Moisture-permeable film composite material and preparation method thereof

A film composite material, moisture permeability technology, applied in chemical instruments and methods, cap products, synthetic resin layered products, etc. , to ensure the effect of stability

Pending Publication Date: 2021-12-17
NAT BRIDGE IND (SHENZHEN) CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the above-mentioned deficiencies of the prior art, and provide a moisture-permeable film composite material and a preparation method thereof, so as to solve the problem of low moisture permeability of the existing film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moisture-permeable film composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] On the other hand, the present embodiment provides a method for preparing a moisture-permeable film composite material, comprising: bonding a moisture-permeable layer on a non-woven fabric layer to prepare a moisture-permeable film composite material, and the formed material produces a waterproof and moisture-permeable film. The film composite material combines the characteristics of paper, film, cloth, etc., and has the advantages of wear resistance, aging resistance, high strength, light weight, smoothness, not easy to fluff, liquid penetration resistance, heat preservation and moisture permeability, etc. The bonding method can be Thermal bonding can also be used to bond the moisture permeable layer and the non-woven fabric together by means of an external adhesive.

[0027] In an embodiment, the specific steps of bonding the moisture-permeable layer on the non-woven fabric layer to prepare the moisture-permeable film composite material include:

[0028] S1, prepare t...

Embodiment 1

[0038] The non-woven layer is provided with two layers, which are arranged oppositely. The moisture-permeable layer is bonded in the middle of the two non-woven layers. The specific formula of the moisture-permeable layer includes 95wt% TPEE, 4wt% binder and 1wt% cooling masterbatch.

Embodiment 2

[0040] The non-woven layer is provided with two layers, which are arranged oppositely. The moisture-permeable layer is bonded in the middle of the two non-woven layers. The specific formula of the moisture-permeable layer includes 88wt% TPEE, 4wt% adhesive, 1wt% cooling masterbatch and 7wt% elastomeric material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention relates to a moisture-permeable film composite material and a preparation method thereof. The moisture-permeable film composite material comprises at least one non-woven fabric layer and a moisture-permeable layer, wherein the moisture-permeable layer and the non-woven fabric layer are bonded with each other; the moisture-permeable layer is prepared from TPEE, an adhesive and other auxiliaries, the content of the TPEE is 88 to 95 percent by weight, the content of the adhesive is 2 to 4 percent by weight, and the content of the other auxiliaries is 0 to 10 percent by weight. The moisture-permeable film composite material has a multi-layer structure and is composed of the non-woven fabric layer and the moisture-permeable layer, the non-woven fabric layer and the moisture-permeable layer form the laminated film composite material, and the moisture-permeable layer forms a layer of film on the surface of the non-woven fabric. Furthermore, the moisture-permeable layer mainly comprises a TPEE material, the TPEE material has non-porous hydrophilic functional groups and can take away sweat gas of a human body and block liquid, and the non-woven fabric has good liquid resistance and surface strength, so that the moisture-permeable film composite material has good moisture permeability while having certain surface strength.

Description

technical field [0001] The invention relates to the field of composite materials, in particular to a moisture-permeable film composite material and a preparation method. Background technique [0002] In recent years, with the development of industrial technology and the improvement of people's living standards, the market's demand for moisture-permeable and waterproof materials (clothing, shoes, hats and outdoor products) for protection has increased day by day. Materials with hygroscopicity, breathability, touch and other characteristics are widely favored. [0003] Waterproof & Moisture Permeable Fabric (Waterproof & Moisture Permeable Fabric), the so-called waterproof and moisture permeable performance of the fabric, means that the fabric is not penetrated by water under the action of a certain pressure of water, but the sweat vapor emitted by the human body can diffuse or be transmitted to the outside world through the fabric. 1mL of human sweat is about 23 million water...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/36B32B27/32B32B27/02B32B27/12B32B7/12B32B37/08B32B37/10B32B38/00A41D31/02A41D31/10A41D31/12A42B1/019A43B1/00B29C65/00B29C65/18
CPCB32B27/36B32B27/12B32B5/022B32B7/10B32B38/0008B32B37/10B32B37/08B29C65/18B29C66/45A41D31/125A41D31/10A41D31/02A42B1/019A43B1/00B32B2250/40B32B2307/724B32B2307/7265B32B2307/718B32B2307/554B32B2307/552B32B2437/00B32B2437/02B32B2437/04
Inventor 杨自然张峰丁实现
Owner NAT BRIDGE IND (SHENZHEN) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap