Environment-friendly degradable plant fiber tableware and processing technology thereof

A plant fiber, green and environmental protection technology, which is applied in the field of green and environmentally friendly degradable plant fiber tableware and its processing technology, can solve the problems of no synthesis of new materials, environmental damage, and no real solution to the problem of material degradation, so as to increase income and save waste. , the effect of reducing deforestation

Inactive Publication Date: 2020-09-18
安徽壳氏环保科技股份有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As people get used to using plastic products, material waste will increase at a rate of about 15%-20% every year, which has caused cumulative damage to our environment. Therefore, countries around the world have invested in plastic products since the 1970s. A lot of manpower, m

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A green and environment-friendly degradable plant fiber tableware. The raw materials are composed of the following components in parts by weight: 160 parts of grain powder, 200 parts of fiber-containing powder, 10 parts of alginate powder, 5 parts of tapioca starch, and 0.7 part of edible glycerin.

[0023] Wherein, the grain powder can be but not limited to wheat bran flour, soybean flour and broken rice flour, and the grain powder is made by mixing any two of wheat hull flour, soybean flour and broken rice flour in a ratio of 1:1.

[0024] The fiber-containing powder can be but not limited to bamboo fiber powder, grain husk powder and fruit husk powder. The moisture content of the grain powder and the fiber-containing powder is 4%, the particle size of the grain powder is 5 mesh, and the particle size of the fiber-containing powder is 10 mesh.

[0025] A kind of processing technology of green environmental protection degradable plant fiber tableware, this processing te...

Embodiment 2

[0032] A green and environment-friendly degradable plant fiber tableware. The raw materials are composed of the following components in parts by weight: 200 parts of grain powder, 300 parts of fiber-containing powder, 20 parts of alginate powder, 10 parts of tapioca starch, and 1.3 parts of edible glycerin.

[0033] Wherein, the grain powder can be but not limited to wheat bran flour, soybean flour and broken rice flour, and the grain powder is made by mixing any two of wheat hull flour, soybean flour and broken rice flour in a ratio of 1:1.

[0034] The fiber-containing powder can be but not limited to bamboo fiber powder, grain husk powder and fruit husk powder. The moisture content of the grain powder and the fiber-containing powder is 6%, the particle size of the grain powder is 7 mesh, and the particle size of the fiber-containing powder is 13 mesh.

[0035] A kind of processing technology of green environmental protection degradable plant fiber tableware, this processing ...

Embodiment 3

[0042] A green and environment-friendly degradable plant fiber tableware. The raw materials are composed of the following components in parts by weight: 240 parts of grain powder, 400 parts of fiber-containing powder, 30 parts of alginate powder, 15 parts of tapioca starch, and 1.9 parts of edible glycerin.

[0043] Wherein, the grain powder can be but not limited to wheat bran flour, soybean flour and broken rice flour, and the grain powder is made by mixing any two of wheat hull flour, soybean flour and broken rice flour in a ratio of 1:1.

[0044] The fiber-containing powder can be but not limited to bamboo fiber powder, grain husk powder and fruit husk powder. The moisture content of the grain powder and the fiber-containing powder is 8%, the particle size of the grain powder is 9 mesh, and the particle size of the fiber-containing powder is 16 mesh.

[0045] A kind of processing technology of green environmental protection degradable plant fiber tableware, this processing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses environment-friendly degradable plant fiber tableware and a processing technology thereof. The environment-friendly degradable plant fiber tableware is prepared from the following raw materials in parts by weight: 160 to 240 parts of cereal powder, 200 to 400 parts of fiber-containing powder, 10 to 30 parts of seaweed gel powder, 5 to 15 parts of cassava starch and 0.7 to 1.9 parts of edible glycerol. Agricultural wastes such as straws, rice husks, wheat husks, bamboo fiber powder, and the like are utilized; leftovers of toothpicks and other products and the fruit shellpowder after fruit juice are utilized; wastes in agriculture and forestry are reused, the deforestation is reduced, the income of farmers is increased, the used rice flour is prepared from starch ofthe broken rice, rich bran, or white bran during the rice processing process and the waste of food is prevented.

Description

technical field [0001] The invention relates to the technical field of degradable tableware, in particular to a green and environment-friendly degradable plant fiber tableware and its processing technology. Background technique [0002] Plastic material products are widely used in various fields of human production and life. When these items are discarded, they are concentrated in urban garbage disposal points, or scattered in villages, fields, and fields. Because the polymer structure of the material is very tight, it generally takes 300-600 years to degrade in the natural environment, so these wastes pollute the environment in large quantities. As people get used to using plastic products, material waste will increase at a rate of about 15%-20% every year, which has caused cumulative damage to our environment. Therefore, countries around the world have invested in plastic products since the 1970s. A lot of manpower, material resources, and financial resources have been ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L99/00C08L97/02C08L5/00C08L3/02C08K5/053
CPCC08L97/02C08L99/00C08L2201/06C08L2205/025C08L2205/035C08L2205/16C08L5/00C08L3/02C08K5/053
Inventor 谢大兵
Owner 安徽壳氏环保科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap