Preparation method of novel rubber additive

A rubber additive, a new technology, applied in the field of preparation of new rubber additives, can solve problems such as single performance, achieve good compatibility, improve dispersion, and improve plasticity

Pending Publication Date: 2021-11-02
赣州晶鑫新材料有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Different types of processing aids play different roles in rubber. At present, there are many kinds of products, but the performance is relatively single.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of novel rubber additive
  • Preparation method of novel rubber additive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A preparation method of a novel rubber auxiliary agent, the processing aid comprising the following components in parts by weight: 20 parts of vinyl resin, 18 parts of unsaturated polyester resin, 12 parts of unsaturated fatty acid, 1.5 parts of zinc oxide, trifluoropropylene 6 parts of methyl dichlorosilane.

[0015] Specifically include the following steps:

[0016] S1: Add the unsaturated fatty acid into the container, heat to 80° C. to melt, stir and then add zinc oxide, and raise the temperature to 120° C. to react for 2 hours to obtain a viscous liquid.

[0017] S2: Add the viscous liquid obtained in step S1 into vinyl resin, unsaturated polyester resin and trifluoropropylmethyldichlorosilane, raise the temperature to 110° C., and melt blend for 3 hours.

Embodiment 2

[0019] A preparation method of a novel rubber auxiliary agent, the processing aid comprising the following components in parts by weight: 30 parts of vinyl resin, 25 parts of unsaturated polyester resin, 16 parts of unsaturated fatty acid, 2 parts of zinc oxide, trifluoropropylene 9 parts of methyl dichlorosilane.

[0020] Specifically include the following steps:

[0021] S1: Add the unsaturated fatty acid into the container, heat to 90°C to melt, stir and then add zinc oxide, and raise the temperature to 130°C for 3 hours to obtain a viscous liquid.

[0022] S2: Add the viscous liquid obtained in step S1 into vinyl resin, unsaturated polyester resin and trifluoropropylmethyldichlorosilane, raise the temperature to 115° C., and melt blend for 5 hours.

Embodiment 3

[0024] A preparation method of a novel rubber auxiliary agent, the processing aid comprising the following components in parts by weight: 26 parts of vinyl resin, 22 parts of unsaturated polyester resin, 14 parts of unsaturated fatty acid, 1.8 parts of zinc oxide, trifluoropropylene 8 parts of methyl dichlorosilane.

[0025] Specifically include the following steps:

[0026] S1: Add the unsaturated fatty acid into the container, heat to 85°C to melt, then add zinc oxide after stirring, and raise the temperature to 125°C for 2.5 hours to obtain a viscous liquid.

[0027] S2: Add the viscous liquid obtained in step S1 into vinyl resin, unsaturated polyester resin and trifluoropropylmethyldichlorosilane, raise the temperature to 112° C., and melt blend for 4 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a novel rubber additive. The novel rubber additive is prepared from the following components in parts by weight: 20-30 parts of vinyl resin, 18-25 parts of unsaturated polyester resin, 12-16 parts of unsaturated fatty acid, 1.5-2 parts of zinc oxide and 6-9 parts of trifluoropropyl methyl dichlorosilane. The preparation method comprises the steps of adding unsaturated fatty acid into a container, heating to the temperature of 80-90 DEG C for melting, stirring, then adding zinc oxide, raising the temperature to 120-130 DEG C, and reacting for 2-3 hours to obtain viscous liquid; and adding the viscous liquid obtained in the step S1 into vinyl resin, unsaturated polyester resin and trifluoropropyl methyl dichlorosilane, raising the temperature to 110-115 DEG C, and carrying out melt blending for 3-5 hours to obtain the additive.

Description

technical field [0001] The invention belongs to the technical field of fine chemicals, and in particular relates to a preparation method of a novel rubber additive. Background technique [0002] Processing aid is a kind of compound material. Although it is used in a small amount in rubber compound, it can improve the operation performance of the compound and improve the quality of rubber products. There are many classifications of processing aids, including homogenizers, dispersants, plasticizers, lubricants, peptizers, etc. In terms of improving processing performance, the most basic conditions for processing aids are: compatibility with rubber and its compounding agents; non-polar groups with long chains and easy migration into rubber molecules; polar groups for inorganic compounding agents Has strong affinity; easy to add and has a suitable melting point. However, it is impossible for most processing aids to have all the conditions, and a processing aid cannot have the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/10C08L67/06C08K3/22C08K5/09C08K5/5419C08L7/00C08K13/02
CPCC08L63/10C08L7/00C08K2003/2296C08L67/06C08K3/22C08K5/09C08K5/5419C08K13/02
Inventor 罗杰宇
Owner 赣州晶鑫新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products