Environment-friendly material for decoration and preparation method thereof

A technology of environmentally friendly materials and raw materials, applied in luminescent paints, coatings, latex paints, etc., can solve problems such as deterioration and failure, easily affecting sleep, and luminous effect easily causing light pollution, etc., to achieve stable protection, reduce light pollution, and purify the air. Effect

Active Publication Date: 2022-03-22
浙江一方建筑装饰实业有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the luminous effect of the photo-induced energy storage material - photo-induced energy storage luminous powder is easy to cause light pollution, so it is not suitable for use on the inner wall of the building
Such as: use it on the inner wall of the bedroom, it is easy to affect sleep
And it is susceptible to deterioration and failure due to the influence of humid air and strong light

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly material for decoration and preparation method thereof
  • Environment-friendly material for decoration and preparation method thereof
  • Environment-friendly material for decoration and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] Environmentally friendly materials for decoration, consisting of the following raw materials in parts by weight:

[0060] 30 parts of light energy redispersible latex powder, 5 parts of photocatalyst material, 55 parts of inorganic additive, 16 parts of filler, 0.3 part of dispersant, and 0.6 part of defoamer.

[0061] The inorganic additive is composed of heavy calcium powder, light calcium powder and talcum powder in a weight ratio of 10:2:3.

[0062] The filler is composed of attapulgite and diatomite in a weight ratio of 12:5.

[0063] The dispersant is sodium polyacrylate powder.

[0064] The defoamer is composed of simethicone oil and polyethylene glycol powder in a weight ratio of 2:5.

[0065] The preparation method of the light energy redispersible latex powder comprises the following steps:

[0066] S1. Dissolve sodium bicarbonate, potassium persulfate, and sodium dodecyl diphenyl ether disulfonate in water according to the ratio of material to liquid 1g:2g...

Embodiment 2

[0081] Environmentally friendly materials for decoration, consisting of the following raw materials in parts by weight:

[0082] 30 parts of light energy redispersible latex powder, 5 parts of photocatalyst material, 55 parts of inorganic additive, 16 parts of filler, 0.3 part of dispersant, and 0.6 part of defoamer.

[0083] The inorganic additive is composed of heavy calcium powder, light calcium powder and talcum powder in a weight ratio of 10:2:3.

[0084] The filler is composed of attapulgite and diatomite in a weight ratio of 12:5.

[0085] The dispersant is sodium polyacrylate powder.

[0086] The defoamer is composed of simethicone oil and polyethylene glycol powder in a weight ratio of 2:5.

[0087] The preparation method of the light energy redispersible latex powder comprises the following steps:

[0088] S1. Dissolve sodium bicarbonate, potassium persulfate, and sodium dodecyl diphenyl ether disulfonate in water according to the ratio of material to liquid 1g:2g...

Embodiment 3

[0104] Environmentally friendly materials for decoration, consisting of the following raw materials in parts by weight:

[0105] 30 parts of light energy redispersible latex powder, 5 parts of photocatalyst material, 55 parts of inorganic additive, 16 parts of filler, 0.3 part of dispersant, and 0.6 part of defoamer.

[0106] The inorganic additive is composed of heavy calcium powder, light calcium powder and talcum powder in a weight ratio of 10:2:3.

[0107] The filler is composed of attapulgite and diatomite in a weight ratio of 12:5.

[0108] The dispersant is sodium polyacrylate powder.

[0109] The defoamer is composed of simethicone oil and polyethylene glycol powder in a weight ratio of 2:5.

[0110] The preparation method of the light energy redispersible latex powder comprises the following steps:

[0111] S1. Dissolve sodium bicarbonate, potassium persulfate, and sodium dodecyl diphenyl ether disulfonate in water according to the ratio of material to liquid 1g:2g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly material for decoration and a preparation method thereof. The environment-friendly material for decoration comprises light energy redispersible latex powder and a photocatalyst material. Methyl methacrylate and butyl acrylate are used as main core monomer raw materials, methyl methacrylate and styrene are used as main shell monomer raw materials, 2-acrylamide-2-methylpropanesulfonic acid and N-hydroxymethyl acrylamide are added to improve the performance, and the redispersible latex powder with the core-shell structure is generated through two-step polymerization. In the reaction process of generating the core-shell structure, light energy particles enveloped by sodium silicate and methyl cellulose are added. Inorganic and organic coating materials are combined to form a uniform gel composite system with a cross-linked polymerization three-dimensional structure, and the light energy redispersible latex powder is obtained. Wherein the photoluminescent noctilucent material can play a role in catalyzing the photocatalyst under a dark condition, so that the air can be effectively purified for 24 hours, and light pollution is not caused.

Description

technical field [0001] The invention belongs to the technical field of decoration materials, and in particular relates to an environment-friendly material for decoration and a preparation method thereof. Background technique [0002] With the continuous improvement of people's living standards and environmental protection awareness, the requirements for the quality of building decoration materials are also getting higher and higher. Many decoration materials more or less contain small molecular harmful substances such as alcohol and aldehyde, which will be released slowly in the air for a long time. Even after purification treatment such as formaldehyde removal, they cannot be completely eliminated. The prior art has found that the use of interior wall paints with purifying properties that reduce the amount of harmful substances in the air will help to improve the situation. Latex paint is currently one of the most commonly used interior wall paints on the market. Adding co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D151/00C09D5/22C09D5/02C09D7/61
CPCC09D151/003C09D5/22C09D5/024C09D5/028C08K2003/3036C08K2003/265C08K9/10C08K3/30C08K3/26C08K3/34
Inventor 郭加栋
Owner 浙江一方建筑装饰实业有限公司