Polyisocyanate composition with storage stability

A technology of polyisocyanate and isocyanurate, which is applied in the field of polyisocyanate composition, can solve problems such as differences in application performance, and achieve the effect of convenient source and excellent moisture stability

Active Publication Date: 2021-05-28
WANHUA CHEMICAL (NINGBO) CO LTD +1
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN104024219A describes the disadvantages of these compounds, because the pronounced crystallization tendency of the toluenesulfonamide formed by reaction with water leads to the blocking of the paint
The difference from the addition of active substances that react with water as described above is that it changes the composition of polyisocyanate, which will cause differences in its application performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyisocyanate composition with storage stability
  • Polyisocyanate composition with storage stability
  • Polyisocyanate composition with storage stability

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0058] Preparation of polyisocyanate composition:

[0059] Under nitrogen protection conditions, 800g of hexamethylene diisocyanate was heated and stirred in a 75°C water bath for 1.5h, and then 0.6g of a 20wt% isooctyl alcohol solution of N,N,N-trimethylbenzyl ammonium hydroxide was added ( 150ppm), by regulating and controlling the water bath temperature control reaction temperature is 70 ℃; Distilled twice under conditions of 150°C and 0.4 Torr to obtain a polyisocyanate composition.

[0060] The chromaticity of the obtained polyisocyanate composition was 18 Hazen, the viscosity was 2880 mPa·s (25° C.), the NCO content was 21.8 wt %, and the monomer content was 0.12 wt %.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The present invention provides a polyisocyanate composition with storage stability under humid conditions. The polyisocyanate composition comprises a compound A which is obtained through a trimerization reaction of an aliphatic (cyclic) diisocyanate monomer, has an isocyanurate structure and is represented by the following formula (I), and the addition amount of the compound A is more than 20 ppm and less than 500 ppm relative to the mass of the polyisocyanate composition. In the compound A, the X is an N or P atom, the Z is an O or S atom, one or two of R1, R2 and R3 are halogen atoms, and the others are the same or different aryl, alkyl, aryloxy and alkoxy with the carbon number of 1-10.

Description

technical field [0001] The present invention relates to a storage-stable polyisocyanate composition. Background technique [0002] Urethane-based coating compositions using polyisocyanate as a curing agent are widely used as coatings for automobiles, building interiors and exteriors, and home appliances because the resulting coating film has excellent chemical resistance, flexibility, and weather resistance. coating. Among them, polyisocyanates having an isocyanurate structure derived from aliphatic (cyclo)diisocyanates are characterized by non-yellowing and are widely used in fields requiring these properties. When polyisocyanate is used in combination with the main ingredient, if the amount used is small, the same tank needs to be opened and closed multiple times for use, so there is a problem that isocyanate groups react with moisture in the air. [0003] p-toluenesulfonyl isocyanate (H 3 C(C 6 h 4 ) SO 2 -NCO) and triethylorthoformate are examples of water scavenge...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/79C08K5/521C08K5/5313
CPCC08G18/792C08K5/521C08K5/5313
Inventor 王少华孙立冬胡浩尚永华王暖程史培猛孙积钊韩海涛
Owner WANHUA CHEMICAL (NINGBO) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com