Aluminum alloy dyeing additive and dyeing method
An aluminum alloy and additive technology, applied in the field of aluminum alloy, can solve problems such as flow color and discoloration, and achieve the effect of simple operation, thorough removal and easy control
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0033]Example 1
[0034]In the present embodiment, an aluminum alloy dye additive comprises 32 parts by weight of nickel sulfate, 10 parts of sulfate, 20 sulfuric acid, 18 colored stabilizers, and 16 amifier.
[0035]Further, further, the colored stabilizer is a weight ratio of 1: 1 by weight ratio of phosphotungstic acid and tungst acid.
[0036]Further, each of the functional auxiliaries comprises a weight of a weight of a polyhydroxy organic acid, a monohydrol monohydrof ether, 7 parts of fatty alcohol polyoxyethylene ether, 4 parts of mannitol.
[0037]A dyeing method of an aluminum alloy, including the following steps:
[0038](1) Take the aluminum alloy workpiece to absorb the aluminum alloy workpiece, and wash the aluminum alloy workpiece after degreasing;
[0039](2) The aluminum alloy workpiece is chemically polished, and the water washing is carried out after polishing, then the insoluble metal oxide is removed;
[0040](3) The aluminum alloy workpiece is anodized in an anode oxide solution, a...
Example Embodiment
[0056]Example 2
[0057]In this embodiment, an aluminum alloy dye additive comprises 30 parts by weight of the weight of 30 parts of sulfate, 8 serial sulfate, 18 sulfuric acid, 16 colored stabilizers, and 13 degreatment aids.
[0058]Further, the coloring stabilizer is phosphotungstic acid and sodium tungstate according to 1: 1.
[0059]Further, each of the functional auxiliaries comprises 15 parts by weight of a polyhydroxy organic acid, 4 parts of diphenol monomethyl ether, 5 parts of fatty alcohol polyoxyethylene ether, 3 parts of mannitol.
[0060]A dyeing method of an aluminum alloy, including the following steps:
[0061](1) Take the aluminum alloy workpiece to absorb the aluminum alloy workpiece, and wash the aluminum alloy workpiece after degreasing;
[0062](2) The aluminum alloy workpiece is chemically polished, and the water washing is carried out after polishing, then the insoluble metal oxide is removed;
[0063](3) The aluminum alloy workpiece is anodized in an anode oxide solution, and a...
Example Embodiment
[0079]Example 3
[0080]In the present embodiment, an aluminum alloy staining additive comprises 35 parts of the weight of sulfate, 812 parts of sulfate, 22 sulfuric acid, 20 colored stabilizers, and 18 degreasing aid.
[0081]Further, the coloring stabilizer is a hydrideate and tungstic acid according to weight ratio 1: 0.6.
[0082]Further, each of the functional auxiliaries comprises 20 parts by weight of the polyhydroxy organic acid, 7 parts of diol monohydrof ether, 8 parts of fatty alcohol polyoxyethylene ether, 5 parts of mannitol.
[0083]A dyeing method of an aluminum alloy, including the following steps:
[0084](1) Take the aluminum alloy workpiece to absorb the aluminum alloy workpiece, and wash the aluminum alloy workpiece after degreasing;
[0085](2) The aluminum alloy workpiece is chemically polished, and the water washing is carried out after polishing, then the insoluble metal oxide is removed;
[0086](3) The aluminum alloy workpiece is anodized in an anode oxide solution, and an anod...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap