High-temperature-resistant resin anchoring agent and production method thereof

A technology of high temperature resistant resin and production method, applied in the directions of non-polymer adhesive additives, adhesives, adhesive types, etc. ability, improve processing efficiency, and improve the effect of tolerance

Inactive Publication Date: 2020-11-03
淮北金邦新型材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a high-temperature-resistant resin anchoring agent and its production method, which solves the problem that the underground operation environment of coal mines and other mines is very complicated, and the gas content is high, which can easily cause fires. When performing anchoring work, it is often unable to withstand high temperatures, and the anchoring agent in a high-temperature environment tends to soften, which eventually leads to the problem that the overall frame structure becomes very fragile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Step 1: Basic preparation of materials and equipment: Grind the calcined clay and marble powder in the process of materials, and screen out tiny particles with a particle diameter of 1 mm through a vibrating screen. After functional testing of the production equipment, turn on the power and start up to enter the standby state;

[0035] Step 2: Preliminary treatment of materials: Preheat the container with an alcohol furnace, and then add 35 parts of calcined clay, 20 parts of marble powder, 10 parts of aluminum hydroxide, 15 parts of phenoxyethanol, 50 parts of glycerin and antioxidant Pour 10 parts of the agent into the container, heat the poured material, and at the same time slowly stir it, keep it for 5 minutes, and when the temperature rises to 60 degrees Celsius, heat it;

[0036]Step 3: Advanced treatment of materials: add 50 parts of pure water to the insulation material, heat for 5 minutes, stir the material, and add 35 parts of unsaturated polyester resin, 15 p...

Embodiment 2

[0041] Step 1: Basic preparation of materials and equipment: Grind the calcined clay and marble powder in the process of materials, and screen out tiny particles with a particle diameter of 1 mm through a vibrating screen. After functional testing of the production equipment, turn on the power and start up to enter the standby state;

[0042] Step 2: Preliminary treatment of materials: Preheat the container with an alcohol furnace, and then add 40 parts of calcined clay, 25 parts of marble powder, 15 parts of aluminum hydroxide, 20 parts of phenoxyethanol, 55 parts of glycerin and antioxidant Pour 12.5 parts of the agent into the container, heat the poured material, and at the same time slowly stir it, keep it for 10 minutes, and when the temperature rises to 70 degrees Celsius, heat it;

[0043] Step 3: Advanced treatment of materials: Add 75 parts of pure water to the insulation material, heat for 5 minutes, stir the material, and add 40 parts of unsaturated polyester resin, ...

Embodiment 3

[0048] Step 1: Basic preparation of materials and equipment: Grind the calcined clay and marble powder in the process of materials, and screen out tiny particles with a particle diameter of 1 mm through a vibrating screen. After functional testing of the production equipment, turn on the power and start up to enter the standby state;

[0049] Step 2: Preliminary treatment of materials: Preheat the container with an alcohol furnace, and then add 45 parts of calcined clay, 30 parts of marble powder, 20 parts of aluminum hydroxide, 25 parts of phenoxyethanol, 60 parts of glycerin and antioxidant Pour 15 parts of the agent into the container, heat the poured material, and at the same time slowly stir it, keep it for 15 minutes, and when the temperature rises to 80 degrees Celsius, heat it;

[0050] Step 3: Advanced treatment of materials: add 100 parts of pure water to the insulation material, heat for 5 minutes, stir the material, and add 45 parts of unsaturated polyester resin, 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature-resistant resin anchoring agent. The main materials comprise the following components in parts by weight: 50-100 parts of purified water, 35-45 parts of unsaturated polyester resin, 15-25 parts of terephthalic acid, 30-50 parts of diethylene glycol, 15-25 parts of tea polyphenol, 20-40 parts of silicon dioxide, 15-35 parts of aluminum oxide, 15-25 parts of magnesium oxide, 60-80 parts of dibenzoyl peroxide, 10-40 parts of dipotassium glycyrrhizinate, 10-60 parts of hydroxyethyl cellulose, 10-30 parts of defoamer, 5-30 parts of wetting agent, and 10-20parts of an accelerant; and auxiliary materials: 35-45 parts of calcined clay and 20-30 parts of marble powder. The invention relates to the technical field of anchoring agents. According to the high-temperature-resistant resin anchoring agent and the production method thereof, the tolerance degree of the whole product to high temperature is improved, the functions of the whole material are clear, and later treatment and packaging of the material are facilitated.

Description

technical field [0001] The invention relates to the technical field of anchoring agents, in particular to a high-temperature-resistant resin anchoring agent and a production method thereof. Background technique [0002] Anchor bolts and anchor cables are currently the most important roadway support technologies in coal mines in my country, and anchor materials play a decisive role in the anchor bolt and anchor cable support structures. , Reliable performance has become the main anchoring material for coal mine roadway support in my country. Resin anchoring agent is a viscous anchoring adhesive material prepared in a certain proportion from unsaturated polyester resin, curing agent, accelerator and other auxiliary materials. , high bonding strength, reliable anchoring force and good durability. Widely used in roof support of coal mines, shaft installation, rock formation support, equipment foundation fixing, dam crack repair, and seismic reinforcement of buildings, etc. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J167/06C09J101/28C09J11/04C09J11/06
CPCC08K2003/222C08K2003/2227C08K2003/265C08K2201/014C08L2201/08C09J11/04C09J11/06C09J101/284C09J167/06C08L1/284C08K3/346C08K3/26C08K5/092C08K5/06C08K3/36C08K3/22C08K13/06C08K9/00C08L67/06
Inventor 王玉荣
Owner 淮北金邦新型材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com