Reclaimed rubber particle permeable asphalt concrete and preparation method thereof

A technology of permeable asphalt and reclaimed rubber, applied in the field of road materials, can solve the problems of low strength of permeable pavement, poor anti-frost heave ability, insufficient durability, etc. Effect

Active Publication Date: 2020-06-09
CHINA TIESIJU CIVIL ENG GRP CO LTD +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of recycled colloidal permeable asphalt concrete and its preparation method, which are used to solve the problems of low strength, insufficient durability, poor frost heave resistance and easy clogging of pores in traditional permeable pavement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reclaimed rubber particle permeable asphalt concrete and preparation method thereof
  • Reclaimed rubber particle permeable asphalt concrete and preparation method thereof
  • Reclaimed rubber particle permeable asphalt concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The invention provides a method for preparing permeable asphalt concrete with recycled rubber particles, comprising the following steps:

[0036] S1, heat the base asphalt to a certain temperature, add the extension agent while stirring, then add SBS and composite stabilizer, keep the temperature constant and continue stirring to obtain the modified asphalt mixture.

[0037] In a specific embodiment of the present invention, the extension agent in step S1 is one or more of rubber oil, furfural oil, waste engine oil, biomass pitch and heavy mineral oil;

[0038] Composite stabilizer comprises the component of following parts by weight: sulfur powder 40-90 parts (such as 40 parts, 45 parts, 50 parts, 55 parts, 60 parts, 65 parts, 70 parts, 75 parts, 80 parts, 85 parts, 90 parts parts), organic sulfur 10-40 parts (such as 10 parts, 15 parts, 20 parts, 25 parts, 30 parts, 35 parts, 40 parts), polyvinyl alcohol 10-20 parts (such as 10 parts, 11 parts, 12 parts , 13 parts, 1...

Embodiment 1

[0067] This embodiment provides a method for preparing permeable asphalt concrete with recycled rubber particles, which includes the following steps:

[0068] S1, add 100 parts by mass of base asphalt into a mixing tank and heat to 185°C, add 2.5 parts by mass of rubber oil while stirring, then add 6 parts by mass of SBS and 0.15 parts by mass of composite stabilizer, and keep the temperature at 150°C constant Continue to stir to obtain the mixture; wherein the composite stabilizer includes the following components by weight: 60 parts of sulfur powder, 25 parts of organic sulfur, 15 parts of polyvinyl alcohol, 15 parts of stearyl benzoyl methane and 5 parts of nano-zinc oxide ;

[0069] S2, placing the mixture obtained in step S1 in a colloid mill for shearing, storing and developing at 150° C. for 7 hours, and finally obtaining SBS modified asphalt;

[0070] S3, adding 10 parts by mass of old tire rubber powder particles to the SBS modified asphalt in step S2, stirring at 19...

Embodiment 2

[0083] This embodiment provides a method for preparing permeable asphalt concrete with regenerated rubber particles. The difference between this embodiment and Embodiment 1 is that in step S4, the mass ratio of SBS regenerated rubber particles modified asphalt to different graded batches is changed. That is to change the asphalt ratio of recycled rubber particle permeable asphalt concrete with different gradations. The oil-stone ratio of PAC20 recycled rubber particle permeable asphalt concrete is 4.5%, 5%, 5.5% and 6%. The oil-stone ratio of PAC16 recycled rubber particle permeable asphalt concrete is 4.5%, 5%, 5.5% and 6%, the oil-stone ratio of PAC13 recycled rubber particle permeable asphalt concrete is 5%, 5.5%, 6% and 6.5%, the oil-stone ratio of PAC10 recycled rubber particle permeable asphalt concrete is 5%, 5.5% %, 6% and 6.5%; the mass percentages of each component in batches of different grades are shown in Table 5 below.

[0084] The mass percent of each component ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
stabilityaaaaaaaaaa
porosityaaaaaaaaaa
Login to view more

Abstract

The invention provides reclaimed rubber particle permeable asphalt concrete and a preparation method thereof. The preparation method comprises the following steps that S1, a modifier and various auxiliaries are added into matrix asphalt to be stirred and sheared, and a mixture is obtained; S2, storing and developing are carried out to prepare SBS modified asphalt; S3, the SBS regenerated rubber particle modified asphalt is prepared; and S4, the regenerated rubber particle permeable asphalt concrete is prepared. After the regenerated rubber particles are mixed with the SBS modified asphalt, light components in the modified asphalt are absorbed, and the viscosity of the modified asphalt is increased, so that the thickness of a coating aggregate asphalt film is increased, and the cohesive force among aggregate particles is effectively improved. The colloidal particles have excellent elastic performance; when internal pores of the water-permeable asphalt concrete are frozen and heaved at extreme temperature, the freezing and thawing resistance of the water-permeable asphalt concrete is improved, the durability of the water-permeable asphalt concrete is improved, the pore distribution of the water-permeable asphalt concrete can be optimized by the reasonably graded rubber particles, the pore blockage of the water-permeable asphalt concrete is delayed, and the water-permeable function of the water-permeable asphalt concrete is guaranteed.

Description

technical field [0001] The invention belongs to the technical field of road materials, and in particular relates to a recycled rubber particle permeable asphalt concrete and a preparation method thereof. Background technique [0002] With the rapid increase of the level of urbanization in our country, the area of ​​hardened pavement has increased sharply, which not only destroys the original ecosystem, but also changes the original natural ecological background and hydrological characteristics of the city. More than 70% of the rainfall forms runoff and is discharged. As a result, the city cannot store water, and there is a phenomenon that the heavy rain must be fished, and the phenomenon of drought immediately after the rain occurs. Sponge city is a historic and strategic step to realize the six-in-one comprehensive drainage and ecological drainage of "seepage, stagnation, storage, purification, use, and drainage" from the era of fast drainage, timely and nearby drainage, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/26
CPCC04B26/26C04B2111/00008C04B2111/00284C04B2111/0075C04B2201/50C04B24/001C04B24/00C04B2103/0068C04B22/02C04B24/16C04B24/2623C04B24/08C04B22/06C04B18/22
Inventor 查显卫周江孟会含黄建波肖飞鹏王金刚郭瑞
Owner CHINA TIESIJU CIVIL ENG GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap