Cold-resistant plastic bucket and preparation method thereof

A plastic barrel and cold-resistant technology, applied in the field of plastic packaging containers, can solve the problems of poor impact strength and elongation at break, narrow molecular weight distribution, etc., and achieve the effects of enhanced tensile strength, good compatibility and strong corrosion resistance

Active Publication Date: 2018-11-16
青岛邦德化工有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

HDPE is non-toxic, tasteless and odorless white particles with a melting point of about 130°C and a relative density of 0.941-0.960g / cm 3 , it has good heat resistance and cold resistance, good chemical stability, high rigidity and toughness, and good mechanical strength; but due to its low molecular weight and narrow molecular weight distribution, its impact strength and elongation at break slightly worse

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cold-resistant plastic bucket and preparation method thereof
  • Cold-resistant plastic bucket and preparation method thereof
  • Cold-resistant plastic bucket and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Embodiment 1: A kind of cold-resistant plastic barrel is prepared by the following method:

[0046] (1) Premix: 70kg density is 0.936g / cm 3 , high-density polyethylene with a melt index of 1.4g / 10min, and a density of 0.916g / cm in 20kg 3 , linear low density polyethylene with a melt index of 1.0g / 10min, 15kg of maleic anhydride grafted high density polyethylene with a graft rate of 0.8%-1.2%, 6kg of high degree of polymerization polyvinyl chloride and 7kg of ethylene-vinyl acetate The copolymer is placed in a high-speed mixer, stirred at a temperature of 110°C for 30 minutes, and mixed evenly;

[0047] (2) Mixed material: add 0.8kg ultraviolet absorber UV-531, 0.36kg antioxidant 264, 0.84kg antioxidant DLTP, 0.5kg dioctyl phthalate, 0.5kg epoxy four to the premixed material Dioctyl hydrophthalate, 1.5kg epoxy butyl oleate and 6kg silicon micropowder with a particle size of 0.2-0.3μm were stirred at a temperature of 150°C for 35 minutes and mixed uniformly;

[0048] (...

Embodiment 2

[0051] Embodiment 2: A kind of cold-resistant plastic barrel is prepared by the following method:

[0052] (1) Premix: 60kg density is 0.936g / cm 3 , high-density polyethylene with a melt index of 1.4g / 10min, and a density of 0.916g / cm in 15kg 3 , linear low-density polyethylene with a melt index of 1.0g / 10min, 10kg of maleic anhydride grafted high-density polyethylene with a graft rate of 0.8%-1.2%, 5kg of high-polymerization polyvinyl chloride and 6kg of ethylene-vinyl acetate The copolymer is placed in a high-speed mixer, stirred at a temperature of 100°C for 40 minutes, and mixed evenly;

[0053] (2) Mixed material: add 0.5kg ultraviolet absorber UV-531, 0.3kg antioxidant 264, 0.7kg antioxidant DLTP, 0.4kg dioctyl phthalate, 0.4kg epoxy four to the premixed material Dioctyl hydrophthalate, 1.2kg epoxy butyl oleate, and 5kg silicon micropowder with a particle size of 0.2-0.3 μm were stirred at a temperature of 140°C for 40 minutes, and mixed uniformly;

[0054] (3) Extrus...

Embodiment 3

[0057] Embodiment 3: A kind of cold-resistant plastic barrel is prepared by the following method:

[0058] (1) Premix: 80kg density is 0.936g / cm 3 , high-density polyethylene with a melt index of 1.4g / 10min, and a density of 0.916g / cm in 25kg 3 , linear low-density polyethylene with a melt index of 1.0g / 10min, 20kg of maleic anhydride grafted high-density polyethylene with a graft rate of 0.8%-1.2%, 7kg of high-polymerization polyvinyl chloride and 8kg of ethylene-vinyl acetate The copolymer is placed in a high-speed mixer, stirred at a temperature of 120°C for 20 minutes, and mixed evenly;

[0059] (2) Mixed material: add 1.0kg ultraviolet absorber UV-531, 0.45kg antioxidant 264, 1.05kg antioxidant DLTP, 0.6kg dioctyl phthalate, 0.6kg epoxy four to the premixed material Dioctyl hydrophthalate, 1.8kg epoxy butyl oleate and 7kg silicon micropowder with a particle size of 0.2-0.3μm were stirred at a temperature of 160°C for 30 minutes and mixed uniformly;

[0060] (3) Extrusi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a cold-resistant plastic bucket and a preparation method thereof, and belongs to the technical field of a plastic packaging container. The cold-resistant plastic bucket is characterized in that the cold-resistant plastic bucket is prepared from the components in parts by weight: 60 to 80 parts of high-density polyethylene, 15 to 25 parts of linear low-density polyethylene,10 to 20 parts of maleic anhydride grafted high-density polyethylene, 5 to 7 parts of high-polymerization-degree polyvinyl chloride, 6 to 8 parts of ethylene-vinyl acetate copolymer, 0.5 to 1.0 part of ultraviolet absorption agent, 1 to 1.5 parts of antioxidant, 2 to 3 parts of plasticizer and 5 to 7 parts of silica power; the high-density polyethylene has a density of 0.936 g/cm<3> and a melt index of 1.4 g/10 min; the linear low-density polyethylene has a density of 0.920 g/cm<3> and a melt index of 1.0 g/10 min. The invention reaches the technical effect of enabling the polyethylene plasticbucket to also have excellent printing performance when having cold resistance.

Description

technical field [0001] The invention relates to the technical field of plastic packaging containers, more specifically, it relates to a cold-resistant plastic bucket and a preparation method thereof. Background technique [0002] Hollow blow molding containers are also called plastic containers, which are processed by hollow molding methods. There are open plastic barrels, cans and closed plastic barrels, cans and open plastic barrels. The materials used to prepare plastic barrels are mostly polyethylene (PE), Polypropylene (PP) and other thermoplastics are usually made by blow molding and injection molding, and are mostly used to hold liquid and solid items in industries such as chemicals, pesticides, medicine, food, hardware and electronics, and electromechanical industries. [0003] For plastic products, the toughness of plastics decreases and brittleness increases in deep severe cold, and the application is limited; plastics work in the glass state, and the lower limit t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L51/06C08L27/06C08K13/02C08K3/36C08K5/132C08K5/372C08K5/13C08K5/12
CPCC08K2201/003C08L23/06C08L2201/02C08L2201/08C08L2205/035C08L2207/062C08L23/0815C08L51/06C08L27/06C08L23/0853C08K13/02C08K3/36C08K5/132C08K5/372C08K5/13C08K5/12
Inventor 国基
Owner 青岛邦德化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap