Boron-doped non-metal catalyst as well as preparation method and application thereof

A non-metallic catalyst and boron-doped technology, which is applied in chemical instruments and methods, physical/chemical process catalysts, chemical/physical processes, etc., can solve problems such as loss of catalytic effect, sludge, and degradation of reusable performance, and achieve cost reduction Low cost, cost reduction, cost and environmental friendliness

Pending Publication Date: 2020-05-08
TAIYUAN UNIV OF TECH
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition to heavy metal pollution, metal dissolution may also lead to a serious loss of catalytic effect, a decrease in recycling performance, and a large amount of sludge.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Boron-doped non-metal catalyst as well as preparation method and application thereof
  • Boron-doped non-metal catalyst as well as preparation method and application thereof
  • Boron-doped non-metal catalyst as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] The specific implementation manner of the present invention will be further described in detail through the description of various embodiments below. Apparently, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by those skilled in the art without making creative efforts belong to the protection scope of the present invention.

[0035] A kind of preparation of boron-doped non-metallic catalyst:

[0036] According to the data in Table 1, 1.0 g of carbon nanotubes was added to 100 mL of nitric acid solution, heated to reflux in an oil bath at 80°C for 4 h, filtered and washed repeatedly with ultrapure water until neutral to obtain intermediate 1, and intermediate 1 Disperse in 50 mL of absolute ethanol, add 1.0 g of boron-containing precursor, heat and stir in an oil bath at 80 °C for 4 h, after the reaction, filter and wash repeatedly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a boron-doped non-metal catalyst as well as a preparation method and application thereof. The preparation method comprises the following steps: adding a carbon material into anacid solution, heating and soaking the carbon material, filtering the solution, and washing the carbon material with ultrapure water, and drying the carbon material; dispersing the material into a volatile solvent, adding a boron-containing precursor, heating the material in an oil bath, washing the material with ultrapure water after the reaction is finished, and drying a product; and roasting the product in a non-oxidizing atmosphere to obtain the boron-doped non-metal catalyst. The low-toxicity boron-doped non-metal catalyst is used for replacing a high-toxicity heavy metal catalyst, has the characteristic of environmental friendliness, has a good degradation and removal effect on organic pollutants, and shows extremely high catalytic activity and a wide application range.

Description

technical field [0001] The invention relates to the technical field of catalyst materials, in particular to a boron-doped non-metallic catalyst and its preparation method and application. Background technique [0002] In recent decades, with the rapid development of industry and the improvement of people's living standards, many new chemicals have continuously entered the environment. These pollutants have the characteristics of low concentration, high toxicity, and refractory biodegradation, which are difficult to remove through conventional treatment techniques. May cause serious impact on the ecological environment. The advanced oxidation technology based on sulfate radical is a kind of strong oxidizing sulfate radical (SO 4 ●− ) The water treatment technology for degrading organic pollutants has the advantages of environmental friendliness, simple equipment and fast response, and has great application potential in water treatment, soil remediation, sludge disposal and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J21/18B01J35/02C02F1/72C02F101/30C02F101/34
CPCB01J21/185B01J35/023C02F1/725C02F2101/345C02F2305/023C02F2101/30
Inventor 李兴发梁丹丹
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap