A kind of high conductivity aluminum alloy and its heat treatment process

An aluminum alloy, high-conductivity technology, applied in the direction of conductive materials, conductive materials, metal/alloy conductors, etc., can solve problems such as easy cracking or breaking, increased contact resistance, creep, etc., to reduce mechanical properties and improve electrical conductivity , cost reduction effect

Active Publication Date: 2021-03-30
福建祥鑫股份有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the conductor materials of my country's wires and cables use copper conductors, but due to the shortage of copper resources in my country and the high price of copper, copper conductor materials account for more than 70% of the cost of copper wires and cables, resulting in too much cost for manufacturing copper wires and cables; if used Pure aluminum conductor material, after a long period of use in our country, it is found that the pure aluminum conductor material will undergo large creep after long-term operation or current overload, resulting in increased contact resistance, easy to cause accidents, and poor bending performance, easy to crack or break , also prone to accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high conductivity aluminum alloy and its heat treatment process
  • A kind of high conductivity aluminum alloy and its heat treatment process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A highly conductive aluminum alloy comprising the following components: 0.39% Si, 0.1% Fe, 0.124% Cu, 0.65% Mg, 0.04% Zn, 0.05% Cr, 0.12% other unavoidable The impurity element and the balance are Al.

[0018] The preparation method of high-conductivity aluminum alloy: (1) Add the raw materials into the melting furnace in order according to the block weight and size from large to small, then raise the temperature of the furnace gas by 20°C and keep it warm until it is completely melted, then raise the temperature of the furnace gas by 20°C After ℃, add pure zinc ingots one by one, keep warm until it is completely melted to obtain an alloy solution, reduce the temperature of the alloy melt to 730°C, add a covering refining flux, the recommended composition of the covering refining flux is (%, mass fraction): 30 %NaCl, 47% KCl, 23% cryolite, after forming a protective layer on the mirror surface of the melt, refining, refining once during the alloy melting process, the ti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-conductivity aluminum alloy. The high-conductivity aluminum alloy comprises the following components of, in percentage, 0.34%-0.45% of Si, smaller than or equal to 0.12%of Fe, 0.08%-0.18% of Cu, 0.54%-0.76% of Mg, smaller than or equal to 0.05% of Zn, smaller than or equal to 0.05% of Cr and the balance Al and other inevitable impurity elements, the total componentcontents of Mg and Si are smaller than or equal to 1.05%, the mass ratio of Mg to Si is 1.6 to 1.7, the total component contents of Cu and Zn are 0.12%-0.18%, and Cu / Zn is larger than or equal to 2.8and smaller than or equal to 3.4. According to the high-conductivity aluminum alloy and the heating processing technology thereof, on the basis of common elements, the proportion content of the elements is optimized, meanwhile, a heat treatment method is coordinated, it is guaranteed that the mechanical property is not greatly reduced while the conductivity is improved, the cost is reduced, and the application prospect is achieved.

Description

technical field [0001] The invention belongs to the field of aluminum alloy materials, and in particular relates to a high-conductivity aluminum alloy and a heat treatment process thereof. Background technique [0002] With the rapid development of my country's economy, the great development of the power system, and large-scale infrastructure construction, the demand for wires and cables in my country has grown rapidly. At present, most of the conductor materials of my country's wires and cables use copper conductors, but due to the shortage of copper resources in my country and the high price of copper, copper conductor materials account for more than 70% of the cost of copper wires and cables, resulting in too much cost for manufacturing copper wires and cables; if used Pure aluminum conductor material, after long-term use in our country, it is found that the pure aluminum conductor material will undergo large creep after long-term operation or current overload, resulting i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/08C22C1/02C22C1/06C22F1/047H01B1/02
CPCC22C1/026C22C1/06C22C21/08C22F1/002C22F1/047H01B1/023
Inventor 黄铁明黄铁兴冯永平张建雷刘金霞
Owner 福建祥鑫股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products