A kind of preparation method of dimethylvinylsiloxy-terminated low-hydroxyl content mdt silicone oil

A technology of dimethyl vinyl siloxane sealing and divinyl is applied in the field of low hydroxyl content MDT silicone oil, which can solve the problems of bubbles in the release agent, affecting the curing rate and quality of the release agent, and poor storage stability of silicone oil. , to achieve the effect of simple preparation process, uniform molecular weight distribution of silicone oil, and low silanol content

Active Publication Date: 2022-04-01
惠州市永卓科技有限公司 +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] In order to solve the poor storage stability of the silicone oil caused by the high content of silanol in the MDT silicone oil molecule of the branched chain structure and the release of gas when it reacts with the platinum catalyst when used as a component of the release agent, resulting in the presence of bubbles in the release agent, which affects the curing rate and quality of the release agent The problem, the present invention proposes a kind of preparation method of dimethyl vinyl siloxy-terminated MDT silicone oil with low hydroxyl content, the prepared dimethyl vinyl siloxy-terminated MDT silicone oil has low residual silanol content, and the molecular weight of the silicone oil is The distribution is uniform, the preparation process is simple, and it is convenient for large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of dimethylvinylsiloxy-terminated low-hydroxyl content mdt silicone oil
  • A kind of preparation method of dimethylvinylsiloxy-terminated low-hydroxyl content mdt silicone oil
  • A kind of preparation method of dimethylvinylsiloxy-terminated low-hydroxyl content mdt silicone oil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) Add 727.20g (3.90mol) of 1,3-divinyl-1,1,3,3-tetramethyldisilazium to a 3000mL three-necked flask equipped with a stirring device, a thermometer and a reflux condenser at room temperature Oxygen, the temperature was raised to 35°C under stirring, and then the mixed solution consisting of 702.00g (39.0mol) of deionized water and 62.88g (0.637mol) of concentrated HCl with a concentration of 37% was mixed for 2h through a constant pressure dropping funnel. Add it dropwise to the reaction vessel at a constant speed. After the dropwise addition, raise the temperature of the reactant to 70° C. and react at this temperature for 3 hours. After the reaction was finished, it was cooled to room temperature, and the reaction product was two layers up and down;

[0039] (2) Add 531.60g (3.90mol) of methyltrimethoxysilane and 314.40g of toluene into another 5000mL three-necked flask equipped with a stirring device, a thermometer and a reflux condenser, and keep the system tempera...

Embodiment 2

[0043] (1) Add 727.20 g (3.90 mol) of 1,3-divinyl-1,1,3,3-tetramethyldisilazium to a 3000 mL three-necked flask equipped with a stirring device, a thermometer and a reflux condenser at room temperature Oxygen, under stirring, be warmed up to 45 ℃, then through the constant pressure dropping funnel, the mixed solution that the premixed 702.00g (39.0mol) deionized water and 62.88g (0.637mol) concentration is the concentrated HCl composition of 37% is passed through 2.5 h was added dropwise to the reaction vessel at a constant speed. After the dropwise addition, the temperature of the reactant was raised to 70° C. and reacted at this temperature for 3 h. After the reaction was finished, it was cooled to room temperature, and the reaction product was two layers up and down;

[0044] (2) Add 531.60g (3.90mol) of methyltrimethoxysilane and 314.40g of toluene to another 5000mL three-necked flask equipped with a stirring device, a thermometer and a reflux condenser, and keep the syste...

Embodiment 3

[0048] (1) Add 181.80 g (0.975 mol) of 1,3-divinyl-1,1,3,3-tetramethyldisilazium to a 1000 mL three-necked flask equipped with a stirring device, a thermometer and a reflux condenser at room temperature Oxygen, the temperature was raised to 30°C under stirring, and then the mixed solution composed of 175.50g (9.75mol) deionized water and 15.72g (0.159mol) concentration of 37% concentrated HCl was passed through a constant pressure dropping funnel through 0.75 h was added dropwise to the reaction vessel at a constant speed. After the dropwise addition, the temperature of the reactant was raised to 65° C. and reacted at this temperature for 4 hours. After the reaction was finished, it was cooled to room temperature, and the reaction product was two layers up and down;

[0049] (2) Add 132.90g (0.976mol) of methyltrimethoxysilane and 78.60g of toluene to another 1000mL three-necked flask equipped with a stirring device, a thermometer and a reflux condenser, and keep the system te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
polydispersity indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of organic synthesis, in order to solve the poor storage stability of the silicone oil caused by the high content of silanol in the MDT silicone oil molecule of the branched chain structure and the release of gas from the reaction with the platinum catalyst when used as a release agent component, resulting in the presence of bubbles in the release agent. To solve the problem of curing rate and quality of the release agent, the present invention proposes a method for preparing dimethylvinylsiloxy-terminated MDT silicone oil with low hydroxyl content by reactive distillation. The prepared dimethylvinylsiloxy-terminated The high-end MDT silicone oil has low residual silanol content, uniform molecular weight distribution of silicone oil, simple preparation process, and is convenient for large-scale production.

Description

technical field [0001] The invention relates to the field of organic synthesis, in particular to a method for preparing dimethylvinylsiloxy-terminated MDT silicone oil with low hydroxyl content by adopting a reactive distillation coupling method. Background technique [0002] MDT silicone oil is a kind of branched chain silicone oil, which is a kind of liquid polyorganosiloxane containing polyorganosiloxane branches formed by introducing trifunctional chains into the linear silicone oil molecular chain as branch points. The existence of branched chain structure in the molecule leads to the degree of entanglement of branched silicone oil molecular chains greater than that of linear polydimethylsiloxane. Under the action of shear force, the viscosity of branched chain silicone oil decreases, that is, there is a shear thinning effect, which belongs to non-Newtonian fluid. At present, branched chain silicone oil has been widely used in cosmetics, paper anti-adhesive release age...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G77/20C08G77/06
CPCC08G77/20C08G77/06C08G77/70Y02P20/10
Inventor 伍川王细平郭世平方高瞿志荣刘川贵董红刘清月张伟伟
Owner 惠州市永卓科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com