Composition for crease-resistant finishing of polyester cotton garment

A technology of anti-wrinkle finishing and composition, which is applied in liquid/gas/steam finished product treatment, fiber treatment, plant fiber, etc. It can solve the problems of poor hydrophilicity and uncomfortable wearing, so as to improve production efficiency, shorten the soaking time, Easy to reuse effects

Inactive Publication Date: 2020-04-28
江阴创杰佳服装有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the fabric samples finished with anti-wrinkle resin and softener still have disadvantages such as poor hydrophilicity and uncomfortable wearing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The steps of a composition for anti-wrinkle finishing of polyester-cotton garments are as follows:

[0027] S1. Alkaline washing: Soak the sewn polyester-cotton blended garment in a 15% NaOH aqueous solution for 5-10 minutes, remove it, wash it with clean water several times, and then spin it to dry, and at the same time it will be removed during the sewing process. Contaminated stains and the effect of changing the molecular structure of polyester-cotton blended fibers;

[0028] S2. Stacking: the polyester-cotton blended garments described in step S1 are laid flat and stacked one by one, and then placed on the special auxiliary drug-dipping tooling;

[0029] S3. Dispensing: formulating the required anti-wrinkle finishing composition for polyester-cotton garments, including a concentration of 90g / L polyterpene resin, 80g / L polyether modified silicone finishing agent, 7g / L silicone crosslinking agent, 0.5g / L organic acid;

[0030] S4. Preparation: inject the composition for ant...

Embodiment 2

[0038] The steps of a composition for anti-wrinkle finishing of polyester-cotton garments are as follows:

[0039] S1. Alkaline washing: Soak the sewn polyester-cotton blended garment in a 15% NaOH aqueous solution for 10 minutes, take it out, wash it with clean water several times, and then spin it to dry, and at the same time, it can remove contaminants during sewing. Stains and the effect of changing the molecular structure of polyester-cotton blended fibers;

[0040] S2. Stacking: the polyester-cotton blended garments described in step S1 are laid flat and stacked one by one, and then placed on the special auxiliary drug-dipping tooling;

[0041] S3. Dispensing: formulating the desired anti-wrinkle finishing composition for polyester-cotton garments, including a concentration of 100g / L polyterpene resin, 130g / L polyether modified silicone finishing agent, 40g / L silicone crosslinking agent, 1.5g / L organic acid;

[0042] S4. Preparation: inject the composition for anti-wrinkle fini...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a composition for crease-resistant finishing of a polyester cotton garment. The composition is prepared by taking deionized water as a solvent and comprises 90-100g / L of polyterpene resin, 80-130g / L of polyether modified organic silicon finishing agent, 7-40g / L of organic silicon cross-linking agent and 0.5-1.5 g / L of organic acid. The crease-resistant finishing compositionis combined with the special auxiliary tool for medicine soaking and the medicine soaking circulating pool so that a better crease-resistant effect can be achieved, and the economic cost and the timecost of production can be reduced for enterprises. The polyester cotton garment obtained by adopting the crease-resistant after-finishing method does not contain formaldehyde and is good in size and shape stability and can completely meet the requirements of customers for pursuing environmental protection and nature. The crease-resistant finishing agent is green and environment-friendly, the process is simple and reliable, and the requirements of energy conservation and emission reduction of dyeing plants are met.

Description

Technical field [0001] The invention relates to the technical field of clothing processing, in particular to a composition for anti-wrinkle finishing of polyester-cotton garments. Background technique [0002] Polyester cotton refers to the general term for blended fabrics of polyester and cotton, fabrics woven with 65% to 67% polyester and 33% to 35% cotton blended yarn. Cotton, as one of the representatives of natural fibers, has natural and comfortable characteristics; polyester cotton, as one of the representatives of natural and synthetic fiber blended fibers, has the natural comfort of pure cotton and the high strength of polyester fibers and can be washed and worn. The effect has two advantages. Therefore, it is more and more popular. But the main disadvantage of cotton and polyester cotton is that they are easy to wrinkle and shrink after washing. [0003] With the improvement of the people's living standards, the people's concept of clothing has undergone major changes....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/21D06M15/647D06M15/643D06M13/50D06M13/184D06B3/30D06B15/00D06C27/00D06M101/06D06M101/32
CPCD06B3/30D06B15/00D06C27/00D06M13/184D06M13/50D06M15/21D06M15/643D06M15/647D06M2101/06D06M2101/32D06M2200/20
Inventor 陶晓华
Owner 江阴创杰佳服装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com