A copper alloy welding wire, preparation method and application

A copper alloy and welding wire technology, which is applied in welding equipment, metal processing equipment, manufacturing tools, etc., can solve the problems of poor melt fluidity, cold working performance, complex formula of manganese aluminum bronze alloy, and difficult operation, etc., so as to improve cold working performance , better melt fluidity, and the effect of improving flow performance

Active Publication Date: 2022-04-01
CHINA INNOVATION ACADEMY OF INTELLIGENT EQUIP CO LTD
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The manganese-aluminum bronze alloy published in the above-mentioned patent has a complex formula, contains elements such as Ni, Y, and La, and has high cost, and has insufficient melt fluidity and poor cold working performance. Insufficient feeding of the casting melt, after repeated drawing and annealing, the operation is difficult, the production cycle is long, and the disconnection rate is high, the yield is low, and the production efficiency is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A copper alloy welding wire, preparation method and application
  • A copper alloy welding wire, preparation method and application
  • A copper alloy welding wire, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] This embodiment discloses a copper alloy. The specific amount of substances is shown in Table 1. The specific preparation method includes the following steps:

[0055] Casting → hot rolling → annealing → swaging → drawing → peeling → sizing forming;

[0056] Among them, the continuous casting temperature is 1045°C and the casting speed is 0.5 m / min;

[0057] The rolling temperature is 570°C and the speed is 0.15 m / s;

[0058] Annealing temperature 580°C, holding time 1 h, reducing gas and inert gas protection;

[0059] Swivel speed 2.5 m / min;

[0060] Drawing speed 3.6 m / s;

Embodiment 2

[0062] The main difference between this embodiment and embodiment 1 is shown in Table 1;

[0063] The specific preparation method of this embodiment comprises the following steps:

[0064] Casting → hot rolling → annealing → swaging → drawing → peeling → sizing forming;

[0065] Among them, the continuous casting temperature is 1070°C and the casting speed is 0.6 m / min;

[0066] Rolling temperature 550℃, speed 0.2 m / s;

[0067] Annealing temperature 550°C, holding time 1.5 h, reducing gas and inert gas protection;

[0068] Swivel speed 2.5 m / min;

[0069] Drawing speed 3.6 m / s;

Embodiment 3

[0071] The main difference between this embodiment and embodiment 1 is shown in Table 1;

[0072] Concrete preparation method comprises the following steps:

[0073] Casting → hot rolling → annealing → swaging → drawing → peeling → sizing forming;

[0074] Among them, the continuous casting temperature is 1055°C and the casting speed is 0.55 m / min;

[0075] The rolling temperature is 520°C, and the speed is 0.15 m / s;

[0076] Annealing temperature 600°C, holding time 1.3 h, reducing gas and inert gas protection;

[0077] Swivel speed 2.5 m / min;

[0078] Drawing speed 3.6 m / s;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a copper alloy welding wire, which comprises: 8.0 to 10.0% Al; 10.0 to 12.0% Mn; 2.0 to 4.0% Fe; 0.2 to 0.5% Sn; 0.1 to 0.3% Zn; 0.01 to 0.03% P; 0.01 to 0.35% Cr; 0.03 to 0.06% Si; the balance is Cu and unavoidable impurities; the invention also discloses a forming method of copper alloy welding wire, combining material properties, introducing hot rolling and swaging, specifically including: ingredients, Casting, hot rolling, annealing, swaging, wire drawing, peeling, and sizing forming; the invention also discloses the application of the copper alloy welding wire; the copper alloy welding wire casting performance and processing performance of the invention are greatly improved, and with the efficient forming method, The disconnection rate in the production process is reduced, the yield is increased, and the production efficiency is significantly improved.

Description

technical field [0001] The invention relates to the technical field of copper alloys, in particular to a copper alloy welding wire, a preparation method and an application. Background technique [0002] The birth and development of comprehensive mechanized mining with hydraulic support as the main equipment is a major revolution in the history of coal mine production. The face of production has completely changed. Copper melting technology on the inner wall of hydraulic support column oil cylinder, as an emerging oil cylinder repair technology in recent years, adopts CMT (cold metal transition technology) welding method to melt copper alloy welding wire to obtain wear-resistant and corrosion-resistant copper alloy layer combined with base metallurgy , and has the thermal and electrical conductivity of copper, so as to improve the life of the hydraulic support. As the working conditions of the hydraulic support become worse and the working resistance increases, the requirem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C9/05B21C37/04B23K35/30B23K35/40
CPCC22C9/05B21C37/04B23K35/302B23K35/40
Inventor 王朋旭王博孙华为樊志斌何茜宁少晨赵丹纠永涛
Owner CHINA INNOVATION ACADEMY OF INTELLIGENT EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More