-strength PP material containing coffee grounds
  • Preparation method of high-strength PP material containing coffee grounds
  • Preparation method of high-strength PP material containing coffee grounds

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Add 40 parts of copolymerized PP, 43 parts of coffee grounds, 7 parts of talcum powder, 0.3 parts of ultraviolet absorber, 0.4 parts of antioxidant, and 0.3 parts of ethylene bisstearamide into the high-speed mixing tank to mix them evenly; then, in the double Screw extruder mixing, the temperature of each section of the twin-screw is: T1 = 160 ° C, T2 = 170 ° C, T3 = 175 ° C, T4 = 180 ° C, T5 = 185 ° C, T6 = 190 ° C, twin-screw extrusion The rotation speed of the machine is r=350r.min-1. Finally, a high-strength PP material containing coffee grounds is obtained through extrusion, cooling and pelletizing.

Embodiment 2

[0029] Add 45 parts of copolymerized PP, 45 parts of coffee grounds, 9 parts of talcum powder, 0.3 parts of ultraviolet absorber, 0.4 parts of antioxidant, and 0.3 parts of ethylene bisstearamide into the high-speed mixing tank to mix them evenly; then, in the double Screw extruder mixing, the temperature of each section of the twin-screw is: T1 = 160 ° C, T2 = 170 ° C, T3 = 175 ° C, T4 = 180 ° C, T5 = 185 ° C, T6 = 190 ° C, twin-screw extrusion The rotation speed of the machine is r=350r.min-1. Finally, a high-strength PP material containing coffee grounds is obtained through extrusion, cooling and pelletizing.

Embodiment 3

[0031] Add 35 parts of copolymerized PP, 40 parts of coffee grounds, 5 parts of talcum powder, 0.3 parts of ultraviolet absorber, 0.4 parts of antioxidant, and 0.3 parts of ethylene bisstearamide into the high-speed mixing tank to mix them evenly; then, in the double Screw extruder mixing, the temperature of each section of the twin-screw is: T1 = 160 ° C, T2 = 170 ° C, T3 = 175 ° C, T4 = 180 ° C, T5 = 185 ° C, T6 = 190 ° C, twin-screw extrusion The rotation speed of the machine is r=350r.min-1. Finally, a high-strength PP material containing coffee grounds is obtained through extrusion, cooling and pelletizing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosity average molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-strength PP material containing coffee grounds. The high-strength PP material comprises the following components: 35-45% of copolymerized PP, 30-45% of the coffee grounds, 5-10% of talcum powder, 0.2-0.4% of an ultraviolet light absorber, 0.2-0.4% of an antioxidant and 0.2-0.5% of a lubricant. The method comprises the following steps: adding the components into a mixing cylinder according to the ratio, and uniformly mixing; adding the mixture into a double-screw extruder for mixing; wherein the extrusion temperature of the first section and the second section of the double-screw extruder is 160-170 DEG C, the extrusion temperature of other sections is 170-190 DEG C, and the total residence time of reactants in the double-screw extruder is 3-5 minutes; and finally, extruding the obtained material, cooling and dicing to obtain the high-strength PP material containing the coffee grounds. By modifying PP, environmental protection and flame retardance are achieved, and the outdoor long-term anti-aging use requirement can be met.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a method for preparing high-strength PP material containing coffee grounds. Background technique [0002] Polypropylene, referred to as PP, is a colorless, odorless, non-toxic, translucent solid substance. [0003] Polypropylene (PP) is a thermoplastic synthetic resin with excellent performance, which is a colorless and translucent thermoplastic lightweight general-purpose plastic. With chemical resistance, heat resistance, electrical insulation, high-strength mechanical properties and good high wear-resistant processing properties, etc., polypropylene has been rapidly used in machinery, automobiles, electronic appliances, construction, textiles, and packaging since its inception. It has been widely developed and applied in many fields such as agriculture, forestry, fishery and food industry. [0004] In recent years, with the rapid development of my country's pack...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/14C08L99/00C08K13/02C08K3/34C08K5/134C08K5/526C08K5/20C08L67/04
CPCC08L23/14C08L67/04C08L99/00C08L2201/02C08L2201/08C08L2201/22C08K13/02C08K3/34C08K5/1345C08K5/526C08K5/20
Inventor 江骐全邹勇俞健
Owner 咖法科技(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap