Preparation method and application method of a blast furnace slag-supported catalyst

A supported catalyst and blast furnace slag technology, applied in chemical instruments and methods, physical/chemical process catalysts, heterogeneous catalyst chemical elements, etc., can solve problems such as energy consumption

Active Publication Date: 2021-08-20
INST OF MECHANICS - CHINESE ACAD OF SCI
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current conventional technology is to directly burn and release methane through the chimney, resulting in a large amount of energy consumption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application method of a blast furnace slag-supported catalyst
  • Preparation method and application method of a blast furnace slag-supported catalyst
  • Preparation method and application method of a blast furnace slag-supported catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] In order to make the purpose, technical solutions and advantages of the embodiments of the present invention more clear, the following will clearly and completely describe the technical methods in the embodiments of the present invention in conjunction with the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments It is only some embodiments of the present invention, but not all embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative labor achievements belong to the protection scope of the present invention.

[0022] It should be noted that if there is a directional indication (such as up, down, left, right, front, back, etc.) in the embodiment of the present invention, the directional indication is only used to explain the relationship between the components in a certain posture. Relative positional relationship, movem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The embodiment of the present invention relates to a preparation method of a blast furnace slag-supported catalyst, comprising: obtaining blast furnace slag powder; preparing a mixed solution by using active components and absolute ethanol; placing the blast furnace slag powder in the mixed solution, using The magnetic stirrer is continuously stirred at 80° C. for 4-10 hours until the blast furnace slag powder forms a colloid, and the colloid is dried and calcined to obtain a blast furnace slag-supported catalyst. Therefore, the preparation cost is low, the process is simple and easy to control, no treatment steps such as acid hydrolysis are needed, and secondary pollution is effectively avoided. The blast furnace slag is used as a catalyst carrier as a whole, and various components contained in it can be effectively utilized to realize resource utilization and high-value utilization, broaden the resource utilization of blast furnace slag, and achieve the purpose of treating waste with waste. The blast furnace slag-loaded catalyst prepared by the invention has high low-temperature activity and can maintain high CO catalytic removal efficiency in the temperature range of >150°C.

Description

technical field [0001] The embodiments of the present invention relate to the technical field of converter gas treatment, and in particular to a preparation method and application method of a blast furnace slag-supported catalyst. Background technique [0002] Blast furnace slag is the main solid waste produced in the blast furnace ironmaking process of the metallurgical industry, but in terms of its composition, it can be used as high-quality raw materials in the fields of building materials and chemicals. The annual output of blast furnace slag in my country is about 250 million tons. However, most of the existing technologies have the problems of low added value of products and high energy consumption in the recycling process, resulting in poor market competitiveness of resource-based products. , The level of energy utilization is still very low. Therefore, it is of great practical significance to develop a new technology for the comprehensive utilization of blast furnace...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/72B01J35/02F23G7/07
CPCB01J23/002B01J23/72B01J35/023B01J2523/00F23G7/07F23G2209/14B01J2523/17B01J2523/31B01J2523/41B01J2523/47
Inventor 宾峰康润宁魏小林王绍龙何浚珧
Owner INST OF MECHANICS - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap