5D three-dimensional embossment effect material and manufacturing process
A technology of three-dimensional relief and driving roller, which is applied in the direction of lamination, layered products, synthetic resin layered products, etc. It can solve the problems of unfavorable display and unsatisfactory 5D relief three-dimensional effect, so as to facilitate the overall hot pressing and improve the structural strength and tensile properties, the effect of ensuring stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0041] refer to figure 1 Said, a 5D three-dimensional relief effect material, the 5D three-dimensional relief effect material is composed of the following components by weight: 65 parts of PVC resin, 45 parts of polyurethane, 35 parts of polymethyl methacrylate, 12 parts of phosphite, two 15 parts of glycol dibenzoate, 4 parts of PVC stabilizer, 1 part of non-toxic plasticizer, 1.5 parts of p-methoxycyclohexyl cinnamate, 1.2 parts of 4-methyl-6-methoxycoumarin share.
[0042] A manufacturing process of a 5D three-dimensional relief effect material, comprising the following steps;
[0043] Step 1: Put all the raw materials into the mixer in proportion for mixing, the temperature is 115°C, the mixing time is 40min, the stirring speed is 450r / min, the double-mixed material is added to the screw extruder and extruded into masterbatch , the masterbatch is extruded and blown by a plastic film blowing machine, and the temperature of the blown film is controlled at 170°C to obtain a...
Embodiment 2
[0047] refer to figure 1 As shown, as another preferred embodiment of the present invention, the difference from Example 1 is that a 5D three-dimensional relief effect material is composed of the following components in parts by weight: 82 parts of PVC resin, 35 parts of polyurethane 28 parts of polymethyl methacrylate, 16 parts of phosphite, 5 parts of diethylene glycol dibenzoate, 4 parts of PVC stabilizer, 1 part of non-toxic plasticizer, p-methoxycinnamic acid ring 1.1 parts of hexyl ester, 1.5 parts of 4-methyl-6-methoxycoumarin.
[0048] A manufacturing process of a 5D three-dimensional relief effect material, comprising the following steps;
[0049] Step 1: Put all the raw materials into the mixer in proportion for mixing, the temperature is 105°C, the mixing time is 40min, the stirring speed is 350r / min, the double-mixed material is added to the screw extruder and extruded into masterbatch , the masterbatch is extruded and blown by a plastic film blowing machine, and...
Embodiment 3
[0054] refer to Figure 2-11 Shown, a kind of device of 5D three-dimensional relief effect material, device is the bonding machine of step 3, comprises support frame 1, pattern film 4, microstructure mold 5 and horizontal plate 8, and horizontal plate 8 is provided with multiple groups, horizontal plate 8 Both ends of the plate 8 are fixedly installed on the bottom of the inner wall of the support frame 1, and the support frame 1 is connected with a first drive structure 2 for driving the movement of the microstructure mold 5. The first drive structure 2 includes a first pulley 201, a first drive roller 202, Belt 203 and drive motor 204, drive motor 204 is fixedly installed on the side wall of support frame 1, and support frame 1 is connected with the first drive roller 202 through the bearing that is fixedly connected, and one group of first drive roller 202 and drive motor 204 wherein The output end of the first drive roller 202 is fixedly connected with the first pulley 201...