Novel wood-like furniture and preparation method thereof

A technology for imitating wood and furniture, applied in the field of imitation wood furniture, can solve the problems of uncontrollable color and high price, and achieve the effects of controllable appearance effect, long shelf life and good weather resistance.

Inactive Publication Date: 2020-07-31
扬州博业达新型建材科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of China's furniture industry, the current people's pursuit of furniture's aesthetics and performance and environmental protection has been improved, and the core of the above two points is grasped to carry out competition and research in the furniture industry. The furniture materials currently on the market are composite panels. Compared with solid wood boards, the disadvantages of composite boards are organic glue and molding, and the release of formaldehyde is harmful to the human body, while solid wood boards are renewable resources, the price is relatively high, and the color is uncontrollable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel wood-like furniture and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A new type of imitation wood furniture, which is composed of fabric and middle material. The fabric is composed of 45% sulfoaluminate cement, 39.4% natural colored sand (20-40 mesh in particle size), 2.1% iron oxide yellow, and 0.15% polypropylene fiber. %, 1.35% superplasticizer, 0.10% retarder, 0.010% titanium dioxide, 0.39% negative oxygen ions and 11.5% water. Inorganic gelling material 75.3%, superplasticizer 2.26%, negative oxygen ion 0.35%, water 19.50% and polyphenylene particle 2.59% are composed, and above percentage all refers to the percentage that the consumption of this raw material accounts for middle material gross mass; The fabric and the middle material are put into the mold, and then a curing is performed. After the first curing, the mold is separated from the mold for the second curing, and finally product 1 is obtained; the first curing is at 30°C for 24 hours, and the humidity is 90%; the second curing is at Curing at 25°C for 48 hours, with a humi...

Embodiment 2

[0023] A new type of imitation wood furniture, which is composed of fabric and middle material. The fabric is composed of 45% sulfoaluminate cement, 39.4% natural colored sand (80-120 mesh in particle size), 2.1% iron oxide yellow, and 0.15% polypropylene fiber. %, 1.35% superplasticizer, 0.10% retarder, 0.010% titanium dioxide, 0.39% negative oxygen ions and 11.5% water. 67.71% of sulfoaluminate cement, 2.09% of superplasticizer, 9.89% of coarse sawdust (10-60 mesh in particle size), 0.16% of setting retarder, 0.67% of negative oxygen ion and 19.48% of water. It refers to the percentage of the amount of the raw material in the total mass of the middle material; put the above-mentioned fabric and the middle material into the mold, and then perform a curing, after the first curing, it is separated from the mold for the second curing, and finally the product 2 is obtained; the first curing is Curing at 30°C for 24 hours with a humidity of 85%; secondary curing at 25°C for 48 hou...

Embodiment 3

[0025]A new type of imitation wood furniture, which is composed of fabric and middle material. The fabric is composed of 72.22% of sulphoaluminate cement, 2.5% of fine sawdust (60-100 mesh in particle size), 0.25% of polypropylene fiber, and 3.2% of iron oxide red. %, superplasticizer 2.16%, retarder 0.17%, negative oxygen ions 0.73% and water 18.77%. 75.3%, superplasticizer 2.26%, negative oxygen ion 0.35%, water 19.50% and polystyrene particles 2.59%, the above percentages all refer to the percentage of the amount of this raw material in the total mass of the middle material; the above-mentioned fabric and middle material Put it into the mold, and then carry out a curing, after the first curing, leave the mold for the second curing, and finally get product 3; the first curing is at 26°C for 24 hours, and the humidity is 90%; the second curing is at 30°C Curing for 48 hours, humidity is 88%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses novel wood-like furniture and a preparation method thereof, and belongs to the technical field of wood-like furniture. The wood-like furniture is composed of a surface materialand a middle material, and a product is obtained through steam curing. The surface material is a mixture composed of an inorganic cementing material, natural colored sand, toner, short fibers, a super plasticizer, a retarder, titanium dioxide, negative oxygen ions, fine sawdust or a mixture of a plurality of raw materials in water, and the middle material is a mixture composed of an inorganic cementing material, a super plasticizer, negative oxygen ions, polyphenyl granules, coarse sawdust, a retarder or a mixture of a plurality of raw materials in water. The furniture with the wood grain effect similar to silicification, pear flower wood, red sandalwood and the like is manufactured by adopting a process of matching multiple color systems such as cementing materials, natural colored sand,toner and the like, has an ornamental value and practicability, and is natural and real in natural color, vivid in image, not easy to fade, discolor, good in weather resistance, and not easy to falloff and crack and long in quality guarantee period, and a large amount of wood resources is saved.

Description

technical field [0001] The invention belongs to the technical field of wood-like furniture, and in particular relates to a novel wood-like furniture and a preparation method thereof. Background technique [0002] With the development of China's furniture industry, the current people's pursuit of furniture's aesthetics and performance and environmental protection has been improved, and the core of the above two points is grasped to carry out competition and research in the furniture industry. The furniture materials currently on the market are composite panels. Compared with solid wood boards, the disadvantages of composite boards are organic glue and molding, and the release of formaldehyde is harmful to the human body, while solid wood boards are renewable resources, the price is relatively high, and the color is uncontrollable. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a new type of imitation wood furnitu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06
CPCC04B28/065C04B2111/00612C04B14/02C04B14/308C04B16/0633C04B2103/32C04B2103/22C04B14/305C04B2103/0068C04B16/08
Inventor 王文博
Owner 扬州博业达新型建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com