Lithium ion battery composite positive electrode material with core-shell structure, and preparation method thereof

A composite cathode material, lithium-ion battery technology, applied in battery electrodes, positive electrodes, secondary batteries, etc.

Pending Publication Date: 2021-11-26
上海颂柏智能技术开发中心
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The voltage of lithium manganese phosphate LMP is relatively high, which matches the conventional electrolyte, but its capacity must be in the nanometer state to be able to play

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium ion battery composite positive electrode material with core-shell structure, and preparation method thereof
  • Lithium ion battery composite positive electrode material with core-shell structure, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1 of the present invention: a lithium-ion battery composite cathode material with a core-shell structure:

[0020] Lithium-ion battery composite positive electrode material composition is (LiMn 2 o 4 ) 0.9 (LiMnPO 4 ) 0.1 ;LiMn 2 o 4 As the core material, LiMnPO 4 As the housing material, LiMnPO 4 to LiMn 2 o 4 Fully coated; LiMnPO 4 The thickness is 200nm.

Embodiment 2

[0021] Embodiment 2: a lithium-ion battery composite cathode material with a core-shell structure:

[0022] Lithium-ion battery composite positive electrode material composition is (LiNi 0.5 mn 1.5 o 4 ) 0.95 (LiMnPO 4 ) 0.05 ; The LiNi 0.5 mn 1.5 o 4 As the core material, LiMnPO 4 As the housing material, LiMnPO 4 To LiNi 0.5 mn 1.5 o 4 Fully coated; LiMnPO 4 The thickness is 100nm.

Embodiment 3

[0023] Embodiment 3: a lithium-ion battery composite cathode material with a core-shell structure:

[0024] Lithium-ion battery composite positive electrode material composition is (LiNi 0.5 mn 1.5 o 4 ) 0.85 (LiMnPO 4 ) 0.15 ;LiNi 0.5 mn 1.5 o 4 As the core material, LiMnPO 4 As the housing material, LiMnPO 4 To LiNi 0.5 mn 1.5 o 4 Fully coated; LiMnPO 4 The thickness is 900nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a lithium ion battery composite positive electrode material with a core-shell structure. The composite positive electrode material is LTMOxLTMP1-x, and x is more than or equal to 0.75 and less than or equal to 0.95; LTMO is a core material, LTMP is a shell material, and the LTMO is completely coated by the LTMP; and the thickness of the LTMP ranges from 10 nm to 5000 nm. The invention further discloses a preparation method of the composite positive electrode material. According to the positive electrode material disclosed by the invention, the shell LTMP completely coats the inner core LTMO, so that the LTMO is completely separated from the electrolyte, the service life of the lithium ion battery is prolonged, the use safety performance of the lithium ion battery is improved, and meanwhile, the charging time of the battery is shortened; and according to the preparation method, particle distribution is easier to control in a proper range, and preparation of a high-energy positive electrode and a high-energy battery is facilitated.

Description

technical field [0001] The invention relates to the technical field of lithium-ion rechargeable battery materials, in particular to a lithium-ion battery composite cathode material with a core-shell structure and a preparation method thereof. Background technique [0002] At present, the lithium-ion battery cathode materials used by global lithium-ion battery manufacturers can be roughly divided into two categories, one is transition metal oxide lithium salt (LTMO), and its representative material is lithium cobalt oxide, ternary (nickel-manganese Lithium cobalt oxide NMC, lithium nickel cobalt aluminate NCA), lithium manganate and lithium nickel manganese oxide are spinel; the second type is transition metal lithium phosphate salt or olivine (LTMP). Each material has its advantages and disadvantages. [0003] The voltage of lithium cobaltate in transition metal oxide lithium salt LTMO is high, but its gram capacity utilization rate can only reach 50% of its theoretical val...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/36H01M4/50H01M4/58H01M10/0525
CPCH01M4/364H01M4/50H01M4/5825H01M10/0525H01M2004/028Y02E60/10
Inventor 孙升
Owner 上海颂柏智能技术开发中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com