Preparation method of gamma-PGA nanofiber

A technology of nanofibers and hyperbranched polyamides, which is applied in the field of preparation of γ-PGA nanofibers, can solve problems such as low yield, high frictional resistance, and small stretching ratio, and achieve broad application space, extended life time, water The effect of stability improvement

Active Publication Date: 2020-08-28
ZETTA NANO TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the large frictional resistance of the liquid coagulation bath, the drawing rate is relatively low, the drawing ratio is also small, and the yield is low, the diameter of the fiber obtained by air-jet spinning often cannot meet the demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A preparation method of γ-PGA nanofibers, the specific process steps are as follows:

[0025] (1) Diethylenetriamine and methyl acrylate are used as raw materials to synthesize monomers through micheal addition reaction, and then the monomers undergo their own melt polycondensation reaction under high temperature conditions to obtain hyperbranched polyamide-amine.

[0026] (2) Dissolve the above hyperbranched polyamidoamine in methanol to obtain a methanol solution of hyperbranched polyamidoamine, add a certain amount of γ-PGA and 1-ethyl-(3-dimethylaminopropyl) Carbodiimide hydrochloride (EDC.HCl), additional solvent DMSO, mixed reaction for 72 hours, and then dialyzed to obtain spinning solution;

[0027] (3) Utilize the syringe pump to feed the spinning solution obtained in step (2) into the spinneret box body through the metering pump at a speed of 11mL / h, and the spinning solution forms a thin stream when it is extruded from the spinneret, and simultaneously Compr...

Embodiment 2

[0036] A preparation method of γ-PGA nanofibers, the specific process steps are as follows:

[0037] (1) Diethylenetriamine and methyl acrylate are used as raw materials to synthesize monomers through micheal addition reaction, and then the monomers undergo their own melt polycondensation reaction under high temperature conditions to obtain hyperbranched polyamide-amine.

[0038] (2) Dissolve the above hyperbranched polyamidoamine in methanol to obtain a methanol solution of hyperbranched polyamidoamine, add a certain amount of γ-PGA and 1-ethyl-(3-dimethylaminopropyl) Carbodiimide hydrochloride (EDC.HCl), additional solvent DMSO, mixed reaction for 72 hours, and then dialyzed to obtain spinning solution;

[0039] (3) Utilize the syringe pump to feed the spinning solution obtained in step (2) into the spinneret box body through the metering pump at a speed of 11mL / h, and the spinning solution forms a thin stream when it is extruded from the spinneret, and simultaneously Compr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of gamma-PGA nanofiber. The fiber is prepared by adopting a jet spinning method, full water stabilization modification is performed on the modified gamma-PGA nanofiber, spinning jet streams pass through an air section before entering a coagulating bath, full crosslinking of the fiber occurs, the diameter meets the requirement, and the prepared gamma-PGAnanofiber has the advantages of water stability and good applicability.

Description

technical field [0001] The invention belongs to the field of nanofibers, in particular to a method for preparing gamma-PGA nanofibers. Background technique [0002] γ-polyglutamic acid (γ-PGA) is a natural polymer material synthesized by microorganisms. In mammals, γ-PGA can be degraded into harmless glutamic acid by γ-polyglutamic acid transpeptidase. A large number of studies have shown that γ-PGA is a polymer material with good biodegradability, biocompatibility, and non-toxic to humans and the environment. In the field of medicine, γ-PGA can realize the sustained release of drugs, improve the water solubility of drugs, reduce adverse drug reactions, and improve the efficacy of drugs. [0003] γ-PGA fibers can be widely used in the field of biomedicine after being spun into fibers, but γ-PGA fibers alone are easy to degrade in water and have poor water stability, which limits some of their applications. In the prior art, γ-PGA is usually chemically modified to improve ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/12D01F8/16C08G73/02D01D5/04D01D1/02
CPCD01F8/12D01F8/16C08G73/028D01D5/04D01D1/02Y02P20/10
Inventor 徐正东
Owner ZETTA NANO TECH CO LTD