Nitrate-free environment-friendly steel plate enamel high-temperature titanium creamy yellow cover glaze and preparation method thereof

An environmentally friendly, nitrate technology, applied in the field of enamel, to increase the oxidation atmosphere and solve the effect of polluting the environment

Pending Publication Date: 2022-04-15
SINOPIGMENT & ENAMEL CHEM
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] One of the objectives of the present invention is to provide a nitrate-free environment-friendly steel plate enamel high-temperature titanium milk yellow surface glaze without reducing the performance indicators of the product in view of the above-mentioned environmental protection problems existing in the current traditional nitrate-containing steel plate enamel enamel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nitrate-free environment-friendly steel plate enamel high-temperature titanium creamy yellow cover glaze and preparation method thereof
  • Nitrate-free environment-friendly steel plate enamel high-temperature titanium creamy yellow cover glaze and preparation method thereof
  • Nitrate-free environment-friendly steel plate enamel high-temperature titanium creamy yellow cover glaze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] (1) Take the raw materials by the mass parts of the following components:

[0041] Quartz 20.8KG, Zero Water Borax 15.5KG, Rutile 13KG, Potassium Feldspar 23KG, Trisodium Phosphate 9KG, Potassium Carbonate 3.5KG, Sodium Fluosilicate 9KG, Potassium Dichromate 0.04KG

[0042] (2) Pulverize the above raw materials and mix them evenly.

[0043] (3) Put the uniformly mixed material into the melting furnace, and melt it under the condition of pure oxygen, and the melting temperature is controlled at 1290±10°C.

[0044] (4) After the above materials are completely melted, the borosilicate glass body is obtained, and the molten borosilicate glass body is brazed, and quickly drawn into a glass filament of 1.2 to 1.5 meters for detection. The detection requirement is: within 1 meter of the glass filament. The knot is the completion of melting.

[0045] (5) Quenching and quenching the melted borosilicate glass body with water to obtain the product.

Embodiment 2

[0047] The raw materials are weighed according to the mass parts of the following components:

[0048] Quartz 20.8KG, zero-water borax 16KG, rutile 13KG, potassium feldspar 22KG, trisodium phosphate 9KG, potassium carbonate 3.5KG, sodium fluorosilicate 8KG, potassium dichromate 0.04KG.

[0049] The preparation process of this example is basically the same as that of Example 1, the difference is that in step (5), the quenching of the melted borosilicate glass body adopts a tableting process.

Embodiment 3

[0051] The raw materials are weighed according to the mass parts of the following components:

[0052] Quartz 20.8KG, zero-water borax 17KG, rutile 13KG, potassium feldspar 21KG, trisodium phosphate 9KG, potassium carbonate 3.5KG, sodium fluorosilicate 7.5KG, potassium dichromate 0.04KG.

[0053] The preparation process of this embodiment is basically the same as that of embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses nitrate-free environment-friendly steel plate enamel high-temperature titanium creamy yellow cover glaze and a preparation method thereof, and the nitrate-free environment-friendly steel plate enamel high-temperature titanium creamy yellow cover glaze comprises the following components in parts by mass: 18-21 parts of quartz, 15-17 parts of anhydrous borax, 12-14 parts of rutile, 20-23 parts of potassium feldspar, 8-10 parts of trisodium phosphate, 2-4 parts of potassium carbonate and 7-9 parts of sodium fluosilicate. The raw materials are melted at the temperature of 1290 + / -10 DEG C and under the condition of pure oxygen, and the firing temperature of a finished product is 850-880 DEG C. The high-temperature titanium creamy cover glaze does not contain nitrate, and the major technical problem that in the production process of existing steel plate enamel high-temperature titanium creamy cover glaze, nitric oxide gas is generated and discharged to pollute the environment is fundamentally solved.

Description

technical field [0001] The invention belongs to the technical field of enamel, and in particular relates to a nitrate-free environment-friendly steel plate enamel high-temperature titanium milk yellow surface glaze and a preparation method thereof. Background technique [0002] Enamel enamel is mainly composed of refractory materials such as feldspar and quartz, fusible chemical materials such as zero-water borax, sodium nitrate, potassium nitrate, soda ash, and characteristic materials such as non-ferrous metal oxides. They are mixed in a certain proportion, melted at high temperature, and cooled rapidly into granular Or flake borosilicate glass body is prepared. [0003] The introduction of nitrates (sodium nitrate, potassium nitrate, etc.) into enamel glazes as oxidants and fluxes has become a consensus in the industry, and it is an indispensable raw material for enamel glazes in traditional enamel theory. So far, there is no safe, colorless, reasonably priced oxidizing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/08C03C6/06C23D5/00
Inventor 汤上方金泉唐龙
Owner SINOPIGMENT & ENAMEL CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com