Vulcanization composition based on nitrile rubber and butadiene rubber, vulcanized rubber and preparation method and application thereof
A technology of butadiene rubber and nitrile rubber, applied in the field of vulcanized rubber and its preparation, can solve the problems of reduced product performance, large difference in polarity, poor compatibility of composite materials, etc., and achieve excellent low temperature resistance and improved compression set. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0079] Example 1
[0080] The composition formulation of the present embodiment is shown in Table 2.
[0081] The preparation method of vulcanized rubber is as follows:
[0082] First mixed:
[0083] The initial temperature of the renewal is 70 ° C, the rotor speed is 70 rpm, and the rubber substrate, reinforcing agent, calcium sulfate, vulcanized activator, anti-aging agent and plasticizer are added to the mesh for the first mixer for the first mix. Glue, parked for 4 hours to get the mother making gel.
[0084] Second mix:
[0085] The initial temperature of the renewal is set to 50 ° C, the rotor rotor speed is 60 rpm, and the mother refiner, sulfurization agent and vulcanization promoter are put into the mesh, mixed 3 min, and the gelatin.
[0086] The rubber obtained by the above method is 0.5 mm in the roller pitch, and the roller temperature is 60 ° C, then the roller is adjusted to 5 mm, and then the obtained mixed rubber is parked 24 h (below In the case where there is no...
Example Embodiment
[0089] Example 10
[0090] The formulation of the composition employed in the present embodiment is exactly the same as the formulation of the composition in Example 1, and the process of the preparation of the sulfide gel of the present embodiment is different from those of Example 1, specifically:
[0091] The initial temperature of the renewal is set to 55 ° C, the rotational speed is 60 rpm, and the rubber substrate, carbon black, white carbon black, calcium sulfate must, vulcanized activator, anti-aging agent and plasticizer are mixed in the mesh for 4 minutes. The end of the melancholy, putting the mother making gel, sulfurization and vulcanization promoter into the mesh, falling into the endolic bundle, and continues to kill 3 minutes, and the gelatin. The gel obtained by the above method is from 0.5 mm, and the roll temperature is 60 ± 5 ° C, then the roller distance is adjusted to 5 mm, and then the obtained mixed rubber is parked 24 h.
[0092] The above-mentioned mixer ...
PUM
Property | Measurement | Unit |
---|---|---|
Width | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap