A Method for Improving the Insulation Properties of Polypropylene Films Based on Crystal Morphology Control

A polypropylene film and polypropylene technology, applied in the field of polypropylene film, can solve the problems that threaten the safe and stable operation of the DC transmission system, break the microstructure of the molecular chain, and generate electrical weaknesses, so as to avoid insulation failures, improve the microstructure, The effect of improving reliability

Active Publication Date: 2022-05-17
TIANJIN UNIV +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the actual operation process, under the combined action of the electric-thermal field, the microstructure of the polypropylene film will be damaged such as molecular chain breakage, resulting in electrical weakness, which may eventually cause insulation failure, thus threatening the safe and stable operation of the entire DC transmission system.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Method for Improving the Insulation Properties of Polypropylene Films Based on Crystal Morphology Control
  • A Method for Improving the Insulation Properties of Polypropylene Films Based on Crystal Morphology Control
  • A Method for Improving the Insulation Properties of Polypropylene Films Based on Crystal Morphology Control

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0029] 1 Use a twin-roller to fully mix the polypropylene masterbatch with 2,2'-methylene-bis(4,6-di-tert-butylphenyl)sodium phosphate (trade name: Irgastab NA-11) nucleating agent, The content is 0.01% (mass fraction), the mixing temperature is 190° C., and the mixing time is 10 minutes.

[0030] 2 Use a flat vulcanizer to melt the mixture, the melting temperature is 190°C, and the melting time is 5 minutes.

[0031] 3 After that, heat press the mixture. Decrease the temperature of the flat vulcanizer from 190°C to 120°C, keep the pressure at 30MPa during this process, and take 25 minutes for the cooling process.

[0032] 4 After the hot pressing is completed, take out the polypropylene / nucleating agent composite film pattern, and cool it down to 25°C naturally in the air.

example 2

[0034] 1 Use a twin-roller to fully mix the polypropylene masterbatch with 2,2'-methylene-bis(4,6-di-tert-butylphenyl)hydroxyaluminum phosphate (trade name: ADK NA-21) nucleating agent , the content is 0.03% (mass fraction), the mixing temperature is 185° C., and the mixing time is 12 minutes.

[0035] 2 Use a flat vulcanizer to melt the mixture, the melting temperature is 185°C, and the melting time is 5 minutes.

[0036] 3 After that, heat press the mixture. Decrease the temperature of the flat vulcanizer from 185°C to 100°C, keep the pressure at 35MPa during this process, and take 20 minutes for the cooling process.

[0037] 4 After the hot pressing is completed, take out the polypropylene / nucleating agent composite film pattern, and cool it down to 25°C naturally in the air.

example 3

[0039] 1 Use a twin-roller to mix the polypropylene masterbatch with bis[2,2′-methylene-bis-(4,6-di-tert-butylphenoxy)phosphate] hydroxyaluminum (trade name: HBP) ​​nucleating agent Mix well, the content is 0.05% (mass fraction), the mixing temperature is 195°C, and the mixing time is 15 minutes.

[0040] 2 Use a flat vulcanizer to melt the mixture, the melting temperature is 195°C, and the melting time is 5 minutes.

[0041] 3 After that, heat press the mixture. Decrease the temperature of the flat vulcanizer from 195°C to 140°C, keep the pressure at 40MPa during this process, and take 40 minutes for the cooling process.

[0042] 4 After the hot pressing is completed, take out the polypropylene / nucleating agent composite film pattern, and cool it down to 25°C naturally in the air.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

A method for improving insulation properties of polypropylene film based on crystal morphology regulation, comprising: fully mixing polypropylene masterbatch and nucleating agent using a twin-roller machine to obtain a mixture with a nucleating agent content of 0-0.05% by mass fraction; Use a flat vulcanizer to melt the mixture; heat-press the melted mixture, specifically, slowly reduce the temperature of the flat vulcanizer from 185°C to 195°C to 100°C to 140°C; after the hot press shape is completed, The polypropylene / nucleating agent composite film was taken out, and naturally cooled to 25° C. in air to obtain a modified polypropylene film. The invention can realize the control of the crystallization process of the polypropylene film, increase the crystallinity and density of the micron-sized polypropylene film, and improve the microscopic crystal region of the polypropylene film by improving its microstructure and optimizing its micromorphology, so as to limit the carrying current Sub-migration, improve the insulation performance of the film, avoid the occurrence of insulation failure, and improve the reliability of the DC transmission system.

Description

technical field [0001] The present invention relates to a polypropylene film. In particular, it relates to a method for improving the insulation properties of polypropylene films based on crystal morphology regulation. Background technique [0002] High-voltage DC metallized film capacitors play the role of filtering, voltage support, voltage equalization and damping in converter stations, and are the core equipment for smart grids and new energy power generation. Polypropylene is the main insulating medium of capacitors. As the voltage level increases, the requirements for the withstand voltage level of polypropylene insulation for capacitors also gradually increase. In the actual operation process, under the combined action of the electric-thermal field, the microstructure of the polypropylene film will be damaged such as molecular chain breakage, resulting in electrical weakness, which may eventually cause insulation failure, thus threatening the safe and stable operatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C43/02B29C43/34B29C43/52B29L7/00
CPCB29C43/02B29C43/34B29C43/52B29L2007/00Y02E60/60
Inventor 肖萌冉昭玉杜伯学许然然刘浩梁邢继文范凯伦
Owner TIANJIN UNIV