A kind of preparation method of mechanical expansion discoloration mechanism device

A mechanism and mechanical technology, which is applied in the field of preparation of mechanical expansion and color change mechanism devices, can solve the problems of no elastic film rapid response full-chromatographic color change device reports, etc., and achieve the effect of fast color change response speed, simple principle and simple preparation method

Active Publication Date: 2021-07-30
HUAZHONG UNIV OF SCI & TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the relevant elastic color-changing films can only realize two kinds of color changes, and there are no reports of fast-response and full-spectrum color-changing devices prepared by related elastic films.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of mechanical expansion discoloration mechanism device
  • A kind of preparation method of mechanical expansion discoloration mechanism device
  • A kind of preparation method of mechanical expansion discoloration mechanism device

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The preparation method of the double-layer elastic film of the present invention comprises the following steps:

[0034] (1) The polymer elastomer precursor is dissolved in an organic or inorganic solvent by a mechanical stirring / vibration method, wherein the mass percent concentration of the polymer in the mixed solution is 1% to 90%, forming an elastomer solution A, which is divided into two share;

[0035] (2) Disperse the inorganic pigment particles in a part of the solution A obtained in step (1) by mechanical stirring / vibration method, and form a homogeneous mixed solution B after mixing; wherein, the mass percent concentration of the inorganic dye particles is 1% to 70%. ;

[0036] (3) Pour a certain amount of solution A into the petri dish to cover the whole petri dish, put it in an oven and dry until half dry;

[0037] (4) Pour the mixed liquid B into the elastomer petri dish obtained in (3), and put it into an oven to dry until it is completely dry to obtain...

Embodiment 1

[0040] (1) Add 0.25g of titanium dioxide white powder and 5g of natural rubber stock solution in a beaker, form a uniform mixture A by mechanical stirring and ultrasonic vibration, wherein the stirring temperature is 30°C, the speed is 50 rpm, and the time is 1 Hour;

[0041] (2) Pour 5g of rubber stock solution into a petri dish with a diameter of 10cm to cover the entire petri dish, put it in an oven at 80°C and bake for 30 minutes until it is half dry;

[0042] (3) Pour 5 g of mixture A into the elastomer petri dish obtained in (2), put it in an oven at 80° C. and bake for 3 hours until it is completely dry to obtain a double-layer elastic film.

[0043] (4) Add 0.001 g of methylene blue dye to 10 g of aqueous solution in a beaker to obtain a blue filled aqueous solution.

[0044] (5) Seal one end of a steel pipe with a diameter of 1 cm and a length of 15 cm with the prepared double-layer elastic film, with the layer containing titanium dioxide facing outward, and after fi...

Embodiment 2

[0046] (1) Add 2.5g Ecoflex A and 2.5g Ecoflex B into a beaker, and form a uniform polymer A by mechanical stirring method, which is divided into two parts, wherein the stirring temperature is 30°C, the speed is 50 rpm, and the time is 1 Hour;

[0047] (2) Add 0.25g of ferric oxide powder and 2.5g of polymer A in a beaker to form a homogeneous mixture B by means of mechanical stirring and ultrasonic vibration, wherein the stirring temperature is 30°C and the speed is 50 rpm, The time is 1 hour;

[0048] (3) Pour 2.5g of polymer A into a petri dish with a diameter of 10cm to cover the entire petri dish, put it in an oven at 80°C and bake for 30 minutes until it is half dry;

[0049] (4) Pour 2.5 g of mixture B into the elastomer petri dish obtained in (3), put it in an oven at 80° C. and bake for 3 hours until it is completely dry to obtain a double-layer elastic film.

[0050] (5) Add 0.001 g of methylene blue dye to 10 g of aqueous solution in a beaker to obtain a blue filled...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a mechanical expansion and discoloration mechanism device, which consists of a hollow tube, a double-layer elastic film, a base color filler and a piston. The double-layer elastic film fixes and covers one end of the hollow tube. The base color filler is filled in the hollow tube, and the piston is arranged at the other end of the hollow tube. The device of the present invention is low in cost, simple in preparation, easy in operation, and controllable. The equipment used in the method is simple, and the light-controlled double-layer elastic The color composition, structure and performance of the film and the base color filler material can be controlled according to the needs. The device has the characteristics of stable structure, fast response, full color spectrum, large size and repeatable color change. The discoloration device is mainly used in the fields of discoloration display, advertisement, military camouflage and decoration.

Description

technical field [0001] The invention relates to the field of color-changing display and camouflage devices, in particular to a method for preparing a fast and simple mechanical expansion and color-changing mechanism device. Background technique [0002] Color-changing materials or technologies have broad application prospects in the fields of display, camouflage and sensing. However, the current research on color-changing materials and devices still has major deficiencies. For example, existing color-changing materials or devices have high material costs, complex devices (such as patent CN103105794B), long response times (such as patent CN109594112A) and can only be used in specific The problem of discoloration between several colors (such as patent CN103757938B), restricts their application. The light-regulating double-layer elastic film proposed by the present invention refers to adjusting the light transmission and reflectivity of the elastic film through mechanical expa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02B26/00C08J5/18C08L7/00C08L67/02C08K3/22
CPCC08J5/18C08J2307/00C08J2367/02C08K2003/2241C08K2003/2272G02B26/007
Inventor 苏彬彭灵慧
Owner HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products