Stone crystal composite floor and preparation method thereof

A composite flooring, selected technology, applied in the field of floor boards, can solve problems such as arching and shrinkage joints, and achieve the effects of inhibiting expansion, high comfort, and improving dimensional stability

Pending Publication Date: 2022-02-25
ANHUI SENTAI WPC TECH FLOOR CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the use of the floor, due to uneven heating or cooling, there will be arching or shrinkage joints

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stone crystal composite floor and preparation method thereof
  • Stone crystal composite floor and preparation method thereof
  • Stone crystal composite floor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A stone-crystal composite floor, comprising a wear-resistant layer 1, a color film layer 2, a PVC-impregnated glass fiber layer 3, and a substrate layer 4 arranged sequentially from top to bottom; the thickness of the PVC-impregnated glass fiber layer 3 is 0.10mm . The wear-resistant layer 1 is a PMMA film.

[0039] The base layer 4 is made of the following raw materials in parts by weight: 200 parts of filler, 50 parts of PVC resin, 2 parts of internal lubricant, 1.5 parts of external lubricant and 10 parts of stabilizer.

[0040] In this example, the added CPE resin is partially chlorinated high-density polyethylene with a chlorine content of 25% to 35%. CPE resin has the advantages of economical price and good processability, and can be used as an impact modifier for CPVC In the process of processing; compared with PVC, due to the increase of chlorine content, the intermolecular polarity and brittleness of CPVC increase, so a certain amount of impact modifier needs ...

Embodiment 2

[0052] A stone-crystal composite floor, comprising a wear-resistant layer 1, a color film layer 2, a PVC-impregnated glass fiber layer 3, and a substrate layer 4 arranged sequentially from top to bottom; the thickness of the PVC-impregnated glass fiber layer 3 is 0.10mm , the wear-resistant layer 1 is a PMMA film.

[0053] The base layer 4 is made of the following raw materials in parts by weight: 150 parts of filler, 25 parts of PVC resin, 1 part of internal lubricant, 1 part of external lubricant and 5 parts of stabilizer, 10 parts of CPVC resin and 1 part of CPE resin .

[0054] The filler is glass fiber powder with a length of 5-25 μm and an aspect ratio of about 5-10.

[0055] Described PVC is PVC SG-5 type.

[0056] The internal lubricant is G60.

[0057] Described external lubricant is PE wax.

[0058] A preparation method for a stone crystal composite floor, comprising the following steps:

[0059] S1: Preparation of substrate layer 4: Weigh 150 parts of filler, 2...

Embodiment 3

[0063] A stone-crystal composite floor, comprising a wear-resistant layer 1, a color film layer 2, a PVC-impregnated glass fiber layer 3, and a substrate layer 4 arranged sequentially from top to bottom; the wear-resistant layer 1 is a PMMA film, and the The thickness of the PVC-impregnated glass fiber layer 3 is 0.10mm.

[0064] The base layer 4 is made of the following raw materials in parts by weight: 175 parts of filler, 38 parts of PVC resin, 0.95 parts of internal lubricant, 0.83 parts of external lubricant, 7.01 parts of stabilizer, 12 parts of CPVC resin and 2.67 parts of CPE resin .

[0065] The filler is glass fiber powder with a length of 5-25 μm and an aspect ratio of about 5-10.

[0066] Described PVC is PVC SG-5 type.

[0067] The internal lubricant is G60.

[0068] Described external lubricant is PE wax.

[0069] A preparation method for a stone crystal composite floor, comprising the following steps:

[0070] S1: Preparation of substrate layer 4: Weigh 175...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
softening pointaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

A stone crystal composite floor comprises a wear-resistant layer, a color film layer, a PVC impregnated glass fiber layer and a base material layer which are sequentially arranged from top to bottom; the base material layer is prepared from, by weight, 150-200 parts of a filler, 25-50 parts of PVC resin, 0.5-2 parts of an internal lubricant, 0.5-1.5 parts of an external lubricant and 5-10 parts of a stabilizer, the length-diameter ratio of the filler is n, the length of the filler is m, n is more than or equal to 4 and less than or equal to 20, and m is more than or equal to 5 microns and less than or equal to 25 microns; and due to the adoption of the filler with the length-diameter ratio, the floor has excellent dimensional stability when coping with a complex temperature environment.

Description

technical field [0001] The invention relates to the technical field of floor boards, in particular to a stone crystal composite floor and a preparation method thereof. Background technique [0002] Stone crystal flooring is a new type of flooring, which is currently popular in European and American countries, and has a very broad domestic market prospect. Stone crystal floor mainly uses calcium powder and other minerals that can be directly obtained from nature as the main raw material. It is composed of transparent layer, wear-resistant layer, color film layer, base material layer, and rebound layer. It is very suitable for home flooring. Among them, the transparent layer, wear-resistant layer and color film layer account for about 10% of the volume of the whole product. The material of the whole product is mainly a co-extruded base material layer formed by PVC resin and mineral powder. [0003] Due to the low softening point of PVC resin, which is between 72 and 82 °C, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/30B32B27/06B32B17/02B32B33/00B32B17/12C08L27/06C08L27/24C08L23/28C08K7/14E04F15/10B29D7/01
CPCB32B27/308B32B27/06B32B5/02B32B33/00B32B5/26C08L27/06C08K7/14E04F15/107B29D7/01B32B2419/04B32B2262/101B32B2260/021B32B2260/046C08L27/24C08L23/286
Inventor 唐道远
Owner ANHUI SENTAI WPC TECH FLOOR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap