Foamable vinyl chloride resin composition

A technology of vinyl chloride resin and composition, applied in the field of foamable vinyl chloride resin composition, can solve the problems of low gas release, lack of foaming characteristics such as foaming ratio, foaming cell stability, low decomposition temperature, etc. , to achieve the effect of excellent foaming characteristics

Pending Publication Date: 2022-03-11
HANWHA SOLUTIONS CORP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] However, the disadvantage of OBSH is that the amount of gas released during foaming is relatively small and the decomposition temperature is low. Therefore, under the general processing conditions of vinyl chloride resin, compared with ADCA foaming agent, it lacks foaming characteristics such as foaming ratio, foaming rate, etc. Foam cell stability, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Foamable vinyl chloride resin composition
  • Foamable vinyl chloride resin composition
  • Foamable vinyl chloride resin composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] With respect to 100 parts by weight of polyvinyl chloride (polymerization degree 1000), measure 90 parts by weight of DEHCH as a plasticizer, 10 parts by weight of OBSH as a foaming agent, and mix with a mixer (Mixer) for 15 minutes to prepare a foamable chlorine Vinyl resin compositions (plastisols).

Embodiment 2

[0068] A foamable vinyl chloride resin composition was prepared in the same manner as in Example 1 except that 80 parts by weight of DEHCH was used as a plasticizer.

Embodiment 3

[0070] A foamable vinyl chloride resin composition was prepared in the same manner as in Example 1 except that 70 parts by weight of DEHCH was used as a plasticizer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to an environment-friendly foamable vinyl chloride resin composition which has excellent foaming characteristics such as foaming ratio, stability and the like and does not produce harmful substances such as formamide.

Description

technical field [0001] Cross References to Related Applications [0002] This application claims the priority of the Korean patent application with application number 10-2019-0093425 filed on July 31, 2019 and Korean patent application with application number 10-2020-0093870 filed on July 28, 2020, all of which The contents are incorporated in this specification by reference. [0003] The present invention relates to a foamable vinyl chloride resin composition having excellent foaming properties and being environmentally friendly. Background technique [0004] Vinyl chloride resin, as a homopolymer of vinyl chloride and an interpolymer containing more than 50% vinyl chloride, is one of the general-purpose thermoplastic resins prepared by suspension polymerization and emulsion polymerization, wherein polyvinyl chloride resin prepared by emulsion polymerization is Plasticizer (Plasticizer), Stabilizer (Stabilizer), Filler (Filler), Blowing Agent (Blowing Agent), Pigment (Pi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08K5/12C08J9/10
CPCC08J9/105C08J9/0023C08J2327/06C08J2203/04C08L27/06C08K5/372C08K5/12C08J9/00C08K3/013
Inventor 金泯玗金载松崔龙石
Owner HANWHA SOLUTIONS CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com