Environment-friendly putty powder and preparation method thereof

A putty powder, environmentally friendly technology, applied in the field of building decoration materials, can solve the problems of cracking, large drying shrinkage, etc., and achieve the effects of good water resistance, low preparation cost, and sufficient strength and adhesion.

Inactive Publication Date: 2020-10-30
刘超
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its comprehensive performance needs to be further improved, and its drying shrinkage rate is large, which is prone to cracking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly putty powder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] An environment-friendly putty powder is characterized in that it comprises the following components by weight: 20 parts of palygorskite, 10 parts of montmorillonite, 15 parts of white cement, λ-carrageenan modified polyquaternium-101 parts , 2 parts of rosin-modified cationic guar gum, 1 part of konjac gum, 0.5 part of epoxy-terminated hyperbranched polyphosphate, and 0.5 part of amino-terminated hyperbranched polybenzimidazole.

[0026] The preparation method of the rosin-modified cationic guar gum comprises the following steps: adding the rosin and the cationic guar gum to deionized water, stirring and reacting at 70°C for 8 hours, then rotating to remove the solvent, and washing with water for 3 times, Then place it in a vacuum drying oven at 80°C and dry to constant weight; the molar ratio of rosin, cationic guar gum, and deionized water is 1:1:10.

[0027] The preparation method of the λ-carrageenan modified polyquaternium-10 comprises the following steps: adding λ...

Embodiment 2

[0030] An environment-friendly putty powder, characterized in that it comprises the following components by weight: 23 parts of palygorskite, 12 parts of montmorillonite, 16 parts of white cement, λ-carrageenan modified polyquaternium-101.5 parts , 2.5 parts of rosin-modified cationic guar gum, 1.5 parts of konjac gum, 0.7 part of epoxy-terminated hyperbranched polyphosphate, and 0.7 part of amino-terminated hyperbranched polybenzimidazole.

[0031] The preparation method of the rosin-modified cationic guar gum comprises the following steps: adding rosin and cationic guar gum to deionized water, stirring and reacting at 73° C. for 8.5 hours, then rotating to remove the solvent, and washing with water 4 times, Then place it in a vacuum drying oven at 83°C and dry to constant weight; the molar ratio of rosin, cationic guar gum, and deionized water is 1:1:13.

[0032] The preparation method of the λ-carrageenan modified polyquaternium-10 comprises the following steps: adding λ-ca...

Embodiment 3

[0035] An environment-friendly putty powder is characterized in that it comprises the following components in parts by weight: 25 parts of palygorskite, 15 parts of montmorillonite, 17 parts of white cement, λ-carrageenan modified polyquaternium-102 parts , 3 parts of rosin-modified cationic guar gum, 2 parts of konjac gum, 1 part of epoxy-terminated hyperbranched polyphosphate, and 1 part of amino-terminated hyperbranched polybenzimidazole.

[0036] The preparation method of the rosin-modified cationic guar gum comprises the following steps: adding rosin and cationic guar gum to deionized water, stirring and reacting at 75° C. for 9 hours, then rotating to remove the solvent, and washing with water for 5 times, Then place it in a vacuum drying oven at 85°C and dry to constant weight; the molar ratio of rosin, cationic guar gum, and deionized water is 1:1:15.

[0037] The preparation method of the λ-carrageenan modified polyquaternium-10 comprises the following steps: adding λ-c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses environment-friendly putty powder which is characterized in comprising the following components in parts by weight: 20-30 parts of palygorskite, 10-20 parts of montmorillonite,15-20 parts of white cement, 1-3 parts of lambda-carrageenan modified polyquaternium-10, 2-4 parts of rosin modified cationic guar gum, 1-3 parts of konjac gum, 0.5-1.5 parts of epoxy-terminated hyperbranched polyphosphate and 0.5-1.5 parts of amino-terminated hyperbranched polybenzimidazole. The invention further provides a preparation method of the environment-friendly putty powder. The environment-friendly putty powder disclosed by the invention is good in comprehensive performance, sufficient in strength and adhesive force, high in hardness, good in water resistance, free of phenomena ofhollowing, peeling, cracking and falling off after being wetted by water, and safe and environment-friendly to use.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to an environmentally friendly putty powder and a preparation method thereof. Background technique [0002] With the development of society and the improvement of living standards, people's awareness of environmental protection and health is constantly increasing, and their requirements for the comfort and safety of the living environment are getting higher and higher. Putty powder, as a common decorative material on the surface of a flat wall, plays a vital role in the comfort and safety of the living environment. The ideal putty powder requires not only excellent adhesion and water resistance, but also It is safe, green and environmentally friendly, and has a long service life. [0003] Putty powder is based on inorganic gel material, finely processed with bonding materials and other additives, and is an indispensable product before painting. Putty powder i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 刘超
Owner 刘超
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap