Antibacterial and antistatic garment fabric

An anti-static and clothing technology, applied in the field of clothing fabrics, can solve problems such as human skin allergies, static electricity generated from clothing fabrics, and dirty clothing fabrics

Inactive Publication Date: 2020-08-07
NINGBO ZHONGDI SHOES
View PDF9 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Since the human body produces sweat when wearing clothing, the sweat adheres to the clothing fabric and easily breeds bacteria. At the same time, there are a large number of bacteria in the air, and these bacteria will accumulate and adhere to the clothing fabric. If the antibacterial ability of the clothing fabric If the anti-static ability of the clothing fabric is poor, it will cause the human body to have skin allergies and other health problems; and the friction between the clothing fabric and the clothing fabric will easi...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial and antistatic garment fabric
  • Antibacterial and antistatic garment fabric
  • Antibacterial and antistatic garment fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] An antibacterial and antistatic clothing fabric, comprising 15g of chitin fiber, 18g of chitosan fiber, 35g of tea fiber, 20g of Folium viscose fiber, 30g of modified polyamide 6 fiber, and polysulfone with a concentration of 50g / L Acid betaine aqueous solution 120g;

[0061] The preparation method of modified polyamide 6 fiber comprises the steps:

[0062] a. Raw material preparation:

[0063] a1. Weigh adipic acid and zinc oxide, the weight ratio of adipic acid and zinc oxide is 1.5:1, wherein 15g of adipic acid and 10g of zinc oxide are added to 200ml of acetone, and reacted at 30°C for 0.8h;

[0064] a2. Mix the zinc diadipate obtained in step a1 with polyethylene glycol, add a catalytic amount of calcium acetate, and react at 130° C. for 2.7 hours to obtain a polyether derivative of zinc, zinc diadipate, polyethylene glycol The weight ratio of diol is 0.5:1, wherein polyethylene glycol 10g, zinc diadipate 5g;

[0065] a3. First add caprolactam and catalytic amou...

Embodiment 2

[0069] An antibacterial and antistatic clothing fabric, comprising 18g of chitin fiber, 19g of chitosan fiber, 38g of tea fiber, 21.5g of Folium viscose fiber, 32g of modified polyamide 6 fiber, and a polyamide 6 fiber with a concentration of 50g / L 130g of sulfobetaine aqueous solution;

[0070] The preparation method of modified polyamide 6 fiber comprises the steps:

[0071] a. Raw material preparation:

[0072] a1. Weigh adipic acid and zinc oxide, the weight ratio of adipic acid and zinc oxide is 1.7:1, wherein 17g of adipic acid and 10g of zinc oxide are added to 94.4ml of acetone, and reacted at 31°C for 0.9h;

[0073] a2. Mix the zinc diadipate obtained in step a1 with polyethylene glycol, add a catalytic amount of calcium acetate, and react at 140° C. for 2.9 hours to obtain a polyether derivative of zinc, zinc diadipate, polyethylene glycol The weight ratio of diol is 0.7:1, wherein polyethylene glycol 10g, zinc diadipate 7g;

[0074] a3. First add caprolactam and ...

Embodiment 3

[0078] An antibacterial and antistatic clothing fabric, comprising 20g of chitin fiber, 20g of chitosan fiber, 40g of tea fiber, 22.5g of Folium viscose fiber, 35g of modified polyamide 6 fiber, and a polyamide 6 fiber with a concentration of 54g / L 140g of sulfobetaine aqueous solution;

[0079] The preparation method of modified polyamide 6 fiber comprises the steps:

[0080] a. Raw material preparation:

[0081] a1. Weigh adipic acid and zinc oxide, the weight ratio of adipic acid and zinc oxide is 2:1, wherein 20g of adipic acid and 10g of zinc oxide are added to 100ml of acetone, and react at 32°C for 1h;

[0082] a2. Mix the zinc diadipate obtained in step a1 with polyethylene glycol, add a catalytic amount of calcium acetate, and react at 150°C for 3 hours to obtain a polyether derivative of zinc, zinc diadipate, polyethylene glycol The weight ratio of alcohol is 1:1, wherein polyethylene glycol 10g, zinc diadipate 10g;

[0083] a3. First add caprolactam and catalytic a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Login to view more

Abstract

The invention relates to antibacterial and antistatic garment fabric and belongs to the technical field of garment fabric. The antibacterial and antistatic garment fabric comprises the following components including, by weight, 15-25 parts of chitin fiber, 18-22 parts of chitosan fiber, 35-45 parts of tea fiber, 20-25 parts of folium isatidis viscose, 30-40 parts of modified polyamide 6 fiber and120-160 parts of antibacterial agents. According to the antibacterial and antistatic garment fabric, the effect of improving the antibacterial and antistatic performance of the garment fabric is achieved.

Description

technical field [0001] The invention relates to the technical field of clothing fabrics, in particular to an antibacterial and antistatic clothing fabric. Background technique [0002] At present, clothing is composed of three elements: clothing style, clothing color and clothing fabric. Among them, clothing fabric is the most basic element. Clothing fabric can reflect the main characteristics of clothing, and clothing fabric needs to be comfortable to wear and soft to the touch. [0003] Since the human body produces sweat when wearing clothing, the sweat adheres to the clothing fabric and easily breeds bacteria. At the same time, there are a large number of bacteria in the air, and these bacteria will accumulate and adhere to the clothing fabric. If the antibacterial ability of the clothing fabric If the anti-static ability of the clothing fabric is poor, it will cause the human body to have skin allergies and other health problems; and the friction between the clothing fa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D01F8/12D01F9/00D01F1/10D01F1/09D06M11/74D06M15/00D01D5/06D01D1/10D06M101/06D03D15/20D03D15/217D03D15/225D03D15/283D03D15/47D03D15/50D03D15/533
CPCD03D15/00D01F8/12D01F9/00D01F1/103D01F1/09D06M11/74D06M16/00D06M15/00D01D5/06D01D1/103D01D1/106D06M2101/06
Inventor 方小丽
Owner NINGBO ZHONGDI SHOES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap