Water-soluble electroplating brightener and preparation method thereof

A water-soluble brightener technology, applied in the field of water-soluble electroplating brightener and its preparation, can solve the problems of lack of coating current efficiency, elongation and tensile strength improvement effect, general hole filling effect, and physical injury of electroplating workers. Achieve the effects of reducing environmental pollution and harm to the body of electroplating workers, improving performance such as elongation and tensile strength, and saving manpower and equipment costs

Inactive Publication Date: 2020-05-08
浙江金欣新材料科技股份有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] 1. The electroplating brightener needs the help of organic solvents, which are easy to volatilize and difficult to handle, which can easily cause environmental pollution and physical injury to electroplating workers;
[0009] 2. The hole filling effect on the surface of the electroplating (electrogalvanizing) substrate is average, the gloss is not high, and the bright effect is not good;
[0010] 3. The function is single. In addition to achieving the bright effect, it lacks the effect of improving the current efficiency, elongation and tensile strength of the (electro-galvanized) coating, or the effect of the improvement is very small

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A water-soluble electroplating brightener, according to the volume fraction of each raw material in every liter of electroplating bath, comprises the following raw materials in parts by weight:

[0034] Main brightener 15mL / L, auxiliary brightener 12mL / L, inhibitor 1.5mL / L, leveling agent 9mL / L and other additives 0.7mL / L.

[0035] In this embodiment, the main brightener is sodium phenyldithiopropanesulfonate;

[0036] In this embodiment, the auxiliary brightener is epichlorohydrin;

[0037] In this embodiment, the inhibitor is hexamethylenetetramine;

[0038] In the present embodiment, the leveling agent is basic yellow;

[0039] In this embodiment, the other auxiliary agent is water-soluble benzotriazole.

[0040] In the present embodiment, the preparation method of the water-soluble electroplating brightener comprises the following steps:

[0041] A, according to the total volume of electroplating bath, calculate respectively the addition of each raw material of ...

Embodiment 2

[0044] A water-soluble electroplating brightener, according to the volume fraction of each raw material in every liter of electroplating bath, comprises the following raw materials in parts by weight:

[0045] Main brightener 25mL / L, auxiliary brightener 20mL / L, inhibitor 3.5mL / L, leveling agent 14mL / L and other additives 1.2mL / L.

[0046] In this embodiment, the main brightener is sodium phenyldithiopropanesulfonate;

[0047] In this embodiment, the auxiliary brightener is epichlorohydrin;

[0048] In this embodiment, the inhibitor is hexamethylenetetramine;

[0049] In the present embodiment, the leveling agent is basic yellow;

[0050] In this embodiment, the other auxiliary agent is water-soluble benzotriazole.

[0051] In the present embodiment, the preparation method of the water-soluble electroplating brightener comprises the following steps:

[0052] A, according to the total volume of electroplating bath, calculate respectively the addition of each raw material of...

Embodiment 3

[0055] A water-soluble electroplating brightener, according to the volume fraction of each raw material in every liter of electroplating bath, comprises the following raw materials in parts by weight:

[0056] Main brightener 18mL / L, auxiliary brightener 15.5mL / L, inhibitor 2.4mL / L, leveling agent 11mL / L and other additives 0.92mL / L.

[0057] In this embodiment, the main brightener is sodium phenyldithiopropanesulfonate;

[0058] In this embodiment, the auxiliary brightener is epichlorohydrin;

[0059] In this embodiment, the inhibitor is hexamethylenetetramine;

[0060] In the present embodiment, the leveling agent is basic yellow;

[0061] In this embodiment, the other auxiliary agent is water-soluble benzotriazole.

[0062] In the present embodiment, the preparation method of the water-soluble electroplating brightener comprises the following steps:

[0063]A, according to the total volume of electroplating bath, calculate respectively the addition of each raw material ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-soluble electroplating brightener. The water-soluble electroplating brightening agent comprises the following raw materials of, in parts by weight, 15-25 mL / L of a mainbrightener, 12-20 mL / L of an auxiliary brightener, 1.5-3.5 mL / L of an inhibitor, 9-14 mL / L of a leveling agent and 0.7-1.2 mL / L of other auxiliaries according to the volume fraction of each raw material in each liter of electroplating solution. The water-soluble electroplating brightener is composed of 100% water-soluble raw material, does not need an organic solvent, and can effectively reduce environmental pollution and harm to the body of an electroplating worker; the hole filling effect on the surface of an electroplating (electrogalvanizing) base material is good, the glossiness of a plating layer is high, and the bright effect is excellent; in addition, except for achieving the bright effect, the electric current efficiency, the elongation, the tensile strength and other propertiesof the (electrogalvanizing) coating are not greatly improved.

Description

technical field [0001] The invention relates to the technical field of additives for electroplating, in particular to a water-soluble electroplating brightener and a preparation method thereof. Background technique [0002] Electroplating is the process of plating a thin layer of other metals or alloys on the surface of certain metals using the principle of electrolysis. It is a process of using electrolysis to attach a layer of metal film to the surface of metal or other material parts to prevent metal oxidation ( Such as rust), improve wear resistance, electrical conductivity, reflective properties, corrosion resistance (copper sulfate, etc.) and enhance the appearance. [0003] The main function of the brightener is to remove the oil, oxidized and unoxidized surface impurities staying on the metal surface through the active surface, and to maintain the cleanliness, gloss and color fastness of the outside of the object. The texture of the appearance is affected by the gri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/22
CPCC25D3/22
Inventor 潘璐洁黄海宾
Owner 浙江金欣新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com