Raw dolomite high-temperature melting X fluorescence measurement method

A high-temperature melting and fluorescence measurement technology, applied in measurement devices, instruments, scientific instruments, etc., can solve the problems affecting the rhythm of inspection tasks, long time, and high labor intensity of employees, and achieve fast, comprehensive and rapid analysis, rapid inspection, and inspection cycles. short effect

Pending Publication Date: 2022-01-28
SHANDONG LAIGANG YONGFENG STEEL & IRON
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

One sample takes about 4 hours. For large-scale inspections in iron and steel plants, the inspection volume of raw dolomite rubble is about 20 batches per day. In the actual inspection operation, there are low efficiency, long time, many people and labor. The disadvantage of high intensity also seriously restricts and affects the rhythm of existing inspection tasks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Raw dolomite high-temperature melting X fluorescence measurement method
  • Raw dolomite high-temperature melting X fluorescence measurement method
  • Raw dolomite high-temperature melting X fluorescence measurement method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The preferred embodiments of the present invention will be described in detail below in conjunction with the accompanying drawings, so that the advantages and features of the present invention can be more easily understood by those skilled in the art, so as to define the protection scope of the present invention more clearly.

[0030] refer to figure 1 As shown, the present invention provides a method for measuring raw dolomite high-temperature fusion X-ray fluorescence, comprising the following steps:

[0031] S1. Grinding of the sample to be tested: the grinding particle size is ≥180 mesh, the raw dolomite sample developed in the mortar is quantitatively 55-60 grams, and the development time is 100 seconds;

[0032] S2, the test piece of the sample to be tested: the raw dolomite sample powder is compressed by a tablet press to form a test piece of the sample to be tested;

[0033] S3. Preparation of calibration samples: preparing calibration samples for establishing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a raw dolomite high-temperature melting X fluorescence measurement method. The method comprises the following steps: grinding a to-be-measured sample; obtaining a to-be-measured sample test piece; preparing a calibration sample; calibrating the sample test piece; adding a release agent; heating the sample melting furnace; establishing a calibration curve; and determining the elements of the to-be-measured sample test piece. The analysis method can be used for analyzing the content of magnesium and silicon in the raw dolomite by using an X-ray fluorescence spectrum method, can be applied to determination of magnesium and silicon content elements in the raw dolomite, can realize rapid, comprehensive and rapid analysis of the raw dolomite, has a shorter test period which is superior to that of similar high-temperature melting X-ray fluorescence analysis, and achieves accurate and rapid inspection.

Description

technical field [0001] The invention relates to the technical field of raw dolomite testing, and more specifically relates to a method for measuring raw dolomite by high-temperature melting X-ray fluorescence. Background technique [0002] Raw dolomite is a newly purchased material in the iron and steel plant. Raw dolomite plays a role in slag removal, adjustment of slag composition, alkalinity, viscosity and reaction ability in the ironmaking and steelmaking smelting processes in the factory. The purpose is to refine the metal with the required composition and temperature through the reaction of slag and metal. [0003] In order to meet the needs of production inspection indicators, the inspection of raw dolomite in the laboratory refers to "GB / T 3286.1-2012" Limestone and Dolomite Chemical Analysis Methods Part I: Measurement of Calcium Oxide and Magnesium Oxide Content Complexometric Titration and Flame Atomic Absorption Spectrometry and "GB / T 3286.2-2012" Limestone and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N23/223G01N23/2202
CPCG01N23/223G01N23/2202
Inventor 席云荣韩世国刘秀秀李金花卞玉涵
Owner SHANDONG LAIGANG YONGFENG STEEL & IRON
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com