Preparation method of improved epoxy resin-based glass fiber composite material

A technology of epoxy resin and glass fiber, applied in the field of composite materials, can solve the problems of unsatisfactory hardness and strength, poor heat resistance effect, etc., to achieve increased stability and controllability, good heat resistance, and long service life Effect

Inactive Publication Date: 2020-08-18
九江科旭复合材料制造有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a kind of improved preparation method of epoxy resin-based glass fiber composite material, to solve the heat resistance effect of present epoxy resin-based glass fiber composite material proposed in the above-mentioned background technology is poor, hardness and strength can not The problem of meeting needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A method for preparing an improved epoxy resin-based glass fiber composite material, comprising raw materials of the following weight components: 100 parts of epoxy resin, 22 parts of silica nanoparticles, 6 parts of curing agent and 2 parts of adhesive, the specific preparation method comprises the following steps:

[0023] S1: Weigh the raw materials according to the parts by weight;

[0024] S2: Add the weighed epoxy resin and silica nanoparticles into the mixer and stir evenly, and place it under ultrasonic treatment for 15-30min, add curing agent during ultrasonic treatment, and stir evenly;

[0025] S3: Add adhesive to the mixture in S2, and stir evenly to obtain epoxy resin substrate glue;

[0026] S4: Add the epoxy resin substrate glue into the dipping machine, and put the glass fiber cloth into the dipping machine filled with the epoxy resin substrate glue for impregnation treatment, then remove the glass fiber cloth After rising, put it on the drain rack for...

Embodiment 2

[0032] A method for preparing an improved epoxy resin-based glass fiber composite material, comprising raw materials of the following weight components: 100 parts of epoxy resin, 22 parts of silica nanoparticles, 6 parts of curing agent and 2 parts of adhesive, the specific preparation method comprises the following steps:

[0033] S1: Weigh the raw materials according to the parts by weight;

[0034] S2: Add the weighed epoxy resin and silica nanoparticles into the mixer and stir evenly, and place it under ultrasonic treatment for 15-30min, add curing agent during ultrasonic treatment, and stir evenly;

[0035] S3: Add adhesive to the mixture in S2, and stir evenly to obtain epoxy resin substrate glue;

[0036] S4: Add the epoxy resin substrate glue into the dipping machine, and put the glass fiber cloth into the dipping machine filled with the epoxy resin substrate glue for impregnation treatment, then remove the glass fiber cloth After rising, put it on the drain rack for...

Embodiment 3

[0042] An improved preparation method of epoxy resin-based glass fiber composite material, including raw materials of the following weight components: 110 parts of epoxy resin, 20 parts of silica nanoparticles, 8 parts of curing agent and 2 parts of adhesive, specifically prepared The method includes the following steps:

[0043] S1: Weigh the raw materials according to the parts by weight;

[0044] S2: Add the weighed epoxy resin and silica nanoparticles into the mixer and stir evenly, and place it under ultrasonic treatment for 15-30min, add curing agent during ultrasonic treatment, and stir evenly;

[0045] S3: Add adhesive to the mixture in S2, and stir evenly to obtain epoxy resin substrate glue;

[0046] S4: Add the epoxy resin substrate glue into the dipping machine, and put the glass fiber cloth into the dipping machine filled with the epoxy resin substrate glue for impregnation treatment, then remove the glass fiber cloth After rising, put it on the drain rack for 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of composite materials and particularly relates to a preparation method of an improved epoxy resin-based glass fiber composite material. The composition comprises the following raw materials in parts by weight: 100-120 parts of epoxy resin, 20 to 25 parts of silicon dioxide nanometer particles; 5-10 parts of a curing agent and 1-3 parts of an adhesive.According to the preparation method, nano particles are uniformly dispersed in a monomer by adopting ultrasonic waves; polymerization reaction is then carried out, so that the heat resistance, the strength, the hardness, the wear resistance and the corrosion resistance of the resin-based glass fiber composite material can be greatly improved; finally, silicon dioxide nanoparticles are combined toprepare a complex with pores below 100 nm, and then the complex is compounded with glass fibers (the diameter is 11mu m and the length is 3mm); therefore, the prepared composite material has excellentheat resistance.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to an improved method for preparing epoxy resin-based glass fiber composite materials. Background technique [0002] The manufacturing process of traditional high-temperature glass fiber composite materials is to change the resin molding system of glass fiber material and use high-temperature resistant polyimide resin to make it. Because of its high price and complex production process, the domestic price of high-temperature-resistant composite glass fiber materials has been at a high level. However, using silica nano-reinforcement technology, a composite glass fiber material with a similar temperature resistance level can be produced by using a low-cost epoxy resin gluing system. Epoxy resin-based glass fiber composites have excellent mechanical properties, corrosion resistance and chemical stability; small volume shrinkage during processing; low cost and other outstan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08K13/04C08K7/14C08K3/36C08K5/544C08J5/24
CPCC08K13/04C08K7/14C08K3/36C08K5/544C08J5/24C08K2201/011C08J2363/00C08L2201/08C08L63/00
Inventor 汤传宏熊邦新
Owner 九江科旭复合材料制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap