A composite wear-resistant fabric

A kind of wear-resistant fabric and composite technology, which is applied in the direction of wear-resistant fiber, textile and papermaking, biochemical fiber treatment, etc., can solve the problems of unfavorable environmental protection, base fabric layer damage, affecting fabric performance, etc., achieve good windproof effect, improve Abrasion resistance, good anti-mildew protection effect

Active Publication Date: 2022-04-29
江苏三盛纺织有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the wear-resistant and anti-wrinkle coating is an organic system, and organic solvents are used. The organic anti-wrinkle and anti-wrinkle coating is not only unfavorable for environmental protection, but also needs to immerse the base cloth layer in it for 4 hours under the condition of 50-60 ° C, and then Drying at 80-90°C, soaking in organic solvents for a long time will easily cause certain damage to the base fabric layer, which will eventually affect the performance of the fabric

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A composite wear-resistant fabric
  • A composite wear-resistant fabric
  • A composite wear-resistant fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) Add 50g of water-based urethane acrylate, 5g of hydroxyethyl methacrylate, 5g of trimethylolpropane triacrylate, 10g of deionized water and 0.2g of SN-5040 into the stirring tank, stir evenly, and then add 20g of A -171 modified nano-silica, stirred at 1200r / min for 30min, so that A-171 modified nano-silica was evenly dispersed, and finally added 0.5g of methyl benzoylformate, stirred evenly to obtain wear-resistant material;

[0039] (2) Apply the wear-resistant material evenly on the surface of the base fabric layer by roller coating, and the coating amount is 10g / m 2 , the composite wear-resistant fabric is obtained after UV curing, wherein the curing energy of UV curing is 600mJ / cm 2 , The curing speed is 8mm / s.

Embodiment 2

[0041](1) Add 55g of water-based polyurethane acrylate, 10g of tripropylene glycol diacrylate, 3g of pentaerythritol triacrylate, 15g of deionized water and 0.7g of OROTAN731A into the stirring tank, stir evenly, and then add 22g of KH-570 modified nano-dioxide For silicon, stir at 1200r / min for 30min to disperse the KH-570 modified nano-silica evenly, and finally add 1.2g of 1-hydroxycyclohexyl phenyl ketone and stir evenly to obtain a wear-resistant material;

[0042] (2) Apply the wear-resistant material evenly on the surface of the base fabric layer by roller coating, and the coating amount is 10g / m 2 , the composite wear-resistant fabric is obtained after UV curing, wherein the curing energy of UV curing is 600mJ / cm 2 , The curing speed is 8mm / s.

Embodiment 3

[0044] (1) Add 65g of water-based polyurethane acrylate, 10g of dipropylene glycol diacrylate, 8g of trimethylolpropane triacrylate, 25g of deionized water and 1.6g of SN-5040 into the stirring tank, stir evenly, and then add 28g of A- 151 modified nano-silica, stirred at 1200r / min for 30min to disperse A-151 modified nano-silica evenly, and finally added 2.3g of isopropylthioxanthone, stirred evenly to obtain wear-resistant material;

[0045] (2) Apply the wear-resistant material evenly on the surface of the base fabric layer by roller coating, and the coating amount is 10g / m 2 , the composite wear-resistant fabric is obtained after UV curing, wherein the curing energy of UV curing is 600mJ / cm 2 , The curing speed is 8mm / s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
antibacterial rateaaaaaaaaaa
Login to View More

Abstract

The application belongs to the technical field of fabrics, and specifically relates to a composite wear-resistant fabric, including a base fabric layer and a wear-resistant layer, characterized in that: the wear-resistant layer includes the following components in parts by weight: water-based polyurethane acrylate 50- 70 parts, 10-20 parts of reactive diluent, 20-30 parts of modified nano silicon dioxide, 0.2-2 parts of dispersant, 0.5-3 parts of photoinitiator, 10-30 parts of deionized water. In the composite wear-resistant fabric of the present application, an appropriate amount of modified nano-silica is added to the wear-resistant layer, which can effectively improve the wear-resistant performance of the fabric. The prepared fabric is not easy to wear, has a longer life, and has a good windproof effect; wear-resistant The layer adopts a water-based system, which is more environmentally friendly and will not damage the base cloth layer; in addition, the wear-resistant layer is an ultraviolet curing system, which can be cured under ultraviolet light to obtain a wear-resistant layer, and the curing temperature is low.

Description

technical field [0001] The application belongs to the technical field of fabrics, and in particular relates to a composite wear-resistant fabric. Background technique [0002] Traditional fabrics are usually woven from natural fibers such as cotton, hemp, and silk. Natural fibers usually have the advantages of moisture absorption, breathability, and harmlessness to the body, but natural fibers are easy to wrinkle, deform, and wear easily. Man-made fibers are chemical fibers made from polymers through chemical treatment and mechanical processing. Man-made fibers generally have properties similar to natural fibers, good hygroscopicity, air permeability and dyeability, soft to the touch, and full of luster, and are an important class of textile materials. [0003] In order to improve the performance defects of natural fibers, the following methods can be adopted: one is to blend natural fibers with artificial fibers; the other is to compound artificial fiber fabrics on natural...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/79D06M15/263D06M13/507
CPCD06M11/79D06M15/263D06M13/507D06M16/00D06M2200/35
Inventor 张文博
Owner 江苏三盛纺织有限公司