Preparation method of melt-spun profiled polyvinyl alcohol fibers

A polyvinyl alcohol fiber and polyvinyl alcohol technology, which is applied in fiber processing, fiber chemical characteristics, rayon manufacturing and other directions, can solve the problems of large irregularity and difficulty in obtaining controllable cross-section, and achieves large irregularity and improved Small effect of spinnability and shear viscosity change

Active Publication Date: 2020-05-15
SICHUAN UNIV
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a method for preparing melt-spun special-shaped polyvinyl alcohol fibers to solve the problem that it is difficult to obtain special-shaped polyvinyl alcohol fibers with a controllable cross-section, a large degree of special shape, and a high degree of special shape.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of melt-spun profiled polyvinyl alcohol fibers
  • Preparation method of melt-spun profiled polyvinyl alcohol fibers
  • Preparation method of melt-spun profiled polyvinyl alcohol fibers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] In the preparation method of the melt-spun special-shaped polyvinyl alcohol fiber in this embodiment, the special-shaped spinneret microholes of the spinneret adopt a four-lobed shape, and the degree of special shape is 50%. It includes the following steps:

[0045] (1) The chemically modified polyvinyl alcohol powder is melt-spun on extrusion-spinning equipment, and after melt-extruding, filtering and metering, it is sprayed from the special-shaped spinning micropores, and the melt is The special-shaped polyvinyl alcohol primary fiber is prepared by blowing and cooling on the side of the thin stream; wherein, the step of chemically modifying the polyvinyl alcohol powder includes: copolymerizing polyvinyl monomers on the polyvinyl alcohol molecular chain.

[0046] Among them, the spinning temperature is 165°C; the spinning shear rate is 10000s -1 ; Spinning shear viscosity is 300Pa.s; spinning pressure is 25MPa; spinning volume flow rate is 300mm 3 / s; spinneret draw ...

Embodiment 2

[0050] In the preparation method of the melt-spun special-shaped polyvinyl alcohol fiber in this embodiment, the special-shaped spinneret microholes of the spinneret are flat and wavy, and the degree of special shape is 90%. It includes the following steps:

[0051] (1) The chemically modified polyvinyl alcohol powder is melt-spun on extrusion-spinning equipment, and after melt-extruding, filtering and metering, it is sprayed from the special-shaped spinning micropores, and the melt is The special-shaped polyvinyl alcohol primary fiber is prepared by blowing and cooling on the side of the thin stream; wherein, the step of chemically modifying the polyvinyl alcohol powder includes: grafting n-butyl boric acid on the polyvinyl alcohol molecular chain.

[0052] Among them, the spinning temperature is 180°C; the spinning shear rate is 6000s -1 ; Spinning shear viscosity is 200Pa.s; spinning pressure is 30MPa; spinning volume flow rate is 250mm 3 / s; the draw ratio of the spinner...

Embodiment 3

[0056] In the preparation method of the melt-spun special-shaped polyvinyl alcohol fiber in this embodiment, the special-shaped spinneret microholes of the spinneret adopt a trilobal shape, and the degree of special shape is 75%. It includes the following steps:

[0057] (1) The physically modified polyvinyl alcohol powder is melt-spun on extrusion-spinning equipment, and after melt-extruded, filtered and metered, it is ejected from the micro-pores of the special-shaped spinneret, and the melt is Cooling with side air blowing in a thin stream to prepare shaped polyvinyl alcohol primary fibers; wherein, the step of physically modifying polyvinyl alcohol powder includes: mixing and compounding glycerin, starch and polyvinyl alcohol according to the mass ratio of 10:30:60 to obtain modified polyvinyl alcohol fibers. Non-toxic polyvinyl alcohol powder.

[0058] Among them, the spinning temperature is 175°C; the spinning shear rate is 2000s -1 ; Spinning shear viscosity is 150Pa....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Irregularityaaaaaaaaaa
Irregularityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of melt-spun profiled polyvinyl alcohol fibers, and belongs to the technical field of preparation of profiled polyvinyl alcohol fibers. The preparation method comprises the following steps of: carry out melt spinning on modified polyvinyl alcohol powder on extruding-spinning equipment, after melt extruding, filtering and metering, ejecting from a spinneret plate with profiled spinneret micropores, and carrying out blowing cooling on a melt trickle side to prepare profiled polyvinyl alcohol as-formed fibers; and after carrying out multi-stage stretching, wet heat stretching or dry heat stretching and heat setting on the profiled polyvinyl alcohol as-formed fibers, preparing the melt-spun profiled polyvinyl alcohol fibers. According to the preparation method of the melt-spun profiled polyvinyl alcohol fibers, which is disclosed by the invention, stable and continuous melt spinning on the polyvinyl alcohol fibers is implemented, the as-formed fibers of which the sections are of a triangle, three-leaf, four-leaf or flat wave shape can be obtained, the melt-spun profiled polyvinyl alcohol fibers capable of being used for a reinforced toughened composite material are successfully prepared by subsequent stretching and heat setting processes, and the melt-spun profiled polyvinyl alcohol fibers are high in strength and good in profiled shaperetention.

Description

technical field [0001] The invention relates to the technical field of preparation of special-shaped polyvinyl alcohol fibers, in particular to a preparation method of melt-spun special-shaped polyvinyl alcohol fibers. Background technique [0002] Shaped fiber is a kind of differentiated fiber with special cross-sectional shape and function spun by special method. Ordinary circular cross-section fibers have weak surface gloss and waxy feeling, and have disadvantages such as easy to get dirty, easy to pilling, non-absorbent, and small coverage. Compared with the circular cross-section fiber, the chemical composition of the special-shaped cross-section fiber has not changed, but the change of the cross-sectional shape of the fiber endows the special-shaped fiber with better performance characteristics than ordinary chemical fibers. Such as unique luster and stain resistance, different hand feeling and excellent anti-pilling properties, the fabric woven by it is thicker, fluf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/34D01F6/14D01F6/50D01F1/10D01D5/253
CPCD01F6/34D01F6/14D01F6/50D01F1/10D01D5/253
Inventor 陈宁王萌王琪李莉周婷
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap