Special flame retardant for nylon fabrics and preparation method of special flame retardant

A technology of nylon fabric and flame retardant, which is applied in the direction of textiles and papermaking, etc., can solve the problems of not being able to wash, cannot apply fabrics, restrictions, etc., and achieve good flame retardant effect

Pending Publication Date: 2021-12-14
苏州同构科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Nylon 66 is a thermoplastic resin composed of polyhexamethylene adipamide with high mechanical strength and mechanical strength. It is widely used in engineering plastics, mechanical accessories and synthetic fibers, but its flammability limits its use in many other fields. Therefore, the design concept of flame retardant nylon 66 has a very broad application prospect
[0003] CN109836817A discloses a halogen flame retardant and its application, using materials such as decabromodiphenylethane, aluminum fluoride, zinc borate, antimony trioxide, etc., the prepared flame retardant can be used for fire extinguishing, and reduces the flame retardant It is difficult to produce, but it has poor compatibility with fabrics and is not washable, so it cannot be applied to fabrics
[0004] CN102876030A discloses a composite environmentally-friendly flame retardant for nylon 66 and nylon 66 flame-retardant plastics, and uses materials such as antimony trioxide and melamine cyanurate to prepare a special flame retardant for nylon 66. However, when it is applied to clothing, it is easy to cause clothing to change. hard, less skin-friendly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The first aspect of this embodiment provides a special flame retardant for nylon fabrics, the preparation raw materials include: polyhalogenated aromatic compounds, nitrogen oxides, protein derivatives, and additives.

[0043] The weight ratio of the polyhalogenated aromatic compounds, nitrogen oxides, and protein derivatives is 8:2:5.

[0044] The weight ratio of the total weight of the polyhalogenated aromatic compounds, nitrogen oxides, and protein derivatives to the additives is 3:1.

[0045] The polyhalogenated aromatic compound is decabromodiphenylethane with an average particle size of 4 μm, purchased from Shanghai Qizhi Chemical Co., Ltd.

[0046] The nitrogen group oxide is antimony trioxide, the average particle size is 0.5 μm, and the mass content of impurity selenium is 0.002%.

[0047] The protein derivative is melamine cyanurate.

[0048] The additive is polyurethane with a viscosity (80° C.) of 500 mPa.s and a tear strength of 7.85 MPa, purchased from F...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Average particle sizeaaaaaaaaaa
Average particle sizeaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of C09K21 / 04, in particular to a special flame retardant for nylon fabrics and a preparation method of the special flame retardant. The special flame retardant is prepared from the following raw materials: a polyhalogenated aromatic compound, a nitrogen oxide, a protein refined derivative and an auxiliary agent, and the relative molecular mass of the protein refined derivative is 220-400. The flame retardant is good in flame retardant effect, can realize non-combustibility of nylon 66, and is suitable for various application scenes; after being coated with the flame retardant, the flame retardant has no influence on the mechanical property of the nylon 66; and the flame retardant in the prior art can reduce the oxidation resistance and wear resistance of nylon 66, and the flame retardant specifically solves the problems.

Description

technical field [0001] The invention relates to the field of C09K21 / 04, in particular to a special flame retardant for nylon fabric and a preparation method thereof. Background technique [0002] Nylon 66 is a thermoplastic resin composed of polyhexamethylene adipamide with high mechanical strength and mechanical strength. It is widely used in engineering plastics, mechanical accessories and synthetic fibers, but its flammability limits its use in many other fields. Therefore, the design concept of flame retardant nylon 66 has a very broad application prospect. [0003] CN109836817A discloses a halogen flame retardant and its application, using materials such as decabromodiphenylethane, aluminum fluoride, zinc borate, antimony trioxide, etc., the prepared flame retardant can be used for fire extinguishing, and reduces the flame retardant It is difficult to produce, but its compatibility with fabrics is poor, and it is not washable, so it cannot be applied to fabrics. [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/14D06N3/00
CPCD06N3/14D06N3/0034D06N3/0063D06N3/0061D06N2209/067D06N2209/142D06N2209/1642
Inventor 吕东清吕向成姚春苗张孟清
Owner 苏州同构科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products