Metal and polyolefin composite material, preparation method thereof and container

A composite material and polyolefin technology, applied in the field of metal and polyolefin composite materials, can solve the problems of easy peeling, achieve the effect of not easy to crack, high peel strength, and improve the performance of environmental stress cracking resistance

Active Publication Date: 2020-12-08
神华(北京)新材料科技有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem that the existing metal and polyolefin composite material is easy to peel off, to provide a metal and polyolefin composite material, a preparation method of the material, and a container made of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0057] Prepare a polyolefin composition, including the following ingredients:

[0058] (1) polyolefin, 100 parts by weight in total, specifically comprising the following components:

[0059] Polyethylene, total 88 weight parts, by the 1st-1 polyethylene of 44 weight parts (Eastman chemical company, trade mark 811, density is 0.915g / cm 3 , melt index is 20g / 10min), 22 parts by weight of the first-2 polyethylene (Korea Total R902S, density is 0.935g / cm 3 , melt index is 6g / 10min) and 22 parts by weight of the first-third polyethylene (Dushanzi Petrochemical DAMA2911, density is 0.960g / cm 3 , melt index is 20g / 10min);

[0060] Copolymer of ethylene and octene (Dow DuPont, ENGAGE8200), 12 parts by weight;

[0061] (2) compatibilizer: the polyethylene (manufacturer is Jia Yirong company, trade mark is FB16E5, grafting rate 0.8%) of maleic anhydride monomer grafting, 3 parts by weight;

[0062] (3) peroxide crosslinking agent: di-tert-butyl peroxide (purchased from J&K Scientif...

preparation example 2

[0068] Prepare a polyolefin composition, including the following ingredients:

[0069] (1) polyolefin, 100 parts by weight in total, specifically comprising the following components:

[0070] Polyethylene, 90 weight parts altogether, by the 1st-2 polyethylene (Dow DuPont company of Dow, trademark 4012, density is 0.918g / cm2 by 50 weight parts 3 , melt index is 12g / 10min), 20 parts by weight of the 2-2 polyethylene (Yangzi Petrochemical BASF Co., Ltd., brand 2420K, density is 0.924g / cm 3 , melt index is 4.0g / 10min) and 20 parts by weight of the 2nd-3 polyethylene (Tianjin United Chemical Co., Ltd., trade mark DMDA8920, density is 0.954g / cm 3 , melt index is 20.0g / 10min);

[0071] Ethylene-propylene rubber (manufacturer Dow DuPont, trade mark 3660), 10 parts by weight;

[0072] (2) Compatibilizer: ethylene octene copolymer grafted by maleic anhydride (manufacturer is Dow Chemical, the trade mark is GR216, grafting rate 1.2%), 5 parts by weight;

[0073] (3) peroxide crosslin...

preparation example 3

[0080] Prepare a polyolefin composition, including the following ingredients:

[0081] (1) polyolefin, 100 parts by weight in total, specifically comprising the following components:

[0082] Polyethylene, totally 80 weight parts, by the 3-1 polyethylene of 48 weight parts (Dow DuPont Company, trade mark 4016, density is 0.918g / cm 3 , melt index is 16g / 10min), 16 parts by weight of the 3-2 polyethylene (Tianjin United Chemical Co., Ltd., trade mark DNDC7149, density is 0.934g / cm 3 , melt index is 5g / 10min) and 16 parts by weight of the 3rd-3rd polyethylene (Dushanzi Petrochemical DMDA6143, density is 0.952g / cm 3 , melt index is 16g / 10min);

[0083] Copolymer of ethylene and octene (Dow DuPont, ENGAGE8200), 20 parts by weight;

[0084] Ethylene-propylene rubber (Dow DuPont, trademark 3660), 20 parts by weight;

[0085] (2) compatibilizer: polyethylene grafted by glycidyl methacrylate (manufacturer is Jiayi Rong Company, the trade mark is SOG-02, grafting rate 0.8%), 5 parts...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of polymer composite materials, in particular to a metal and polyolefin composite material, a preparation method thereof and a container. The composite material of the metal and the polyolefin comprises a metal material and a polyolefin material, the polyolefin material is obtained by performing a cross-linking reaction on a polyolefin composition, the polyolefincomposition comprises polyolefin, a compatilizer, a peroxide cross-linking agent and a silane coupling agent, and relative to 100 parts by weight of polyolefin, the content of the compatilizer is 0.1-20 parts by weight, the content of the peroxide cross-linking agent is 0.01-6 parts by weight, and the content of the silane coupling agent is 0.1-5 parts by weight. The metal and polyolefin composite material provided by the invention is not easy to crack, good in high temperature resistance and longer in service life.

Description

technical field [0001] The invention relates to the field of polymer composite materials, in particular to a composite material of metal and polyolefin, a preparation method of the material, and a container made of the material. Background technique [0002] Crosslinkable polyolefin has excellent high temperature resistance, chemical corrosion resistance, good impact strength, etc., and has important application value in chemical storage and transportation, oil and gas transportation, and chemical anticorrosion. However, as a low-polarity mixture, crosslinkable polyolefin has poor adhesion to polar substrates (such as metals), so the metal part and polyolefin part in the prepared polyolefin and metal composite member are easy to peel off, greatly Reduced service life of polyolefin and metal composite components. [0003] At present, there are few dedicated studies on the metal bonding properties of polyolefins. Therefore, finding a composite material of metal and polyolefi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/16C08L23/08C08L51/06C08K13/02C08K3/08C08K5/14C08K5/5425C08K5/544
CPCC08L23/06C08L2205/035C08L2205/025C08L2312/08C08L2201/08C08L23/0815C08L51/06C08K13/02C08K3/08C08K5/14C08K5/544C08L23/16C08K5/5425
Inventor 朱鹤翔孙小杰梁文斌王珂
Owner 神华(北京)新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com