Polypropylene fiber bulked filament for environment-friendly fiber bundle filter and preparation method of polypropylene fiber bulked filament

The technology of bulked filament and fiber bundle is applied in the field of polypropylene bulked filament and its preparation, and can solve the problems of not considering the cross-sectional shape of the thick fiber filament, shortening the service life of the fiber filter, and blocking the use time of the fiber filter, etc. To achieve the effect of improving filtration efficiency and interception capacity, small filtration resistance and good rebound

Pending Publication Date: 2021-12-10
GUANGDONG MODERN HIGH TECH FIBER CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the patent document CN200710038014.2 only requires the diameter of the thick fiber to be 100 to 1000 microns, without considering the cross-sectional shape of the thick fiber, and the diameter of the thick fiber is difficult to reach 100 microns, which causes fiber loops The elasticity is not high, causing the fiber filter to be blocked after a short service life
When filtering chlorine-containing substances, table salt, tap water, bleaching powder, disinfectant, pesticide, paint, etc. will cause fiber oxidation, and ultraviolet radiation will cause fiber aging, resulting in shortened service life of fiber filter

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene fiber bulked filament for environment-friendly fiber bundle filter and preparation method of polypropylene fiber bulked filament
  • Polypropylene fiber bulked filament for environment-friendly fiber bundle filter and preparation method of polypropylene fiber bulked filament

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A polypropylene bulked filament used for environmental protection fiber bundle filters, the linear density of the single filament is 40dtex, the linear density of the multifilament is 3000dtex, the addition ratio of fiber-grade polypropylene chips is 96.0%, and the addition ratio of anti-chlorine masterbatch is 2.0%, the addition ratio of anti-UV masterbatch is 2.0%.

[0037] like figure 1 shown, including the following steps:

[0038] A: Add 1 polypropylene chip, 2 anti-chlorine masterbatch, and 3 anti-UV masterbatch in proportion, and put them into the extruder to melt after precise measurement of 4 raw and auxiliary materials. The temperature of each zone adopts a heating mode from high to low, five The heating temperatures were 210°C, 208°C, 206°C, 204°C and 202°C, respectively.

[0039] B: The molten fiber is spun through a 5-lobed special-shaped spinneret, and a three-lobed spinneret micro-hole is set on the 5-three-lobed special-shaped spinneret, and a three-lo...

Embodiment 2

[0047]A polypropylene bulked filament used for environmental protection fiber bundle filters, the linear density of the single filament is 43dtex, the linear density of the multifilament is 3300dtex, the addition ratio of fiber-grade polypropylene chips is 95.5%, and the addition ratio of anti-chlorine masterbatch is 2.0%, the anti-UV masterbatch addition ratio is 2.5%.

[0048] like figure 1 shown, including the following steps:

[0049] A: Add 1 polypropylene chip, 2 anti-chlorine masterbatch, and 3 anti-UV masterbatch in proportion, and put them into the extruder to melt after precise measurement of 4 raw and auxiliary materials. The temperature of each zone adopts a heating mode from high to low, five The heating temperatures were 215°C, 213°C, 210°C, 208°C and 206°C, respectively.

[0050] B: The molten fiber is spun through a 5-lobed special-shaped spinneret, and a three-lobed spinneret micro-hole is set on the 5-three-lobed special-shaped spinneret, and a three-lobed ...

Embodiment 3

[0058] A polypropylene bulked filament for environmental protection fiber bundle filter, the linear density of the single filament is 45dtex, the linear density of the multifilament is 3600dtex, the addition ratio of fiber-grade polypropylene chips is 95.0%, and the addition ratio of anti-chlorine masterbatch is 2.5%, the anti-UV masterbatch addition ratio is 2.5%.

[0059] like figure 1 shown, including the following steps:

[0060] A: Add 1 polypropylene chip, 2 anti-chlorine masterbatch, and 3 anti-UV masterbatch in proportion, and put them into the extruder to melt after precise measurement of 4 raw and auxiliary materials. The temperature of each zone adopts a heating mode from high to low, five The heating temperatures were 220°C, 218°C, 216°C, 214°C and 212°C, respectively.

[0061] B: The molten fiber is spun through a 5-lobed special-shaped spinneret, and a three-lobed spinneret micro-hole is set on the 5-three-lobed special-shaped spinneret, and a three-lobed speci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a polypropylene fiber bulked filament for an environment-friendly fiber bundle filter and a preparation method of the polypropylene fiber bulked filament, and belongs to the technical field of chemical fiber materials. The cross section of a monofilament is a trilobal special-shaped bulked filament, polypropylene slices, chlorine-resistant master batches and anti-UV master batches are mixed for spinning, the linear density of a single filament is 40-45 dtex, the density of a multifilament is 3000-3600 dtex, and the diameter of the fiber is 100 microns or above. The anti-chlorine master batch is prepared by mixing, melting and pelletizing a chlorine-resistant antioxidant double-effect agent and polypropylene powder according to a ratio of 1: 1, and the anti-UV master batch is prepared by mixing, melting and pelletizing 15.0-17.0% of an anti-aging agent, 15.0-17.0% of UV powder and 66.0-70.0% of polypropylene powder. The polypropylene fiber bulked filament has the advantages of large diameter, high fluffiness, good springback, low cost, large specific surface area, and low filtering resistance, the filtering efficiency and the pollutant intercepting capacity are improved, the chlorine oxidation resistance and the UV aging resistance are improved, and the service life of the filter is prolonged.

Description

technical field [0001] The invention relates to the technical field of chemical fiber materials, in particular to a polypropylene bulked filament used for an environmental-friendly fiber bundle filter and a preparation method thereof. Background technique [0002] Fiber bundle filter is a pressure type fiber filter equipment with advanced structure and excellent performance, which is widely used in environmental engineering, water treatment equipment and environmental protection equipment. In the prior art, the patent document CN200710038014.2 only requires the diameter of the thick fiber to be 100 to 1000 microns, without considering the cross-sectional shape of the thick fiber, and the diameter of the thick fiber is difficult to reach 100 microns, which causes fiber loops The elasticity is not high, causing the fiber filter to be blocked after a short service life. When filtering chlorine-containing substances, table salt, tap water, bleaching powder, disinfectant, pestic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/46D01F1/10D01D5/253B01D39/04
CPCD01F6/46D01F1/106D01F1/10D01D5/253B01D39/04B01D2239/0407B01D2239/10
Inventor 郭清海郭人琦江建平张远清柯伟斌
Owner GUANGDONG MODERN HIGH TECH FIBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap