Anti-skid male shoe and preparation method thereof

An anti-skid and upper technology, applied in the field of men's shoes, can solve the problem of insufficient anti-skid performance of soles, and achieve the effects of improving anti-skid effect, anti-skid performance and improving wear resistance.

Active Publication Date: 2022-02-25
温州市耀阳鞋业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to improve the problem of insufficient anti-skid performance of soles, the application provides a kind of anti-skid men's shoes and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-skid male shoe and preparation method thereof
  • Anti-skid male shoe and preparation method thereof
  • Anti-skid male shoe and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0050] Preparation of the fly ash-zinc stearate mixture: take 20 g of zinc stearate and stir at room temperature for 10 minutes, then add 80 g of fly ash and stir for 5 minutes to prepare the fly ash-zinc stearate mixture.

[0051] A large number of agglomerates appeared in the fly ash-zinc stearate mixture, and the diameter of the agglomerates was 0.1-2mm.

Embodiment 1

[0054] The application discloses a non-slip men's shoe, which includes a vamp and a sole. There are several air holes on the sole, and the air holes on the surface of the sole are open. The sole includes the following raw materials: styrene-butadiene rubber, fly ash-zinc stearate mixture, Silicon dioxide, polyethylene glycol, foaming agent, and vulcanizing agent, wherein, the mixture of fly ash-zinc stearate is prepared from Preparation Example 1, and the contents of each component are shown in Table 1-1 below.

[0055] The preparation method of anti-slip men's shoes comprises the following steps:

[0056] S1. Preparation of shoe soles: mix silicon dioxide and polyethylene glycol and stir for 20 minutes to prepare mixture A, then dissolve the foaming agent in 100ml of solvent, add mixture A and soak for 14 hours, then place under vacuum at 50°C Dry for 14h to prepare mixture B;

[0057] Put styrene-butadiene rubber into an internal mixer and knead at 80°C for 20 minutes, then...

Embodiment 2

[0060] The application discloses a non-slip men's shoe, which includes a vamp and a sole. There are several air holes on the sole, and the air holes on the surface of the sole are open. The sole includes the following raw materials: styrene-butadiene rubber, fly ash-zinc stearate mixture, Silicon dioxide, polyethylene glycol, foaming agent, and vulcanizing agent, wherein, the mixture of fly ash-zinc stearate is prepared from Preparation Example 1, and the contents of each component are shown in Table 1-1 below.

[0061] The preparation method of anti-slip men's shoes comprises the following steps:

[0062] S1. Preparation of shoe soles: Mix silicon dioxide and polyethylene glycol and stir for 30 minutes to prepare mixture A, then dissolve the foaming agent in 100ml of solvent, add mixture A and soak for 12 hours, then place under vacuum at 60°C Dry for 12h to prepare mixture B;

[0063] Put styrene-butadiene rubber into an internal mixer and knead at 100°C for 15 minutes, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of male shoes, and particularly discloses an anti-skid male shoe and a preparation method thereof. The anti-skid male shoe comprises a vamp and a sole, and the sole is provided with a plurality of air holes. The vamp comprises the following raw materials: butadiene styrene rubber, a fly ash-zinc stearate mixture, silica, polyethylene glycol, a foaming agent, and a vulcanizing agent. The preparation method comprises the following steps: S1, preparing the sole; and S2, preparing the male shoe. According to the anti-skid male shoe, the coal ash-zinc stearate mixture is adopted in the shoe sole, the coal ash-zinc stearate mixture contains a plurality of block masses which are not uniform in size, and after the coal ash-zinc stearate mixture is mixed with the butadiene styrene rubber, the roughness of the surface of the shoe sole is improved, so that the anti-skid performance of the male shoe is improved. Besides, the fly ash is utilized, so that the discharge of the fly ash is reduced, and the method has certain environmental protection and energy saving effect.According to the preparation method, the surface of the shoe sole is polished, so that air holes in the surface of the shoe sole are open, adsorption force is formed between the shoe sole and the road surface during walking, and the anti-skid performance of the male shoe is improved.

Description

technical field [0001] The present application relates to the field of men's shoes, more specifically, it relates to a non-slip men's shoe and a preparation method thereof. Background technique [0002] Most boys love running. The soles of running shoes are generally made of rubber. During running, the soles of running shoes will keep in contact with the road surface. When there is water or snow on the road surface, if the running shoes have poor anti-skid performance, People are prone to slipping or falling on the road, and in severe cases, they will be injured. Therefore, the soles need to have good anti-skid performance. Contents of the invention [0003] In order to improve the problem of insufficient anti-slip performance of shoe soles, the present application provides an anti-slip men's shoe and a preparation method thereof. [0004] In the first aspect, the present application provides a non-slip men's shoe, which adopts the following technical solution: [0005] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/06C08L7/00C08L9/02C08L71/02C08K7/26C08K5/098C08K3/36C08J9/10A43B13/04A43B13/22
CPCC08J9/103C08J9/0095C08J9/0066C08J9/0061C08J9/0023A43B13/04A43B13/22C08J2309/06C08J2407/00C08J2409/02C08J2471/02C08J2203/04
Inventor 张庆丰袁会生高凤英
Owner 温州市耀阳鞋业有限公司