Method of Catecholamine Polymer for Inhibiting Crystal Transformation of ε-cl-20 Crystal and Highly Anti-crystal Transformation Property of ε-cl-20 Crystal

A technology of CL-20 and catecholamines, which is applied in the field of CL-20 modification, can solve the problems of complex process and limited effect of increasing the crystal transformation temperature of CL-20, and achieve the effect of good safety and simple operation

Inactive Publication Date: 2021-10-29
BEIJING INSTITUTE OF TECHNOLOGYGY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the conventional coating of CL-20 with natural rubber, butadiene rubber, EPDM rubber, etc. can increase the crystal transition temperature of CL-20 to a certain extent (about 15-20°C), but this method The process is complicated and the effect of increasing the crystal transformation temperature of CL-20 is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of Catecholamine Polymer for Inhibiting Crystal Transformation of ε-cl-20 Crystal and Highly Anti-crystal Transformation Property of ε-cl-20 Crystal
  • Method of Catecholamine Polymer for Inhibiting Crystal Transformation of ε-cl-20 Crystal and Highly Anti-crystal Transformation Property of ε-cl-20 Crystal
  • Method of Catecholamine Polymer for Inhibiting Crystal Transformation of ε-cl-20 Crystal and Highly Anti-crystal Transformation Property of ε-cl-20 Crystal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] (1) Weigh 0.2 g of dopamine, dissolve it in 300 mL of Tris-HCl buffer (10 mM, pH=8.5) and stir for 10 min, so that dopamine is fully dissolved in Tris-HCl buffer to obtain a dopamine solution;

[0041] (2) Weigh 19.8g of ε-CL-20 crystal material (particle size is 150~300μm), add it into the dopamine solution, stir and react at room temperature (25°C) and 180r / min for 12h, during the reaction process Observe that the color of the system changes from transparent to dark brown;

[0042] (3) The suspension obtained after the reaction was suction-filtered, the obtained solid material was washed with absolute ethanol, and then dried in an oven at 50° C. for 6 hours to obtain ε-CL-20 crystals with high crystal transformation resistance.

Embodiment 2

[0044] The ε-CL-20 crystal with high anti-crystal transformation property was prepared according to the method of Example 1, except that levodopa was used instead of dopamine.

Embodiment 3

[0046] The high crystal transformation resistance ε-CL-20 crystal was prepared according to the method of Example 1, except that 6-hydroxydopamine was used instead of dopamine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for inhibiting the crystal transformation of ε-CL-20 crystal by a catecholamine polymer and an ε-CL-20 crystal with high crystal transformation resistance, belonging to the technical field of CL-20 modification. The present invention utilizes the self-polymerization characteristics of catecholamines to form a catecholamine polymer coating layer on the surface of ε-CL-20 crystal raw material, and can effectively inhibit the ε-CL-20 crystal and catecholamine polymer content within a specific range CL‑20 crystal transformation; compared with the ε‑CL‑20 crystal raw material, after being treated by the method provided by the invention, the crystal transformation temperature of the obtained product will increase by 35-40°C. In addition, the method provided by the invention is simple to operate, has good safety and is suitable for large-scale production.

Description

technical field [0001] The invention relates to the technical field of CL-20 modification, in particular to a method for inhibiting the crystal transformation of ε-CL-20 crystal by a catecholamine polymer and an ε-CL-20 crystal with high crystal transformation resistance. Background technique [0002] Hexanitrohexaazaisowurtzitane (HNIW or CL-20) is a polymorphic compound with high energy density. There are four crystal forms under normal temperature and pressure conditions, namely α, β, γ and ε, of which ε The crystal form has the highest density, the highest energy, and the lowest sensitivity, and has the most application prospects. In terms of thermodynamics, the ε crystal form is the most thermodynamically stable crystal form under normal temperature and pressure conditions. Studies have found that under certain conditions, such as heat or the action of surrounding media, ε-CL-20 will transform into other crystal forms, and this process is called the crystal form transfo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B33/00C30B29/54
CPCC30B29/54C30B33/00
Inventor 焦清介张洪垒郭学永潘启吴成成向俊舟王书记
Owner BEIJING INSTITUTE OF TECHNOLOGYGY