Polyethylene fiber cloth capable of absorbing sweat on skin surface and preparation method thereof

A polyethylene fiber and polyethylene technology, applied in the field of fabric production, can solve the problems of inability to absorb wearers, poor sweat absorption, weak antibacterial effect, etc., and achieve the effect of good antibacterial effect, high product quality and easy removal.

Pending Publication Date: 2021-11-26
青岛信泰科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The elongation at break of polyene fiber filter cloth is 18-35%, the strength is low, the surface of fiber filter cloth is smooth, and the texture is soft, and the clothes made of polyethylene fiber cloth have poor sweat absorption ability, weak antibacterial effect, and cannot absorb skin. Sweat on the surface makes the wearer uncomfortable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] An absorbing sweat on the skin of polyethylene fiber cloth, including ultrahigh molecular weight polyethylene fibers between two layers of cloth, and the two adhesive layers blended fabrics, ultrahigh molecular weight polyethylene fiber cloth layers are bonded by an adhesive , two blended fabric layer is provided on the outermost layer, ultrahigh molecular weight polyethylene fiber was passed through a filter cloth to dissolve high molecular weight polyethylene, fibers made of a hard and solvent naphtha, dissolved liquid and ultrahigh molecular weight polyethylene, hard fibers and the mass of the solvent to oil ratio of 25: 3: 0.5, blended fabric layer is made of bamboo fiber and cotton fibers;

[0033] In this embodiment, the preparation method can absorb sweat on the skin of polyethylene fiber cloth comprising the steps of:

[0034] S11: Preparation of ultrahigh molecular weight polyethylene fiber cloth;

[0035] S12: Preparation blended fabric layer;

[0036] S13: The ul...

Embodiment 2

[0051] An absorbing sweat on the skin of polyethylene fiber cloth, three layers of ultrahigh molecular weight polyethylene fibers comprising filter cloth, two layers blended fabrics and adhesives, both between each adjacent two of ultrahigh molecular weight polyethylene filter cloth by adhesive bonding, two blended fabric layer disposed on an outermost layer, ultrahigh molecular weight polyethylene fiber was passed through a filter cloth to dissolve high molecular weight polyethylene, fibers made of a hard and solvent naphtha, and ultrahigh molecular weight polyethylene lysate , mass ratio of the hard fibers and solvent oil is 30: 3: 0.4, blended fabric layer is made of bamboo fiber and cotton fibers;

[0052] In this embodiment, the preparation method can absorb sweat on the skin of polyethylene fiber cloth comprising the steps of:

[0053] S11: Preparation of ultrahigh molecular weight polyethylene fiber cloth;

[0054] S12: Preparation blended fabric layer;

[0055] S13: The ul...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
aspect ratioaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of fabric production, in particular to polyethylene fiber cloth capable of absorbing sweat on the skin surface and a preparation method thereof.The polyethylene fiber cloth comprises at least two layers of ultra-high molecular weight polyethylene fiber filter cloth, two blended fabric layers and an adhesive, every two adjacent layers of ultra-high molecular weight polyethylene fiber filter cloth are bonded through the adhesive, the two blended fabric layers are arranged on the outermost layer. According to the invention, the multi-layer ultra-high molecular weight polyethylene fiber filter cloth and the blended fabric are combined and are bonded through the adhesive, and the edges are sewn after bonding, so that the adhesion among the multi-layer fiber filter cloth is facilitated, the multi-layer fiber filter cloth is not layered, and the blended fabric arranged on the outer surface is good in sweat absorption performance, soft, comfortable and good in antibacterial effect; the polyethylene fiber cloth is attached to the skin of the human body and makes contact with the skin to absorb sweat on the surface of the skin, the sweat on the surface of the skin can be effectively absorbed, more comfort is achieved, and the body health of people is protected.

Description

Technical field [0001] The present invention relates to fabric production technology, and in particular a polyethylene fiber cloth and a method of preparing a skin surface can absorb sweat. Background technique [0002] Industrial use more filter cloth woven from natural and synthetic fibers, synthetic fibers using polyester multi-long, short fibers, long nylon, polypropylene short fibers and long and short fibers. Synthetic fibers, the polyester fiber cloth acid, weak base resistance, good recovery, elongation at break of 20 to 50%, a breaking strength of 438g / d. Polyalkylene filter cloth is 18 to 35% elongation at break, low strength, the fiber cloth surface is smooth, soft and absorbent capacity of the laundry is now prepared polyethylene fiber cloth poor weak antibacterial effect, can not be absorbed by the skin surface wear sweat makes people uncomfortable. Inventive content [0003] Object of the present invention to provide a method for preparing polyethylene fiber fabr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/02
CPCB32B5/02B32B5/06B32B5/08B32B5/26B32B7/12B32B37/1284B32B38/00D03D15/217D03D15/283D01D5/12D01D10/02B32B2038/008B32B2250/40B32B2262/0253B32B2262/065B32B2262/062B32B2307/7145B32B2307/726B32B2262/105B32B2262/106B32B2437/00D10B2201/02D10B2201/10D10B2321/021
Inventor 房朕杜兴信陈龙
Owner 青岛信泰科技有限公司