Method for heat preservation of molten steel in abnormal molten steel tank

A technology for molten steel tanks and abnormalities, which is applied in the field of molten steel insulation for abnormal molten steel tanks, can solve problems such as reducing the operation rate of casting machines, affecting the superheat of molten steel in tundishes, and unfavorable inclusions, etc., achieving convenient and easy technology, reducing labor intensity, Simple operation effect

Active Publication Date: 2021-06-18
ANGANG STEEL CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the influence of the thermal insulation performance of the ladle, the temperature of the molten steel continues to decrease as the pouring progresses, especially for the molten steel tanks with a long turnaround time or after major repairs or minor repairs, the temperature drops rapidly in the later stage of pouring, which will seriously affect the tundish steel Water superheat control
Too low temperature of molten steel in the tundish will lead to poor fluidity of molten steel, which is not conducive to the full floating of inclusions in the tundish. Adhesion and aggregation at places, resulting in the occurrence of low-temperature flocculation accidents, which not only affects the quality of the product, but also easily causes casting machine interruption accidents, affects the smooth flow of production, and reduces the operation rate of the casting machine

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for heat preservation of molten steel in abnormal molten steel tank

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0034] Refined LF furnace produces steel SWRCH22A, medium package target temperature is 1555 ± 5 ° C, and the total length of the large can turn interval is 8 hours and 25 minutes. This steel tank determination level is a can, which belongs to an abnormal steel jug, internal control ingredient Requirements are required to be controlled at 1590 ± 5 ° C as follows.

[0035] element C,% Si,% Mn,% P,% S,% ALS,% Standard range 0.18-0.22 ≤0.10 0.70-1.00 ≤0.025 ≤0.020 0.015-0.055 Target value 0.20 ≤0.10 0.80 ≤0.025 ≤0.020 0.030

[0036] When the steel component is adjusted, the control requirements are met, the tanker stopped the temperature of 1592 ° C, the steel tank stops the bottom blown argon, the lower electrode to the slag interface, and then the temperature control operation, the time controls 2 min, the temperature is completed, and the electrode is increased, this It is strictly forbidden to stir argon stir, and the steel tanker is directl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for heat preservation of molten steel in an abnormal molten steel tank. The method comprises the following steps: 1) feeding the molten steel tank into an LF furnace for refining; 2) after refining is finished, stopping ladle bottom argon blowing stirring of the abnormal molten steel tank, lowering an electrode of the LF furnace to a steel slag interface, and carrying out heating for 1-3 min;3) after heating is finished, removing an argon blowing pipe, moving out the molten steel tank, covering the molten steel tank with a cover, and carrying out pouring in front of a machine. According to the method, heat preservation control is performed on top molten steel mainly in a manner of heating for refining of the LF furnace and stopping molten steel argon blowing stirring, and stable control of the temperature of a tundish in the molten steel pouring process is realized. The method is convenient and feasible in technology and simple to operate, cost input for changing the heat preservation performance of a refractory material is not required, a heat preservation agent is not required to be added by a worker for heat preservation, the labor intensity of the worker is reduced, and the production rhythm of procedures is not affected.

Description

Technical field [0001] The present invention relates to the field of smelting, and more particularly to an abnormal steel water tank steel water insulation. Background technique [0002] After the steel water is treated with the LF furnace, the convection of the casting machine is pouring. Due to the impact of the insulation performance of the wire, the temperature of the steel water is constantly decreasing, especially the steel tank, the steel tank, the water tank after the small repair time is long, and the temperature of the water is faster, which will seriously affect the intermediate package steel. Control of water overheat. Excessive intermediate package steel temperature, resulting in deterioration of molten steel, not conducive to the full upper floating of inclusions in the middle package, the inclusions in the steel are very easy to spit out of the holes in the water, and the diameter water port and the middle packet underwater joint At the point of adhesion, the occur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/18B22D41/015C22C38/02C22C38/04C22C38/06
CPCB22D11/18C22C38/02C22C38/04C22C38/06C22C38/002B22D41/015Y02P10/20
Inventor 王成青孙振宇梁祥远郭猛那廷权马辉
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products