Energy bone china vacuum cup and preparation process thereof

A preparation process and technology of thermos cups, which are applied in the production of clay products, other household utensils, ceramic materials, etc., can solve the problems of poor thermal insulation performance of thermos cups, low antibacterial and antibacterial effects, and inability to ensure the safety of drinking water for users, etc., to achieve Effect of activating water quality and promoting blood circulation

Inactive Publication Date: 2020-07-10
东莞醇原纳米新材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides an energy bone china thermos cup and its preparation process, which solves the problem that the existing thermos cup has poor thermal insulation performance, and the antibacterial and antibacterial effect is not high, and the safety of drinking water for users cannot be guaranteed. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Energy bone china vacuum cup and preparation process thereof
  • Energy bone china vacuum cup and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Prepare 50g of clay, 20g of bovine bone powder, 10g of six-ring stone powder (purchased from Shijiazhuang Zhuzhong Technology Co., Ltd., model LHS003), 8g of medical stone powder (purchased from Shijiazhuang Zhuzhong Technology Co., Ltd., model MFS102), 6g of titanium dioxide, and lanthanide rare earth 2g of compound salt (purchased from Shijiazhuang Zhuzhong Technology Co., Ltd.), 1.5g of nano-silver ion material (purchased from Hope Biotechnology Model: H-AG-F12500), and then the above raw materials were mixed together and ground by a three-roller machine to prepare The molding mud with a particle size of 400 meshes was obtained; the molding mud was made into the shape of a thermos cup liner, and the first biscuit firing was carried out at a temperature of 800 ° C for 8 hours to obtain a green body of a bone china thermos cup; a raw bone china thermos cup The blank is evenly glazed with bright glaze, and then glazed for the second time; the temperature is 1350 ° C, and...

Embodiment 2

[0029] Prepare 50g of clay, 20g of bovine bone powder, 9g of hexacyclic stone powder (purchased from Shijiazhuang Zhuzhong Science and Technology Co., Ltd., model LHS003), 9g of medical stone powder (purchased from Shijiazhuang Zhuzhong Science and Technology Co., Ltd., model MFS102), 6g of titanium dioxide, and lanthanide rare earth 1.5g of compound salt (purchased from Shijiazhuang Zhuzhong Technology Co., Ltd.), 2g of nano-silver ion material (purchased from Hope Biotechnology Model: H-AG-F12500), and then the above raw materials were mixed together and ground by a three-roller machine to prepare The molding mud with a particle size of 400 meshes was obtained; the molding mud was made into the shape of a thermos cup liner, and the first biscuit firing was carried out at a temperature of 850 ° C for 8 hours to obtain a green body of a bone china thermos cup; a raw bone china thermos cup The blank is evenly glazed with bright glaze, and then glazed for the second time; the tem...

Embodiment 3

[0032] Prepare 50g of clay, 20g of bovine bone powder, 10g of six-ring stone powder (purchased from Shijiazhuang Zhuzhong Technology Co., Ltd., model LHS003), 10g of medical stone powder (purchased from Shijiazhuang Zhuzhong Technology Co., Ltd., model MFS102), 6g of titanium dioxide, and lanthanide rare earth 2g of compound salt (purchased from Shijiazhuang Zhuzhong Technology Co., Ltd.), 2g of nano-silver ion material (purchased from Hope Biotechnology Model: H-AG-F12500), and then the above raw materials were mixed together and ground by a three-roll machine to obtain Molding mud with a particle size of 400 meshes; make the molding mud into the shape of the inner liner of the thermos cup, and perform the first biscuit firing at a temperature of 900°C for 9 hours to obtain a green body of a bone china thermos cup; a green body of a bone china thermos cup Apply bright glaze evenly, and then conduct the second glaze firing; the temperature is 1350 ° C, and the time is 13 hours,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an energy bone china vacuum cup and a preparation process thereof. The raw materials of the energy bone china vacuum cup comprise the following components in parts by weight: 50-60 parts of clay, 20-25 parts of bovine bone meal, 8-10 parts of hexacyclic stone powder, 8-10 parts of medical stone powder, 6-10 parts of titanium dioxide, 1.5-2 parts of lanthanide rare earth composite salt and 1.5-2 parts of nano-silver ion materials, wherein the lanthanide series rare earth composite salt is one or a combination of two of lanthanide series rare earth magnesium phosphate orlanthanide series rare earth silver fluoride, and the nano-silver ion material is a nano-silver ion-containing material obtained by mixing nano-silver powder into a fiber material and carrying out drying treatment, and the invention relates to the technical field of bone china vacuum cups. According to the energy bone china vacuum cup and the preparation process thereof, the manufactured bone china vacuum cup contains the hexacyclic stone powder and the medical stone powder, negative ions can be generated, the negative ion concentration detection numerical value can reach 800-1000 / cm < 3 >, blood circulation is promoted, water quality is activated, silver ions have the sterilization and disinfection effects, escherichia coli and staphylococcus aureus can be effectively killed, and the goodantibacterial effect is achieved.

Description

technical field [0001] The invention relates to the technical field of bone china thermos cups, in particular to an energy bone china thermos cup and a preparation process thereof. Background technique [0002] The thermos cup is simply a cup that can keep warm. It is generally a water container made of ceramics or stainless steel with a vacuum layer. There is a cover on the top and it is tightly sealed. To achieve the purpose of heat preservation, the thermos cup is developed from the thermos bottle to achieve the purpose of heat preservation. The appearance of the thermos cup is smooth and odorless, and the inside and outside are made of stainless steel. The seam and sealing performance are good, and it has good heat preservation performance. It can put ice cubes or hot drinks. During the use of the thermos cup, avoid collision and impact, so as not to damage the cup body or plastic, causing insulation failure or water leakage. Tighten the screw. Use appropriate force whe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B41/86A47G19/22
CPCA47G19/2205A47G2400/022C04B33/132C04B41/5022C04B41/86C04B2235/3206C04B2235/3224C04B2235/3232C04B2235/3291C04B2235/3463C04B2235/408Y02P40/60
Inventor 余玉生代飞王学大
Owner 东莞醇原纳米新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com