High-transparency cover glaze

A high-transparency, top-glaze technology, applied in the field of architectural ceramics, can solve the problems of gray visual perception, unsatisfactory wear resistance, and low color development of glazed surfaces, and achieve excellent mechanical properties and excellent light-transmitting properties.

Pending Publication Date: 2021-06-01
亚细亚新材料科技股份公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the formula composition system of the surface glaze is different, but its gloss is generally 8-15 degrees, and most of them have crystallization phenomenon on the glaze

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023]Example 1

[0024]This embodiment provides a high-permeable glaze, and a raw material of glaze according to a weight portion comprises 10 parts of potassium, 20 sodium waones, 8 parts of water, 2 hydroxide, zinc oxide 2 2 copies of burn, 8 silicahydrate, 8 dolomite, 2 quartz, 5 calcium carbonate, 0.2 pieces of phosphate, 0.2 parts of white gratum, 5 calcined soil, 0.5 alumina .

Example Embodiment

[0025]Example 2

[0026]This embodiment provides a high-permeable glaze, and the raw material of the glaze described in weight parts includes: 20 copies of glaze described in weight parts include: 20 copies of potassium, 30 sodium waones, water washing 12 copies of hydroxide, 8 copies of zinc oxide, 6 fever talc, 12 silicahydrate, 12 copies of dolomite, 8 pieces of quartz, 10 carbonate, 0.5 pieces of phosphate, 1 granient, calcination 10 parts of the earth, 6 square almenes, 2 alumina.

Example Embodiment

[0027]Example 3

[0028]This embodiment provides a high-perverted glaze, and the raw material of the glaze according to the weight of the weight comprises: the raw material of the glaze described in weight parts includes 15 copies of potassium, 22 sodium stones, water washing soil. 9 copies of indium hydroxide, 3 copies of zinc oxide, 3 bark talones, 9 serviles, 9 pieces of dolomite, 3 quartz, 6 pieces of carbonate, 0.4 pieces of phosphate, 0.4 white gratum, calcination 6 parts of the earth, 3 square almenes, 0.8 alumina.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Drying timeaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-transparency cover glaze. The cover glaze is prepared from the following raw materials: potassium feldspar, albite, indium hydroxide and barium phosphate. The cover glaze has excellent light transmission performance and also has excellent mechanical properties.

Description

technical field [0001] The invention belongs to the field of architectural ceramics, and relates to a surface glaze, in particular to a high-transparency surface glaze. Background technique [0002] At present, the ceramic market shows the characteristics of high-grade, artistic, personalized, and functional products. Decorative materials with healthy and high taste have become the mainstream of consumption. [0003] Glaze is a kind of glass or glass and crystal connection and adhesion attached to the surface of the ceramic body. Most glazes are glass bodies. The role of glaze in the production of ceramics is very important. First, it can be used to decorate ceramic products, so that the flaws of the ceramic body can be covered, and the surface can be smooth. It can also produce a variety of color patterns and special effects, which can improve its artistic appreciation value. Improve the various properties of ceramics, such as dense glass body surface to improve the chemic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/86C04B41/5022C04B41/4539C04B41/0072
Inventor 林要军
Owner 亚细亚新材料科技股份公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap