A smelting method and zinc powder technology are applied in the field of combined alkaline zinc powder smelting, which can solve the problems of expensive equipment, harsh operating environment and high cost, and achieve the effect of solving expensive equipment.
Active Publication Date: 2021-07-16
云南云铜锌业股份有限公司
View PDF10 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0004] In view of the above-mentioned deficiencies in the prior art, the object of the present invention is to provide a method for combined smelting of zinc powder by the alkaline method, which aims to solve the problem of expensive equipment, high cost, high energy consumption and problems of zinc powder in the drying process of the existing zinc powder by the alkaline method. There is a problem of poor working environment in the process of unloading
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0059] A smelter adopts a hydrometallurgical method and a three-stage antimony purification method to achieve deep purification.
[0060] The analysis of the new electrolytic solution is as follows, the unit is mg / L, and the unit of Zn is g / L,
[0061] Zn Fe Sb Cd co Ge pH Liquid 1 139.62 6.28 0.003 0.03 0.10 0.006 4.95
[0062] Use 3L of electrolytic new solution, add appropriate amount of caustic soda to obtain a zinc precipitation solution with pH = 7, obtain zinc precipitation residue after filtration, and put the zinc precipitation filter residue into the zinc precipitation filter residue with an initial concentration of 6mol / L according to the ratio of liquid to solid ratio of 8:1 In NaOH solution, stir at 50°C for 1 hour to obtain an alkaline immersion solution, which is directly used in alkaline electrolysis. After electrolysis for 2 hours, the obtained alkaline zinc powder is collected, filtered, and washed. 10%, 15%, and 20% w...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses an alkaline-process zinc powder combined smelting method. The method comprises a zinc deposition process, a filtering process, an alkaline leaching process, an electrolysis process, a washing process, a size mixing process and a purification process, and a stock solution before zinc deposition in the zinc deposition process is a new electrolytic solution in a zinc hydrometallurgy process. The alkaline-process zinc powder combined smelting method adopts an alkaline-process zinc powder preparation and wet-process purification combined smelting mode and simultaneously utilizes a zinc powder wet adding technology, so that the problems of high equipment price, high cost and high energy consumption in the existing alkaline-process zinc powder drying process and severe operation environment in the zinc powder transferring process are solved; and meanwhile, the problems that the grade of alkaline leaching raw materials of alkaline-process zinc powder is unstable, the impurity content is high, and a purification procedure needs to be added to remove impurities are solved. The combined smelting method has the characteristics of low use cost, good effect and excellent working environment, and meets the requirements of low carbon, greenness and environmental protection.
Description
technical field [0001] The invention relates to the field of zinc smelting, in particular to an alkaline zinc powder combined smelting method. Background technique [0002] In the production process of alkaline zinc powder, the alkaline zinc powder produced by electrolysis has high activity. After vacuum filtration and washing, put the wet alkaline zinc powder in the drying chamber of the double-cone rotary dryer to dry, and start the vacuum pump to vacuum after closing. After reaching a certain degree of vacuum, turn on the heating device and dry at a temperature lower than 60-80°C for 1-2 hours. The produced alkaline zinc powder is crushed, screened, weighed, and packaged for sale. In the traditional zinc hydrometallurgy process, metal zinc powder and electric furnace zinc powder need to be used in the purification process to remove impurities such as copper, cadmium, cobalt, antimony, etc. Alkaline zinc powder has the characteristics of large specific surface area and hig...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information