Manufacturing method of novel metal door and window profile

A technology for metal doors and windows and manufacturing methods, which is applied in the field of doors and windows, can solve problems such as general corrosion resistance, decreased toughness, and easy deformation, and achieve the effects of good toughness and rigidity, good acid resistance, and improved production efficiency

Inactive Publication Date: 2022-03-18
怀化林源门窗幕墙有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current metal composite materials have average corrosion resistance, are easily deformed, and their toughness decreases under low temperature conditions, and they are easy to break

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A method for making a novel metal door and window profile, comprising the steps of:

[0018] 1) Preparation of metal raw materials: Pour copper, silicon, magnesium, manganese and zinc into the furnace in sequence for heating. After the metal is completely melted, keep it warm to obtain mixed metal 1; add rare earth to mixed metal 1 and stir and heat to obtain a mixture Metal 2: add nickel, chromium, titanium, boron, zirconium and strontium to the mixed metal 2 in sequence, and then transfer to a refining furnace for refining to obtain material 1; pour material 1 into a mold and cool to room temperature, then quench, Hot rolling process, obtain material two;

[0019] 2) Making door and window profiles: Cut material two out of the blanks of doors and windows, then engrave or die-cast the blanks with engraving machines or die-casting machines, then color the blanks, and then make blanking molds and feed them Fill the mold with wipeable paint, select a suitable position on...

Embodiment 2

[0022] A method for making a novel metal door and window profile, comprising the steps of:

[0023] 1) Preparation of metal raw materials: Pour copper, silicon, magnesium, manganese and zinc into the furnace in sequence for heating. After the metal is completely melted, keep it warm to obtain mixed metal 1; add rare earth to mixed metal 1 and stir and heat to obtain a mixture Metal 2: add nickel, chromium, titanium, boron, zirconium and strontium to the mixed metal 2 in sequence, and then transfer to a refining furnace for refining to obtain material 1; pour material 1 into a mold and cool to room temperature, then quench, Hot rolling process, obtain material two;

[0024] 2) Making door and window profiles: Cut material two out of the blanks of doors and windows, then engrave or die-cast the blanks with engraving machines or die-casting machines, then color the blanks, and then make blanking molds and feed them Fill the mold with wipeable paint, select a suitable position on...

Embodiment 3

[0027] A method for making a novel metal door and window profile, comprising the steps of:

[0028] 1) Preparation of metal raw materials: Pour copper, silicon, magnesium, manganese and zinc into the furnace in sequence for heating. After the metal is completely melted, keep it warm to obtain mixed metal 1; add rare earth to mixed metal 1 and stir and heat to obtain a mixture Metal 2: add nickel, chromium, titanium, boron, zirconium and strontium to the mixed metal 2 in sequence, and then transfer to a refining furnace for refining to obtain material 1; pour material 1 into a mold and cool to room temperature, then quench, Hot rolling process, obtain material two;

[0029] 2) Making door and window profiles: Cut material two out of the blanks of doors and windows, then engrave or die-cast the blanks with engraving machines or die-casting machines, then color the blanks, and then make blanking molds and feed them Fill the mold with wipeable paint, select a suitable position on...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method of a novel metal door and window profile, which comprises the following steps: 1) preparing metal raw materials: sequentially pouring copper, silicon, magnesium, manganese and zinc into a smelting furnace, heating, and preserving heat after the metal is completely smelted to obtain mixed metal I; adding rare earth into the mixed metal I, stirring and heating to obtain mixed metal II; nickel, chromium, titanium, boron, zirconium and strontium are sequentially added into the second mixed metal, then the second mixed metal is transferred into a refining furnace to be refined, and a first material is obtained; the first material is poured into a mold to be cooled to the normal temperature and then subjected to quenching and hot rolling treatment, and a second material is obtained; and (2) door and window sectional material manufacturing: cutting the second material into a door and window blank, performing engraving or die casting work on the blank through an engraving machine or a die casting machine, then coloring the blank, and finally cutting the door and window sectional material along a blanking line.

Description

technical field [0001] The invention relates to the field of doors and windows, in particular to a method for making novel metal door and window profiles. Background technique [0002] As people's living and home styles become more and more diverse, the demand for living and home styles has also increased. Among them, the improvement of building quality requirements is particularly prominent, and the requirements for building doors and windows are the most prominent. The doors and windows used today are made of metal, There are several kinds of plastic, wood, etc., so the material for making doors and windows has become the main research object. [0003] With the development of science and technology, more and more metal composite materials are used in the profiles of doors and windows. Titanium alloys, aluminum alloys, etc. can be used as profiles of doors and windows. compound more and more. However, the current metal composite materials have average corrosion resistance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C30/06C22C30/02C22C1/02B23P15/00
CPCC22C30/06C22C30/02C22C1/02B23P15/00
Inventor 樊娟
Owner 怀化林源门窗幕墙有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap