Modified cellulose spunlace non-woven fabric and preparation method thereof

A technology of spunlace non-woven fabric and cellulose, applied in the direction of plant fiber, fiber treatment, fiber type, etc., can solve the problems of poor durability and poor mechanical properties of spunlace non-woven fabric, so as to improve the mechanical properties and improve the The effect of photocatalytic antibacterial performance and improving the performance of decomposing formaldehyde

Active Publication Date: 2021-12-10
深圳市鑫唯科防静电科技有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has high transparency and high water absorption, and its raw materials are all from plants, so that the cellulose spunlace non-woven fabric also has good skin-friendly properties, but the spunlace non-woven fabric has poor mechanical properties and poor durability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified cellulose spunlace non-woven fabric and preparation method thereof
  • Modified cellulose spunlace non-woven fabric and preparation method thereof
  • Modified cellulose spunlace non-woven fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0035] Preparation Example 1 Modified Cellulose

[0036] Synthetic route such as figure 1 , the preparation method is as follows:

[0037] S1. Cellulose treatment: Soak 50g of cellulose in 200mL of petroleum ether and ethyl acetate mixed solvent (the volume ratio of petroleum ether and ethyl acetate is 3:2) for 1h, filter, dry, and then add 100mL of silane In the aqueous ethanol solution of coupling agent KH550 (the content of KH550 is 3wt%, the content of ethanol is 35wt%, and the balance is water), add ammonia water dropwise to adjust the pH value to 8, react for 0.5h, filter, and dry at 120°C for 0.5 h, then placed in 100mL ethanol, ultrasonically cleaned for 0.5h, filtered, and dried to obtain surface-grafted cellulose;

[0038] S2. Preparation of intermediate: Dissolve 20g of 3-bromopropylamine in 200mL of dichloromethane, add 100g of surface-grafted cellulose prepared in step S1, heat to 30°C under nitrogen protection, stir for 2h, filter, and use Wash with ethanol an...

preparation example 2

[0040] Preparation Example 2 Modified Cellulose

[0041] Synthetic route such as figure 1 , the preparation method is as follows:

[0042] S1. Cellulose treatment: Soak 50g of cellulose in 200mL of petroleum ether and ethyl acetate mixed solvent (the volume ratio of petroleum ether and ethyl acetate is 5:2) for 2h, filter, dry, and then add 100mL of silane In the ethanol aqueous solution of coupling agent KH550 (the content of KH550 is 5wt%, the content of ethanol is 40wt%, and the balance is water), ammonia water is added dropwise to adjust the pH value to 9, react for 1h, filter, and dry at 140°C for 1h, Then placed in 100mL ethanol, ultrasonically cleaned for 1h, filtered, and dried to obtain surface-grafted cellulose;

[0043] S2. Preparation of intermediate: Dissolve 40g of 3-bromopropylamine in 200mL of dichloromethane, add 100g of surface-grafted cellulose prepared in step S1, heat to 50°C under nitrogen protection, stir for 4h, filter, and use Wash with ethanol and dr...

preparation example 3

[0045] Preparation Example 3 Modified Cellulose

[0046] Synthetic route such as figure 1 , the preparation method is as follows:

[0047] S1. Treatment of cellulose: Soak 50g of cellulose in 200mL of petroleum ether and ethyl acetate mixed solvent (the volume ratio of petroleum ether and ethyl acetate is 4:2) for 1.5h, filter, dry, and then add 100mL of Silane coupling agent KH550 in ethanol aqueous solution (the content of KH550 is 4wt%, the content of ethanol is 37wt%, and the balance is water), add ammonia water dropwise to adjust the pH value to 8.5, react for 1h, filter, and dry at 130°C for 1h , then placed in 100mL ethanol, ultrasonically cleaned for 1h, filtered, and dried to obtain surface-grafted cellulose;

[0048] S2. Preparation of intermediate: Dissolve 30g of 3-bromopropylamine in 200mL of dichloromethane, add 100g of surface-grafted cellulose prepared in step S1, heat to 40°C under nitrogen protection, stir for 3h, filter, and use Wash with ethanol and dry ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a modified cellulose spunlace non-woven fabric and a preparation method thereof, and belongs to the technical field of spunlace non-woven fabrics. The modified cellulose spunlace non-woven fabric is prepared from the following raw materials of modified cellulose, polypropylene, tetrabutyl titanate and deionized water. The modified cellulose has a structure shown in the specification, wherein n is equal to 100 to 300. The prepared modified cellulose spunlace non-woven fabric not only has good antibacterial and bacteriostatic performance, but also has certain formaldehyde purification capacity, good skin-friendly performance and good mechanical performance; after spunlace reinforcement, fibers in the non-woven fabric are displaced, interspersed, entangled and cohered to form countless flexible entanglement points, so that the non-woven fabric is reinforced, and the high-performance spunlace non-woven fabric is obtained.

Description

technical field [0001] The invention relates to the technical field of spunlace nonwoven fabrics, in particular to a modified cellulose spunlace nonwoven fabric and a preparation method thereof. Background technique [0002] Cellulose spunlace non-woven fabric is made of cellulose through spunlace process. Since the cellulose comes from plants and no chemical binder is added during the processing, the non-woven fabric is soft, hydrophilic, Skin-adhesive properties, widely used in fabric base fabrics, wet wipes, medical dressings and other occasions. [0003] Non-woven fabrics, also known as non-woven fabrics, are composed of oriented or random fibers. It is called cloth because of its appearance and certain properties. To put it simply: it is not interwoven and knitted together by one yarn, but the fibers are directly bonded together by physical or chemical methods, so when you get the glue in your clothes When you weigh it, you will find that you can't pull out the threa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/56D04H1/559D04H1/49D04H1/541D04H1/544C08B15/06D06M11/46D06M101/06D06M101/20
CPCD04H1/56D04H1/559D04H1/49D04H1/544D04H1/5418C08B15/06D06M11/46D06M16/00D06M2101/06D06M2101/20
Inventor 苏鹏
Owner 深圳市鑫唯科防静电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap