Low-size-shrinkage WPC floor and preparation method thereof

A size and floor technology, applied in the field of low-dimensional shrinkage WPC floor and its preparation, can solve the problems of high density, inferior physical properties to SPC floor, thick texture, etc. The effect of size performance

Pending Publication Date: 2021-06-15
DECORIA MATERIALS JIANGSU CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The industry is also constantly looking for new floor materials to replace, but the traditional SPC hard floor has the disadvantages of thick texture and high density; although the WPC floor has a low density, its physical properties are not as good as SPC floor, especially the floor dimensional stability and heat dissipation. Warpage and other properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for preparing a low-size shrinkage WPC floor, specifically comprising the following steps:

[0024] (1) Preparation of WPC base material: Weigh the corresponding weight parts of each raw material, perform high mixing at 100°C for 15 minutes, cold mixing at 50°C for 10 minutes, extruder temperature at 150°C, mold temperature at 170°C ;

[0025] The WPC base material includes the following preparation materials by weight: 100 parts of PVC resin, 5 parts of glass fiber with a specification of 6 mm, 2 parts of montmorillonite, 18 parts of dioctyl terephthalate, 8 parts of acrylic acid derivatives, alkyl 2 parts of sodium sulfonate, 1 part of foaming agent, 5 parts of stabilizer, 100 parts of stone powder, and 1 part of coloring agent; The weight ratio is 100:1; the specific treatment method is: mix KH-550 and alcohol in a ratio of 1:3 and spray it on the montmorillonite;

[0026] (2) Preparation of PVC film: Weigh each raw material of corresponding parts by weigh...

Embodiment 2

[0032] A method for preparing a low-size shrinkage WPC floor, specifically comprising the following steps:

[0033] (1) Preparation of WPC base material: Weigh the corresponding weight parts of each raw material, carry out high mixing at 100°C for 15 minutes, cold mixing at 50°C for 10 minutes, extruder temperature at 180°C, mold temperature at 190°C ;

[0034] The WPC substrate includes the following raw materials by weight: 100 parts of PVC resin, 15 parts of glass fiber with a specification of 10mm, 3 parts of montmorillonite, 25 parts of dioctyl terephthalate, 10 parts of acrylic acid derivatives, 4 parts of sodium sulfonate, 3 parts of foaming agent, 10 parts of stabilizer, 120 parts of stone powder, and 4 parts of coloring agent; The weight ratio is 100:2.5; the specific treatment method is: mix KH-550 and alcohol in a ratio of 1:3 and spray it on the montmorillonite;

[0035] (2) Preparation of PVC film: Weigh each raw material of corresponding weight portion, with 12...

Embodiment 3

[0041] A method for preparing a low-size shrinkage WPC floor, specifically comprising the following steps:

[0042] (1) Preparation of WPC base material: Weigh the corresponding weight parts of each raw material, perform high mixing at 100°C for 15 minutes, cold mixing at 50°C for 10 minutes, extruder temperature at 175°C, mold temperature at 180°C ;

[0043] The WPC substrate includes the following preparation raw materials by weight: 100 parts of PVC resin, 11 parts of glass fiber with a specification of 8 mm, 2 parts of montmorillonite, 22 parts of dioctyl terephthalate, 9 parts of acrylic acid derivatives, alkyl 3 parts of sodium sulfonate, 2 parts of foaming agent, 7 parts of stabilizer, 110 parts of stone powder, and 3 parts of coloring agent; The weight ratio is 100:2; the specific treatment method is: mix KH-550 and alcohol in a ratio of 1:3 and spray it on the montmorillonite;

[0044] (2) Preparation of PVC film: Weigh each raw material of corresponding parts by we...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-size-shrinkage WPC floor and a preparation method thereof. The low-size-shrinkage WPC floor is formed by compounding a laminated structure composed of a skin, a WPC base material and cork wood from top to bottom in sequence, wherein the WPC base material comprises the following preparation raw materials by weight: PVC resin, glass fiber, montmorillonite, dioctyl terephthalate, an acrylic acid derivative, alkyl sodium sulfonate, a foaming agent, a stabilizer, stone powder and a coloring agent. The glass fiber reinforced WPC base material is prepared by adding the glass fiber, due to the characteristics of the glass fiber, the deformability of the WPC base material can be obviously improved, the heat resistance of the WPC base material is improved, for example, the size shrinkage rate of the WPC base material is improved, the heat warping performance of the base material is improved, and finally the glass fiber reinforced WPC base material can be added to the WPC floor, so that the WPC floor has the heat-resistant characteristic close to that of an SPC floor on the premise that the density is reduced.

Description

technical field [0001] The invention relates to the field of preparation of a low-size shrinkage floor, in particular to a low-size shrinkage WPC floor and a preparation method thereof. Background technique [0002] As a new type of floor covering material, PVC floor has excellent wear resistance, decoration, stain resistance and chemical reagent resistance, so it is more and more popular and recognized by consumers. The traditional hard PVC floor not only has excellent dimensional stability, high locking strength, mildew resistance, moisture resistance, insect resistance, convenient and quick installation, etc., it is very popular in developed countries in Europe and the United States and in the Asia-Pacific market. [0003] The industry is also constantly looking for new floor materials to replace, but the traditional SPC hard floor has the disadvantages of thick texture and high density; although the WPC floor has a low density, its physical properties are not as good as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B27/30B32B27/06B32B21/08B32B21/14C08L27/06C08K13/06C08K7/14C08K9/06C08K9/04C08K3/34C08J9/04C08L91/00C08K5/12C08K3/26
CPCB32B27/304B32B27/06B32B27/08B32B21/08B32B21/14C08J9/04C08J9/0085C08J9/009C08J9/0095C08L27/06C08K2003/265B32B2419/04
Inventor 韦余康李进董玉娇倪清兰陆伟
Owner DECORIA MATERIALS JIANGSU CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com