Manufacturing process of high-weather-resistance reflective film

A production process and technology of reflective film, applied in the direction of film/sheet adhesive, optics, optical components, etc., can solve the problems of short service life, poor weather resistance of reflective film, etc., and achieve good mechanical strength and good viscosity stability , Improve the effect of weather resistance

Inactive Publication Date: 2020-12-15
JINJIANG LIANXING REFLECTIVE MATERIAL
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the reflective film plays an obvious warning role with its bright colors in the daytime, at night or in the case of insufficient light, its bright reflective effect can effectively enhance people's recognition ability, see the target clearly, arouse vigilance, and thus avoid accidents , reduce casualties, reduce economic losses, and become an indispensable safety guard for road traffic, which has obvious social benefits. However, in the prior art, the weather resistance of the reflective film is poor and the service life is short, which needs further improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] Specifically, the preparation method of the transparent protective slurry includes:

[0041] A. Add acetyl tributyl citrate, tributyl citrate, bis(2-ethylhexyl) phthalate, plasticizer TXIB, and heat stabilizer to a high-speed mixer and mix evenly, and set aside;

[0042] B. Pour the polyvinyl chloride paste resin into a high-speed mixer, heat it to 100°C while stirring, then add epoxy soybean oil, diatomaceous earth, titanium dioxide, light calcium carbonate, heavy calcium carbonate, and foaming agent , coupling agent, impact modifier, zinc oxide, after mixing for 5 minutes, add the mixture prepared in step A, and continue mixing for 3 minutes;

[0043] C. Add viscosity reducer D40 to the mixture obtained in step B to adjust the viscosity of the mixture to 1500mPa·s to obtain a transparent protective slurry.

[0044] In the second step, the temperature of the elastic mirror steel roller is 140-160°C, and the temperature of the mold belt is 160-170°C.

Embodiment 1

[0046] The production process of the high weather resistance reflective film, the reflective film includes a transparent protective layer, a microprism layer, a packaging layer, a pressure-sensitive adhesive layer and a release layer arranged in sequence from top to bottom.

[0047] The transparent protective layer comprises the following raw materials in parts by weight: 90 parts of polyvinyl chloride paste resin, 18 parts of acetyl tributyl citrate, 12 parts of tributyl citrate, 6 parts of bis(2-ethylhexyl) phthalate 12 parts of plasticizer TXIB, 3 parts of heat stabilizer, 4 parts of epoxy soybean oil, 10 parts of diatomaceous earth, 5 parts of titanium dioxide, 3 parts of light calcium carbonate, 10 parts of heavy calcium carbonate, and 3 parts of foaming agent , 2 parts of coupling agent, 4 parts of impact modifier, 1 part of zinc oxide.

[0048]The encapsulation layer is composed of the following components: 45 parts of polyester resin, 3 parts of toluene diisocyanate, 3...

Embodiment 2

[0063] The production process of the high weather resistance reflective film, the reflective film includes a transparent protective layer, a microprism layer, a packaging layer, a pressure-sensitive adhesive layer and a release layer arranged in sequence from top to bottom.

[0064] The transparent protective layer comprises the following raw materials in parts by weight: 110 parts of polyvinyl chloride paste resin, 12 parts of acetyl tributyl citrate, 18 parts of tributyl citrate, 10 parts of bis(2-ethylhexyl) phthalate , 6 parts of plasticizer TXIB, 5 parts of heat stabilizer, 6 parts of epoxy soybean oil, 5 parts of diatomaceous earth, 10 parts of titanium dioxide, 5 parts of light calcium carbonate, 6 parts of heavy calcium carbonate, and 5 parts of foaming agent , 1 part of coupling agent, 7 parts of impact modifier, 0.3 part of zinc oxide.

[0065] The encapsulation layer is composed of the following components: 35 parts of polyester resin, 6 parts of toluene diisocyanat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing process of a high-weather-resistance reflective film. The reflective film comprises a transparent protective layer, a microprism layer, a packaging layer, a pressure-sensitive adhesive layer and a release layer which are sequentially arranged from top to bottom, the transparent protective layer is prepared from the following raw materials in parts by weight:polyvinyl chloride paste resin, acetyl tributyl citrate, tributyl citrate, di(2ethylhexyl)phthalate, a plasticizer TXIB, a heat stabilizer, epoxidized soybean oil, diatomite, titanium dioxide, lightcalcium carbonate, ground calcium carbonate, a foaming agent, a coupling agent, an impact modifier and zinc oxide. By limiting plasticizers such as acetyl tributyl citrate, tributyl citrate, di(2ethylhexyl) phthalate and a plasticizer TXIB to be matched with polyvinyl chloride paste resin, the transparent protective layer formed on a microprism is high in plasticizing efficiency, low in plasticizer mobility, good in cold resistance and extraction resistance and high in wear resistance, so that the weather resistance of the reflective film is improved, and the service life of the reflective film is prolonged.

Description

technical field [0001] The invention belongs to the field of reflective film preparation, and in particular relates to a process for producing a highly weather-resistant reflective film. Background technique [0002] Reflective film is mainly used for guide signs, signs, outline signs, raised road signs of various roads and railways, traffic cones, anti-collision tubes, safety islands, mine airport safety signs, place names, license plates, property community safety signs, construction signs, Billboards, stage sets, logos, etc. Because the reflective film plays an obvious warning role with its bright colors in the daytime, at night or in the case of insufficient light, its bright reflective effect can effectively enhance people's recognition ability, see the target clearly, arouse vigilance, and thus avoid accidents , reduce casualties, reduce economic losses, become an indispensable safety guard for road traffic, and have obvious social benefits, but in the prior art, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/25C08J7/12C08J7/046C09D127/06C09D7/61C09D7/63C09D7/65C09D167/00C09D5/38G02B5/126
CPCC09J7/255C08J7/123C08J7/046C09D127/06C09D7/61C09D7/63C09D7/65C09D7/70C09D167/00C09D5/38G02B5/126C08J2367/02C08J2427/06C08J2467/00C08L2201/10C08L2205/03C08K2201/014C08K2003/265C08K2003/2296C08K2003/0806C08L91/00C08K13/04C08K7/26C08K5/11C08K3/26C08K3/22C08K13/02C08K5/29C08K5/14C08K3/08
Inventor 杨汉阳张培实杨帆陈明聪
Owner JINJIANG LIANXING REFLECTIVE MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com