High-temperature-resistant polyvinyl chloride/nitrile rubber composite cable material

A polyvinyl chloride and nitrile rubber technology, applied in the field of cable materials, can solve problems such as poor heat resistance, achieve good cost performance, improve temperature resistance, and expand the scope of use.

Active Publication Date: 2020-04-21
CGN DELTA (ZHONGSHAN) POLYMER CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies in the prior art, the present invention provides a high temperature resistant polyvinyl chloride / nitrile rubber composite cable material, the purpose of which is to solve the problem of poor heat resistance of the polyvinyl chloride / nitrile rubber composite cable material system, and to provide Oil resistance of the material combined with high temperature resistance, good flexibility, wear resistance to provide a new solution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant polyvinyl chloride/nitrile rubber composite cable material
  • High-temperature-resistant polyvinyl chloride/nitrile rubber composite cable material
  • High-temperature-resistant polyvinyl chloride/nitrile rubber composite cable material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] The present invention will be further described below in conjunction with embodiment:

[0040] The composition of the raw materials for implementation 1-4 is shown in Table 1, and the numerical values ​​of the composition of the raw materials in Table 1 are all parts by weight.

[0041] The raw material formula of table 1 embodiment 1-4 cable material:

[0042]

[0043]

[0044] Table 2: is the name of each component raw material used in the embodiment:

[0045]

[0046] In Example 1 of the above table, "M" means 6-(2-benzotriazolyl)-4-tert-amyl-6'-tert-butyl-4'-methyl-2,2'- methylene diphenol.

[0047] The production process of Example 1-4 of the present invention is carried out according to the following steps: the first step, preparation of raw and auxiliary materials; the second step, metering and weighing according to the formula ratio; the third step, high-speed kneading; the fourth step, twin-screw extrusion unit Carry out extrusion mixing and plastic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A high-temperature-resistant polyvinyl chloride / nitrile rubber composite cable material comprises the following components in parts by weight: 100 parts of polyvinyl chloride, 20-50 parts of nitrile rubber, 20-40 parts of a plasticizer a, 20-30 parts of a plasticizer b, 5-10 parts of a flame retardant a, 5-20 parts of a flame retardant b, 10-40 parts of a filler a, 20-30 parts of a filler b, 2-10parts of a heat stabilizer, 0.5 to 2 parts of a lubricant, 0.2 to 0.8 part of an antioxidant a, 0.2 to 0.8 part of an antioxidant b, 0.2 to 0.8 part of an antioxidant c, and 1-3 parts of a processingmodifier. According to the invention, the problem of poor heat resistance of a polyvinyl chloride / nitrile rubber composite cable material system is solved, the temperature resistance grade is improvedto 105 DEG C from the original 80 DEG C, and the cable material can be applied to high-flexibility and high-toughness mobile cables such as household oil-resistant occasions, locomotive cables, robotcables and the like.

Description

technical field [0001] The invention belongs to the technical field of cable materials, and in particular relates to a high-temperature-resistant polyvinyl chloride / nitrile rubber composite cable material. The cable material can be widely used in the wire and cable industry as a soft wire insulation material and sheath material. Background technique [0002] Polyvinyl chloride (PVC) is a halogen-containing polymer material. Pure PVC granular material has high mechanical strength, very good weather resistance, water resistance, chemical resistance and good electrical insulation properties. Although this material is sensitive to light and heat, the stability of PVC resin against light and heat can be improved by adding a stabilizer. [0003] With the improvement of the production capacity of PVC resin, plasticizer and industrial additives and the development and application of environmentally friendly products, the application of PVC in wire and cable has made a qualitative l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L9/02C08L79/04C08K13/02C08K5/3475C08K5/01C08K5/18C08K5/1545
CPCC08L27/06C08L2205/03C08L2201/08C08L2203/202C08L9/02C08K13/02C08K5/3475C08K5/01C08K5/18C08L79/04C08K5/1545
Inventor 聂政黄玉龙廖小军刘泽华卢志生
Owner CGN DELTA (ZHONGSHAN) POLYMER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com