A hot-rolled low-yield ratio high-strength acid corrosion-resistant steel plate and its production method

A technology with acid corrosion resistance and low yield strength ratio, applied in the direction of improving process efficiency, can solve the problems of high manufacturing cost and high yield strength of acid-resistant steel, and achieve excellent welding performance, low yield strength ratio, and excellent atmospheric corrosion resistance. Effect

Active Publication Date: 2022-04-01
MAANSHAN IRON & STEEL CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The acid-resistant steel involved in the third patent (CN109628843A) has a relatively high yield strength, and the addition of precious alloy Mo results in higher manufacturing costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A hot-rolled low-yield ratio high-strength acid corrosion-resistant steel plate and its production method
  • A hot-rolled low-yield ratio high-strength acid corrosion-resistant steel plate and its production method
  • A hot-rolled low-yield ratio high-strength acid corrosion-resistant steel plate and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0042] The present invention will be described in detail below in conjunction with examples.

[0043] The invention provides a hot-rolled low-yield ratio high-strength acid corrosion-resistant steel plate and a production method thereof. The main chemical composition and weight percentage content (wt%) of the steel strip are C: 0.06-0.08%; Si: 0.20%~0.40%; Mn: 0.80~1.20%; P: ≤0.012%; S: ≤0.005%; Cr: 0.70~1.20%; Ni: 0.10~0.30%; 0.045%; Nb: 0.015~0.030%; Ti: 0.010~0.025%; Sb: 0.06~0.12%; the balance is Fe and unavoidable inclusions, and Pcm=C+Si / 30+(Mn+Cu+Cr) / 20+Mo / 15+Ni / 60+V / 10+5B≤0.20%.

[0044] The invention adopts the traditional hot continuous rolling process to produce, and the process flow includes: deep desulfurization of molten iron pretreatment→converter smelting→external refining→continuous casting→stacking and slow cooling→slab heating→controlled rolling→controlled cooling→coiling.

[0045] 1) Carry out molten steel smelting according to the above chemical composi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a hot-rolled low-yield-ratio high-strength acid corrosion-resistant steel plate and a production method thereof. The main chemical composition and weight percentage content thereof are: C 0.06-0.08%; Si 0.20%-0.40%; Mn 0.80-0.00% 1.20%; P≤0.012%; S≤0.005%; Cr 0.70~1.20%; Ni 0.10~0.30%; Cu 0.20~0.40%; Alt 0.020~0.045%; 0.06~0.12%; the balance is Fe and unavoidable inclusions; the present invention adopts microalloying control technology combined with controlled rolling and controlled cooling principles, based on microstructure type control, deep desulfurization in molten iron pretreatment→converter smelting→furnace External refining→continuous casting→stacking and slow cooling→slab heating→controlled rolling→controlled cooling→coiling Hot continuous rolling strip production line develops high-strength acid-resistant steel products with low yield ratio, excellent formability and acid corrosion resistance , can be used in the manufacture of steel structures serving in acidic corrosive medium environments in transportation, tobacco, electric power, chemical energy, metallurgy and other industries.

Description

technical field [0001] The invention belongs to the technical field of iron and steel materials and their production, and in particular relates to a hot-rolled low yield ratio high-strength acid corrosion-resistant steel plate and a production method thereof. Background technique [0002] In metallurgy, petrochemical, electric power and other industries with heavy oil or coal as the main fuel for flue gas treatment systems, the sulfur in the fuel produces a large amount of SO during the combustion process. 3 , SO 2 Such as acidic medium gas, acidic medium gas and water vapor combine to form sulfuric acid vapor. When encountering low temperature components, condensation on the surface will easily cause severe sulfuric acid dew point corrosion, greatly shortening the service life of components. Sulfuric acid dew point corrosion-resistant steel has good sulfuric acid corrosion resistance, and is widely used in air preheaters, heat exchangers, economizers, desulfurization and d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/04C22C38/02C22C38/04C22C38/06C22C38/42C22C38/48C22C38/50C22C38/60C21C1/02C21D8/02C21C7/076C21C7/00
CPCC22C33/04C21C1/02C21C7/076C21C7/0056C22C38/02C22C38/04C22C38/06C22C38/42C22C38/48C22C38/50C22C38/60C21D8/0205C21D8/0263C21D8/0226C21D2211/005C21D2211/002C21D2211/008Y02P10/20
Inventor 胡学文何博张建朱涛郭锐王海波汪飞石践李雄杰
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap